CONDUCTIVE HYDROGEL AND METHOD OF PREPARING THE SAME

• US 20130270491A1
• Filed: 04/17/2012
• Published: 10/17/2013
• Est. Priority Date: 04/17/2012
• Status: Abandoned Application

• Current Assignee: Bio-Protech, Inc.
• Original Assignee: Bio-Protech, Inc.
• Inventors: PARK, Ik-Ro, CHUNG, Chan-Moon
• Application Number:
  US13/448,968
• Publication Number:
  US 20130270491A1
• Time in Patent Office: Days
• US Class Current: 252/519.3
• CPC Class Codes: A61B 5/259 using conductive adhesive means, e.g. gels
• CPC Class Codes: H01B 1/122 Ionic conductors

Abstract

A conductive hydrogel includes: a first monomer; a second monomer; a crosslinking agent; a photoinitiator; a wetting agent; an electrolyte; and deionized water, wherein the first monomer is a 3-sulfopropyl acrylate potassium salt, and the second monomer is acrylic acid. The conductive hydrogel has high adhesivity, conductivity and moisture-retaining capacity and low skin irritancy compared to conventional hydrogels because it has the optimum composition ratio.

Claims

1. A conductive hydrogel, comprising:

a first monomer;

a second monomer;

a crosslinking agent;

a photoinitiator;

a wetting agent;

an electrolyte; and

deionized water,

wherein the first monomer is a 3-sulfopropyl acrylate potassium salt,

the second monomer is acrylic acid,

the crosslinking agent is selected from the group consisting of ethyleneglycol dimethacrylate, poly(ethyleneglycol) diacrylate, diethyleneglycol dimethacrylate, ethyleneglycol diacrylate, 1,3-dihydroxypropyl dimethacrylate and mixtures thereof,

the photoinitiator is selected from the group consisting of 1-hydroxycyclohexyl phenyl ketone, monoacyl phosphine oxide, benzoyl alkyl ether, mercaptobenzothiazoyl and mixtures thereof,

the wetting agent is glycerol, and

the electrolyte is selected from the group consisting of sodium, potassium chloride, phosphate, citrate, acetate and lactate.

2. The conductive hydrogel according to claim 1, wherein an amount of the 3-sulfopropyl acrylate potassium salt is 24˜

32 wt %, an amount of the acrylic acid is 1˜

4 wt %, an amount of the crosslinking agent is 0.06˜

0.1 wt %, an amount of the photoinitiator is 0.01˜

0.1 wt %, an amount of the wetting agent is 32˜

40 wt %, an amount of the electrolyte is 2.5˜

3.5 wt %, and an amount of the deionized water is 28˜

35 wt %.

3. The conductive hydrogel according to claim 1, wherein the crosslinking agent is poly(ethyleneglycol) diacrylate, the photoinitiator is 1-hydroxycyclohexyl phenyl ketone, and the electrolyte is potassium chloride.

4. The conductive hydrogel according to claim 3, wherein an amount of the 3-sulfopropyl acrylate potassium salt is 24˜

32 wt %, an amount of the acrylic acid is 3˜

4 wt %, an amount of the poly(ethyleneglycol) diacrylate is 0.08˜

0.1 wt %, an amount of the 1-hydroxycyclohexyl phenyl ketone is 0.08˜

0.1 wt %, an amount of the glycerol is 35˜

40 wt %, an amount of the potassium chloride is 2.5˜

3.0 wt %, and an amount of the deionized water is 28˜

32 wt %.

5. The conductive hydrogel according to claim 1, further comprising at least one additive selected from the group consisting of a moisture-retaining agent, an enzyme, a surfactant, an antibiotic, a permeation enhancer, a pH adjuster, and mixtures thereof.

6. A method of preparing the conductive hydrogel of claim 1, comprising the steps of:

(I) mixing the first monomer, the second monomer, the crosslinking agent, the photoinitiator, the wetting agent and the electrolyte with the deionized water and stirring the mixture to prepare a composition; and

(II) irradiating the composition with ultraviolet to crosslink the composition.

7. The method according to claim 6, wherein, in the step (I) of preparing the composition, the crosslinking agent, the first monomer, the electrolyte, the wetting agent, the deionized water and the second monomer are sequentially mixed and stirred, and then the photoinitiator is added and stirred.