METHOD FOR PRODUCING A VENEER

• US 20140027020A1
• Filed: 02/15/2011
• Published: 01/30/2014
• Est. Priority Date: 02/15/2010
• Status: Active Grant

• Current Assignee: Hd Wood Technologies Limited
• Original Assignee: Hd Wood Technologies Limited
• Inventors: Wagoner, Glenn L., Klaeusler, Oliver Frederik
• Granted Patent: US 9,855,673 B2
• Time in Patent Office: Days
• US Class Current: 144/351
• CPC Class Codes: B27L 5/00 Manufacture of veneer working veneer or plywood B27D ; Preparatory processing therefor drying F26B
• CPC Class Codes: B44C 5/0415 containing metallic elements
• CPC Class Codes: B44C 5/043 containing wooden elements

Abstract

Method for manufacturing second wood sheets from first wood sheets, comprising steps (i) to (iv): (i) providing first wood sheets having a laminarly developed front side and backside, wherein the moisture content of said first wood sheets is below the fiber saturation point of the wood; (ii) applying a water-comprising adhesive to one or more front sides and/or one or more backsides of said first wood sheets provided in step (i); (iii) adhering said wood sheets from step (ii) and optionally from step (i) with laminar sides to each other in order to form a block which comprises adhered layers of said first wood sheets, wherein the adhering is performed such to increase the moisture content of said formed block up to or above the fiber saturation point of the wood; (iv) slicing said block formed in step (iii) to form said second wood sheets.

Claims

1-15. -15. (canceled)

16. A method for producing one or more second wood sheets from first wood sheets, comprising:

(i) providing first wood sheets having a laminarly developed front side and backside, wherein the moisture content of the first wood sheets is below the fiber saturation point of the wood;

(ii) applying a water-comprising adhesive to at least one front side, at least one backside, or at least one front side and at least one backside of the first wood sheets;

(iii) adhering the first wood sheets from (ii) and optionally from (i) with laminar sides to each other thereby forming a block of adhered layers, wherein the adhering is performed such as to increase the moisture content of the block of adhered layers up to or above the fiber saturation point of the wood which is 30-100%; and

(iv) slicing the block of adhered layers to form at least one second wood sheet.

17. A method according to claim 16, wherein the water-comprising adhesive increases the moisture content of the up to or above the fiber saturation point of the wood sheets from (ii).

18. A method according to claim 16, wherein the thickness of the first wood sheets is from 0.1 mm to 3 mm.

19. A method according to claim 16, wherein the moisture content of the first wood sheets provided in (i) is below 30%.

20. A method according to claim 16, wherein at least one of the first wood sheets and the second wood sheet or sheets is a veneer.

21. A method according to claim 16, wherein the first wood sheets are sliced or peeled veneer.

22. A method according to claim 16, wherein the first wood sheets provided in (i) comprise hardwood.

23. A method according to claim 16, wherein the first wood sheets provided in (i) comprise at least two different wood species.

24. A method according to claim 16, wherein the water-comprising adhesive is an aqueous suspension of an organic polymer.

25. A method according to claim 24, wherein the organic polymer is selected from the group consisting of a polyvinyl acetate, a polyvinyl alcohol, a partially saponified polyvinyl acetate, an ethylene vinylactetate copolymer, a phenolic resin, a urea resin, a polyurethane resin, and combinations thereof.

26. A method according to claim 16, wherein (iii) is performed under pressure.

27. A method according to claim 16, wherein the block of adhered layers has a moisture content of greater than 40% prior to (iv).

28. A method according to claim 16, wherein (iv) comprises one of:

slicing the block of adhered layers in a direction which is perpendicular to the plane which is defined by the adhesion layers of the adhered first wood sheets;

slicing the block of adhered layers in a direction which is horizontal to the plane which is defined by the adhesion layers of the adhered first wood sheets;

or

slicing the block of adhered layers in a direction which is inclined to the plane which is defined by the adhesion layers of the adhered first wood sheets.

29. A method according to claim 16, further comprising:

(v) drying the second wood sheet or sheets until a moisture content below the fiber saturation point of the wood is reached.

30. A method according to claim 16, wherein the water-comprising adhesive has a solids content of 30-80% by weight based on the total weight of the water-comprising adhesive.

31. A method according to claim 16, further comprising at least one of the following:

dyeing the water-comprising adhesive prior to or after the applying in (ii);

dyeing at least one of the first wood sheets prior to the applying in (ii) or prior to the adhering in (iii);

inserting glitter between at least two of the first wood sheets prior to the adhering in (iii);

inserting metal powder between at least two of the first wood sheets prior to the adhering in (iii);

inserting a metal sheet between at least two of the first wood sheets prior to the adhering in (iii);

inserting a plastic sheet between at least two of the wood sheets prior to the adhering in (iii);

planing the front side, the backside or both the front side and the backside of at least one second wood sheet;

sanding the front side, the backside or both the front side and the backside of at least one second wood sheet; and

gluing at least one second wood sheet onto a substrate.

32. A method according to claim 29, further comprising at least one of the following:

dyeing the water-based adhesive prior to or after the applying in (ii);

dyeing at least one of the first wood sheets prior to the applying in (ii) or prior to the adhering in (iii);

inserting glitter between at least two of the first wood sheets prior to the adhering in (iii);

inserting metal powder between at least two of the first wood sheets prior to the adhering in (iii);

inserting a metal sheet between at least two of the first wood sheets prior to the adhering in (iii);

inserting a plastic sheet between at least two of the wood sheets prior to the adhering in (iii);

planing the front side, the backside or both the front side and the backside of at least one second wood sheet;

sanding the front side, the backside or both the front side and the backside of at least one second wood sheet; and

gluing at least one second wood sheet onto a substrate.

33. A method for producing one or more second wood sheets from first wood sheets, comprising:

(i) providing first wood veneer sheets having a laminarly developed front side and backside, wherein the moisture content of the first wood sheets is below the fiber saturation point of the wood;

(ii) applying a water-comprising adhesive to at least one front side, at least one backside, or at least one front side and at least one backside of the first wood sheets;

(iii) adhering the first wood sheets from (ii) and optionally from (i) with laminar sides to each other thereby forming a block of adhered layers, wherein the adhering is performed such as to increase the moisture content of the block of adhered layers is up to or above the fiber saturation point of the wood which is 30-100%; and

(iv) slicing the block of adhered layers to form at least one second wood sheet.

34. A method for producing one or more second wood sheets from first wood sheets, comprising:

(i) providing first wood veneer sheets having a laminarly developed front side and backside, wherein the moisture content of the first wood sheets is below the fiber saturation point of the wood;

(ii) applying a water-comprising adhesive to at least one front side, at least one backside, or at least one front side and at least one backside of the first wood sheets wherein the water-comprising adhesive is an aqueous suspension of at least one organic polymer;

(iii) adhering the first wood sheets from (ii) and optionally from (i) with laminar sides to each other thereby forming a block of adhered layers, wherein the adhering is performed such as to increase the moisture content of the block of adhered layers is up to or above the fiber saturation point of the wood which is 30-100%; and

(iv) slicing the block of adhered layers to form at least one second wood sheet.

35. A method according to claim 34, further comprising:

(v) drying the second wood sheet or sheets until a moisture content below the fiber saturation point of the wood is reached.