Method for producing conducting and transparent films from combined graphene and conductive nano filaments

• US 20140272172A1
• Filed: 03/14/2013
• Published: 09/18/2014
• Est. Priority Date: 03/14/2013
• Status: Active Grant

• Current Assignee: Global Graphene Group, Inc.
• Original Assignee: Yi-Jun Lin
• Inventors: Zhamu, Aruna, Lin, Yi-jun, Jang, Bor Z.
• Granted Patent: US 8,871,296 B2
• Time in Patent Office: Days
• US Class Current: 427/457
• CPC Class Codes: B05D 1/02 performed by spraying
• CPC Class Codes: B05D 5/12 to obtain a coating with specific electrical properties
• CPC Class Codes: B05D 7/12 to leather chemical treatment of leather C14C; dyeing leather D06P
• CPC Class Codes: B22F 1/0547 Nanofibres or nanotubes
• CPC Class Codes: B22F 2007/042 characterised by the layer forming method
• CPC Class Codes: B22F 7/04 with one or more layers not made from powder, e.g. made from solid metal
• CPC Class Codes: C22C 26/00 Alloys containing diamond or cubic or wurtzitic boron nitride, fullerenes or carbon nanotubes
• CPC Class Codes: C23C 16/26 Deposition of carbon only
• CPC Class Codes: H01B 13/0036 Details
• CPC Class Codes: H01L 31/1884 Manufacture of transparent electrodes, e.g. TCO, ITO
• CPC Class Codes: H10K 30/821 comprising carbon nanotubes
• CPC Class Codes: H10K 71/60 Forming conductive regions or layers, e.g. electrodes
• CPC Class Codes: H10K 85/221 Carbon nanotubes
• CPC Class Codes: Y02E 10/50 Photovoltaic [PV] energy
• CPC Class Codes: Y10S 427/101 Liquid Source Chemical Depostion, i.e. LSCVD or Aerosol Chemical Vapor Deposition, i.e. ACVD

Abstract

A method of producing a transparent and conductive film, comprising (a) forming aerosol droplets of a first dispersion comprising a first conducting nano filaments in a first liquid; (b) forming aerosol droplets of a second dispersion comprising a graphene material in a second liquid; (c) depositing the aerosol droplets of a first dispersion and the aerosol droplets of a second dispersion onto a supporting substrate; and (d) removing the first liquid and the second liquid from the droplets to form the film, which is composed of the first conducting nano filaments and the graphene material having a nano filament-to-graphene weight ratio of from 1/99 to 99/1, wherein the film exhibits an optical transparence no less than 80% and sheet resistance no higher than 300 ohm/square.

Claims

1. A method of producing an optically transparent and electrically conductive film, said method comprising (a) forming aerosol droplets of a first dispersion comprising first conducting nano filaments in a first liquid wherein said nano filaments have a dimension less than 200 nm;

(b) forming aerosol droplets of a second dispersion or solution comprising a graphene material in a second liquid;

(c) depositing said aerosol droplets of a first dispersion and said aerosol droplets of a second dispersion or solution onto a supporting substrate; and

(d) removing the first liquid and the second liquid from the droplets to form said optically transparent and electrically conductive film, which is composed of said first conducting nano filaments and said graphene material having a nano filament-to-graphene weight ratio of from 1/99 to 99/1, wherein said film exhibits an optical transparence no less than 80% and sheet resistance no higher than 300 ohm/square.

2. The method of claim 1, wherein said first conducting nano filaments are selected from metal nanowires, metal nano-rods, metal nanotubes, metal oxide filaments, metal-coated filaments, conducting polymer fibers, carbon nano-fibers, carbon nanotubes, carbon nano-rods, or a combination thereof.

3. The method of claim 2, wherein said metal nanowires are selected from nanowires of silver (Ag), gold (Au), copper (Cu), platinum (Pt), zinc (Zn), cadmium (Cd), cobalt (Co), molybdenum (Mo), aluminum (Al), an alloy thereof, or a combination thereof.

4. The method of claim 2, wherein said metal nanowires contain silver nanowires.

5. The method of claim 2, wherein said metal nanowires contain copper nanowires.

6. The method of claim 2, wherein said metal nanowires are selected from nanowires of a transition metal or an alloy of a transition metal.

7. The method of claim 1, wherein said graphene material is selected from a single-layer or few-layer variant of pristine graphene, graphene oxide, reduced graphene oxide, hydrogenated graphene, nitrogenated graphene, doped graphene, chemically functionalized graphene, or a combination thereof, wherein said few-layer is defined as having less than 10 planes of hexagonal carbon atoms.

8. The method of claim 1, wherein said graphene material is selected from a single-layer or few-layer pristine graphene having 1 to 5 planes of hexagonal carbon atoms.

9. The method of claim 1, wherein said step (a) of forming aerosol droplets of a first dispersion or said step (b) of forming aerosol droplets of a second dispersion or solution is conducted through syringe-based atomization, compressed air-driven atomization, electrostatically-driven atomization, electro-spinning atomization, or a combination thereof.

10. The method of claim 1, wherein said step (c) contains depositing said aerosol droplets of a first dispersion and depositing said aerosol droplets of a second dispersion or solution in a sequential or concurrent manner.

11. The method of claim 1, wherein said step (c) contains depositing said aerosol droplets of a first dispersion onto said supporting substrate to form an aggregate of said first nano filaments prior to depositing said aerosol droplets of a second dispersion or solution to from a graphene film covering said aggregate.

12. The method of claim 1, wherein said step (a) of forming said aerosol droplets of a first dispersion and said step (b) of forming said aerosol droplets of a second dispersion or solution are conducted in one step.

13. The method of claim 1, wherein said step (a) and said step (b) contain dispersing said first conducting filaments and said graphene material in said first liquid, said second liquid, or a mixture of said first liquid and said second liquid to form a hybrid dispersion, which is aerosolized to form a mixture of aerosol droplets of said first dispersion and aerosol droplets of said second dispersion.

14. The method of claim 1, wherein said step (c) contains intermittently or continuously feeding said supporting substrate from a feeder roller into a deposition zone where said aerosol droplets of a first dispersion and aerosol droplets of a second dispersion or solution are deposited onto said supporting substrate to form a transparent conductive film-coated substrate, and the method further contains a step of collecting said coated substrate on a collector roller.

15. The method of claim 1, wherein said aerosol droplets of a first dispersion or aerosol droplets of a second dispersion or solution are propelled to deposit onto said supporting substrate at an impingement speed of at least 1.0 cm/s.

16. The method of claim 1, wherein said aerosol droplets of a first dispersion or aerosol droplets of a second dispersion or solution are propelled to deposit onto said supporting substrate at an impingement speed of at least 10 cm/s.

17. The method of claim 1, wherein said optically transparent and electrically conductive film exhibits an optical transparence no less than 85% and sheet resistance no higher than 100 ohm/square.

18. The method of claim 1, wherein said optically transparent and electrically conductive film exhibits an optical transparence no less than 85% and sheet resistance no higher than 50 ohm/square.

19. The method of claim 1, wherein said optically transparent and electrically conductive film exhibits an optical transparence no less than 90% and sheet resistance no higher than 200 ohm/square.

20. The method of claim 1, wherein said optically transparent and electrically conductive film exhibits an optical transparence no less than 90% and sheet resistance no higher than 100 ohm/square.

21. The method of claim 1, wherein said optically transparent and electrically conductive film exhibits an optical transparence no less than 92% and sheet resistance no higher than 100 ohm/square.

22. The method of claim 1, wherein said supporting substrate is optically transparent.

23. The method of claim 1, wherein said supporting substrate is moved from a feeder roller to a collector roller and the method contains a roll-to-roll procedure.