Sealing glass for laser glass
First Claim
Patent Images
1. A SEALING GLASS FOR LASER GLASS PRODUCED BY ADDING V2O5 0-18 MOL.%, FE2O3 0-18 MOL.%, (V2O5+FE2O3 5-18 MOL.%), CO2O3 0-6 MOL.% AND NIO 0-7 MOL.% TO A BALANCING AMOUNT OF A BASE GLASS CONSISTING OF P2O5 70-30 MOL.%, B2O3 0-15 MOL.%, AL2O3 0-5 MOL.%, (P2O5+B2O3+AL2O3 30-70 MOL.%), PBO 0-55 MOL.%, TL2O 0-55 MOL.%, ZNO 5-50 MOL.%,
0 Assignments
0 Petitions
Accused Products
Abstract
A sealing glass for laser glass produced by adding V2O5 0-18 mol.%, Fe2O3 0-18 mol.%, (V2O5+Fe2O3 5-18 mol.%), Co2O3 0-6 mol.% and NiO 0-7 mol.% to a balancing amount of a base glass composed of P2O5 70-30 mol.%, B2O3 0-15 mol.%, Al2O3 0-5 mol.%, (P2O5+B2O3+Al2O3 30-70 mol.%), PbO 0-55 mol.%, Tl2O 0-55 mol.%, ZnO 5-50 mol.%, (PbO+Tl2O 20-55 mol.%; PbO+Tl2O+ZnO 25-60 mol.%) and BaO 0-10 mol.%.
-
Citations
3 Claims
-
1. A SEALING GLASS FOR LASER GLASS PRODUCED BY ADDING V2O5 0-18 MOL.%, FE2O3 0-18 MOL.%, (V2O5+FE2O3 5-18 MOL.%), CO2O3 0-6 MOL.% AND NIO 0-7 MOL.% TO A BALANCING AMOUNT OF A BASE GLASS CONSISTING OF P2O5 70-30 MOL.%, B2O3 0-15 MOL.%, AL2O3 0-5 MOL.%, (P2O5+B2O3+AL2O3 30-70 MOL.%), PBO 0-55 MOL.%, TL2O 0-55 MOL.%, ZNO 5-50 MOL.%,
-
2. A sealing glass for laser glass according to claim 1 which is produced by adding V2O5 in an amount of 5-18 mol.%.
-
3. A sealing glass for the laser glass according to claim 1 which consists of:
- P2O5 45-50 mol.%, PbO 25-35 mol.%;
Tl2O 5-15 mol.%;
ZnO 5-15 mol.%;
Al2O3 1-5 mol.%;
V2O5 5-15 mol.%.
- P2O5 45-50 mol.%, PbO 25-35 mol.%;
Specification