Polymer fabric compacting process

• US 3,986,828 A
• Filed: 03/05/1974
• Issued: 10/19/1976
• Est. Priority Date: 03/05/1974
• Status: Expired due to Term

• Current Assignee: Meadox Medicals, Inc. (Boston Scientific Corporation)
• Original Assignee: Meadox Medicals, Inc. (Boston Scientific Corporation)
• Inventors: Hoffman, Harmon L. Jr., Tolsma, Jacob
• Primary Examiner(s): Lechert, Jr., Stephen J.
• Application Number:
  US05/448,447
• Time in Patent Office: 959 Days
• Field of Search: 8/115.5, 8/149.2, 8/149.1
• US Class Current: 8/115.68
• CPC Class Codes: A61F 2/06 Blood vessels
• CPC Class Codes: A61F 2002/065 Y-shaped blood vessels
• CPC Class Codes: A61L 27/18 obtained otherwise than by reactions only involving carbon-to-carbon unsaturated bonds
• CPC Class Codes: C08L 67/00 Compositions of polyesters obtained by reactions forming a carboxylic ester link in the main chain of polyester-amides C08L77/12; of polyester-imides C08L79/08; Compositions of derivatives of such polymers

Abstract

Polyester fabric which may be in the form of a warp-knitted lock-stitched or tricot-stitched tubular construction is compacted by treatment with NO₂ either in the gaseous phase or in solution. The product, after neutralization, washing and crimping is suitable for vascular prostheses. In one form, the compacted product is crimped and bifurcated. Shrinkage in both the longitudinal and transverse directions is at least 30%. The porosity of the fabric is reduced by the compacting treatment.

Claims

1. A method of preparing a synthetic vascular graft, comprising the step of treating a porous polyester fabric with a member of the group consisting of gaseous NO₂ and NO₂ in solution in CH₂ Cl₂ under conditions such that said fabric is shrunk and the porosity thereof is reduced, thereby compacting said fabric.

2. The method as defined in claim 1 wherein said solution of NO₂ in CH₂ Cl₂ contains 0.08 to 0.3% water.

3. The method as defined in claim 1 wherein the ratio of NO₂ to CH₂ Cl₂ ranges from 5:

95 to 18;

82 by weight.

4. The method as defined in claim 1 wherein thee ratio of NO₂ to CH₂ Cl₂ ranges from 8:

92 to 10;

90 by weight.

5. The method as defined in claim 1 wherein said polyester is a terephthalic acid ethylene glycol condensate.

6. The method as defined in claim 1 wherein the polyester of said fabric is in the form of a multi-filament thread.

7. The method as defined in claim 1, further comprising the steps of washing said treated fabric with a dilute alkaline solution in sufficient quantity so that the final pH of said solution subsequent to washing the fabric therein is at least 7.0, washing said fabric with a detergent solution, and washing said fabric with water.

8. The method as defined in claim 7 wherein said steps of washing with dilute alkaline solution and with detergent solution are carried out simultaneously by utilizing a dilute alkaline solution containing detergent.

9. The method as defined in claim 7 wherein said dilute alkaline solution consists of about 0.5 to 4.0 g of Na₂ CO₃ /liter of water.

10. The method as defined in claim 7 wherein said detergent solution contains at least one member of the group consisting of octyl phenoxy polyethoxy ethanol, polyoxyethylene ether alcohol, and condensate of ethylene oxide with hydrophobic bases formed by condensing propylene oxide with propylene glycol.

11. The method as defined in claim 1 wherein the time of treatment of said fabric with said member of said group is sufficient to shrink the fabric by at least 30% in the wale direction.

12. The method defined in claim 1 wherein the time of treatment is sufficient to shrink said fabric by at least 40% in the wale direction.

13. The method defined in claim 1 wherein said fabric is a warp-knitted tricot fabric.

14. The method as defined in claim 11 wherein said fabric is tubular in form.

15. The method as defined in claim 14 wherein said tubular fabric is bifurcated.

16. The method as defined in claim 1 wherein said knitted polyester fabric is treated with gaseous NO₂ for at least about two hours.

17. The method as defined in claim 1 wherein said fabric is treated with said solution of NO₂ in CH₂ Cl₂ for at least about 30 seconds.

18. The method as defined in claim 1 wherein said fabric is knitted of a yarn between 40 and 70 denier.

19. The method as defined in claim 18 wherein said 40 denier fabric after compaction has about 55 - 62 wales ×

84 - 90 courses and said 70 denier fabric after compaction has about 45 - 50 wales ×

74 - 80 courses.

20. The method as defined in claim 2 wherein said fabric is knitted of a yarn between 40 and 70 denier.

21. The method as defined in claim 20 wherein said 40 denier fabric after compaction has about 55 - 65 wales ×

85 - 95 courses and said 70 denier fabric after compaction has about 45 - 55 wales ×

74 - 84 courses.

22. The method as defined in claim 1 wherein said polyester fabric prior to treatment has a porosity on the Wesolowski scale above about 20,000.

23. The method of claim 1 wherein said polyester fabric prior to said treatment has a porosity on the Wesolowski scale above about 20,000 and the time of treatment is such as to reduce the porosity of a compacted fabric to between about 30 and about 5,500.

24. The method as defined in claim 23, wherein the time of treatment is such as to reduce the porosity on the Wesolowski scale to between about 1,200 and 4,000.

25. The method as defined in claim 7 wherein said method further comprises the steps of preparing said fabric in the form of a warp-knitted tricot tube prior to compacting said fabric and drying said compacted tube and crimping same into a spiral, thereby imparting relative rigidity to said tube and rendering said tube spring-like longitudinally.

26. The method as defined in claim 25 wherein the treatment is such that said crimped tube has a porosity on the Wesolowski scale between about 800 and 2,500.

27. The method as defined in claim 25 wherein said tube is bifurcated.

28. A polyester fabric compacted by a member of the group consisting of NO₂ and a solution of NO₂ in CH₂ Cl₂.

29. The fabric as defined in claim 28 wherein said solution contains 0.08% - 0.3% of water.

30. The fabric as defined in claim 29 wherein said fabric is a knitted fabric and is knitted of a multi-filament thread having a denier between 40 and 70.

31. The compacted knitted fabric of claim 29 wherein said fabric has between 45 and 65 wales ×

74 and 95 courses.

32. The compacted fabric as defined in claim 28, wherein said fabric is of warp-knitted tricot construction and is tubular in form.

33. The compacted knitted fabric as defined in claim 32 wherein said tubular fabric is spiral-crimped, thereby imparting rigidity to said construction and making same elastic longitudinally.

34. The compacted knitted fabric as defined in claim 33 wherein said tubular fabric is bifurcated.

35. The compacted knitted fabric as defined in claim 33 wherein the porosity of said material on the Wesolowski scale lies between about 30 to 5,500.

36. The compacted knitted fabric as defined in claim 33 wherein the porosity of said material on the Wesolowski scale lies between about 1,200 to 4,000.

37. A knitted fabric as defined in claim 28 wherein said polyester is of multi-filament, polymeric terephthalic acid ethylene glycol condensate having a denier of 40 - 70 and is in the form of crimped bifurcated tube.