COMPOSITION FOR AN INTUMESCENT FIRE PROTECTION COATING, FIRE PROTECTION COATING, ITS USE AND MANUFACTURING PROCESS FOR AN INTUMESCENT FIRE PROTECTION COATING

• US 20140005298A1
• Filed: 03/17/2011
• Published: 01/02/2014
• Est. Priority Date: 03/17/2011
• Status: Abandoned Application

• Current Assignee: Rudolf Hensel GmbH
• Original Assignee: Rudolf Hensel GmbH
• Inventors: Thewes, Volker
• Application Number:
  US13/695,521
• Publication Number:
  US 20140005298A1
• Time in Patent Office: Days
• US Class Current: 523/179
• CPC Class Codes: C09D 5/185 Intumescent paints
• CPC Class Codes: C09K 21/10 containing nitrogen

Abstract

The invention is a composition for an aqueous, intumescent fire protection coating, consisting of at least one silicone resin emulsion and an agent forming foam in case of fire. Furthermore, the invention concerns an intumescent fire protection coating made with such composition, as well as the application and a manufacturing process for this composition.

Claims

1. A composition for an aqueous intumescent fire protection coating, containing at least one silicone resin emulsion as bonding agent, as well as an agent producing foam in case of fire.

2. The composition for an intumescent fire protection coating of claim 1, whereby the composition contains solid additives as foam-producing agents.

3. The composition for an intumescent fire protection coating of claim 1, whereby the silicone resin emulsion is of aqueous nature and contains an organic solvent ratio—

preferably aromatic hydrocarbons, alcohols and/or poylether—

of 0-25%.

4. The composition for an intumescent fire protection coating of claim 1, whereby the silicone resin emulsion consists of polysiloxane, silane-siloxane mixtures and/or modified polysiloxane,

5. The composition for an intumescent fire protection coating claim 1, whereby the bonding agent—

in addition to the silicone resin emulsion—

is an aqueous organic polymer dispersion at random mixing ratio and the organic polymer dispersion is a dispersion of one or several of the following polymer components;

homopolymerisate on vinyl acetate basis,

copolymers on vinyl acetate, ethyl and vinyl chloride basis,

copolymers on basis of vinyl acetate and vinyl ester of a long chain,

branched carbonic acid,

copolymers on vinyl acetate and maleic acid di-n-butyl ester basis,

copolymers on vinyl acetate and acrylic acid ester basis,

copolymers on styrene and acrylic acid ester basis,

copolymers on acrylic acid ester basis,

copolymers on vinyl toluol and acrylic acid ester basis,

6. The composition for an intumescent fire protection coating claim 1, characterised by the fact that it contains

1 to 75 pbw of a film-forming bonding agent according to claims 3-5,

5 to 50 pbw of an acid-producing substance,

5 to 25 pbw of a carbon-producing substance,

5 to 25 pbw of a propellant, and

to 50 pbw of standard excipients and additives.

7. The composition for an intumescent fire protection coating claim 1, containing an acid-producing substance selected from ammonium salts of phosphoric acids and/or poly-phosphoric acids or ammonium polyphosphates of the formula (NH4PO3)n, whereby n is a number from 10 to ≧

1000.

8. The composition for an intumescent fire protection coating claim 1, containing a carbon-producing substance, selected from carbohydrates, in particular pentaerythritol, dipentaerythritol, tripentaerythritol and/or poly-condensation products of pentaerythritol;

amylum and expanded graphite.

9. The composition for an intumescent fire protection coating claim 1, containing a propellant, selected from melamine and/or guanidine as well as their salts and/or dicyandiamide, as well as trichloroethylene (hydroxyethyl), isocyanogen urate and its derivatives, and where optionally melamine phosphate, melamine cyanurate, melamine borate, melamine polyphosphate, melamine silicate are used as melamine salts and guanidine phosphates are used as guanidine salts.

10. The composition for an intumescent fire protection coating claim 1, additionally containing one or more expedients and additives, selected from pigments, such as—

among others—

glass fibres, mineral fibres, kaolin, talcum powder, alumina, aluminium hydroxide, magnesium hydroxide, precipitation silicic acids, silicates and/or pulverised celluloses, phosphine acid salts and/or diphosphine acid salts and/or their polymers, plasticizers, film-forming aids, thixotropic agents, wetting agents and dispersants as well as preservatives.

11. A fire protection coating, manufactured by physically drying a composition layer in line with claim 1, in particular by evaporating the contained solvent, or parts thereof, whereby the fire protection coating contains at least one silicone resin bonding agent.

12. Application of the composition for a fire protection coating claim 1 in paintable, spreadable or sprayable form for the protection of various undergrounds as well as of conventional and industrial structural elements, preferably made of steel, aluminium, wood, concrete, electrical cables and pipes, or for the coating of open steel profiles, closed and/or castellated profiles, or for workshop applications.

13. A manufacturing process for the composition for an intumescent fire protection coating claim 1, characterised by the fact that a silicone resin emulsion is mixed as a bonding agent in a high-shearing dissolver with an agent forming foam in case of fire.

14. The manufacturing process for a composition for an intumescent fire protection coating of claim 13, characterised by the fact that it is dispersed in a high shearing dissolver while ensuring that the composition temperature of T=50°

C. to T=40°

C. is not exceeded during the entire manufacture process.