LAMINATED POROUS FILM AND NON-AQUEOUS ELECTROLYTE SECONDARY BATTERY

• US 20140178741A1
• Filed: 07/17/2012
• Published: 06/26/2014
• Est. Priority Date: 07/28/2011
• Status: Active Grant

• Current Assignee: Sumitomo Chemical Company Limited
• Original Assignee: Sumitomo Chemical Company Limited
• Inventors: Hasegawa, Hirohiko, Saitou, Yuzuru
• Granted Patent: US 9,705,120 B2
• Time in Patent Office: Days
• US Class Current: 429/144
• CPC Class Codes: C08J 2323/06 Polyethene
• CPC Class Codes: C08J 2400/14 Water soluble or water swellable polymers, e.g. aqueous gels
• CPC Class Codes: C08J 2401/28 Alkyl ethers
• CPC Class Codes: C08J 7/0427 with only one layer of a composition containing a polymer binder with more layers C08J7/042
• CPC Class Codes: C08J 7/043 Improving the adhesiveness of the coatings per se, e.g. forming primers adhesives in the form of films or foils characterised by the primer layers between the polymer carriers and the adhesives C09J7/50
• CPC Class Codes: C08J 7/123 Treatment by wave energy or particle radiation C08J7/18 takes precedence
• CPC Class Codes: H01M 50/446 Composite material consisting of a mixture of organic and inorganic materials
• CPC Class Codes: Y02E 60/10 Energy storage using batteries

Abstract

The present invention provides a laminated porous film and a non-aqueous electrolyte secondary battery. The laminated porous film is a laminated porous film in which a heat-resistant layer comprising a binder resin and a filler is laminated on one or both of the surfaces of a porous film substrate mainly comprising a polyolefin, wherein a part occupied by at least one out of the binder resin and the filler is formed in the porous film substrate so as to touch the heat-resistant layer, and the total thickness of the occupied part is not less than 1% and not more than 20% of the overall thickness of the porous film substrate. The non-aqueous electrolyte secondary battery comprises the laminated porous film according as a separator.

Claims

1. A laminated porous film in which a heat-resistant layer comprising a binder resin and a filler is laminated on one or both of the surfaces of a porous film substrate mainly comprising a polyolefin, wherein a part occupied by at least one out of the binder resin and the filler is formed in the porous film substrate so as to touch the heat-resistant layer, and the total thickness of the occupied part is not less than 1% and not more than 20% of the overall thickness of the porous film substrate.

2. The laminated porous film according to claim 1, wherein the thickness of the part occupied by the at least one out of the binder resin and the filler relative to the interface between the porous film substrate and the heat-resistant layer is not less than 1% and not more than 10% of the overall thickness of the porous film substrate.

3. The laminated porous film according to claim 1, wherein the thickness of a part substantially unoccupied by any binder resin or any filler in the porous film substrate is not less than 7 μ

m.

4. The laminated porous film according to claim 1, wherein the binder resin is a water-soluble polymer.

5. The laminated porous film according to claim 4, wherein the binder resin is a cellulose ether.

6. The laminated porous film according to claim 1, wherein the filler is an inorganic filler.

7. The laminated porous film according to claim 6, wherein the inorganic filler is alumina.

8. The laminated porous film according to claim 1, wherein the laminated porous film is obtained by applying a coating slurry to the surface of the porous film substrate, the coating slurry comprising the binder resin, the filler and a solvent to form the heat-resistant layer and having a contact angle with a polyethylene sheet of 60°

or more, and the porous film substrate having been surface treated so as to have a contact angle with the coating slurry of 65°

or less, and removing the solvent.

9. A non-aqueous electrolyte secondary battery comprising the laminated porous film according to claim 1 as a separator.