Quinary silver alloy
First Claim
Patent Images
1. A quinary Ag-Cu-Zn-Sn-Si alloy having the following composition consisting essentially by weight of about 35 to 48% Ag, about 25 to 35% Zn, about 0.5 to 3.5% Sn, about 0.01 to 0.4% Si, 0 to about 1% Ni, 0 to 1% Pd, 0 to 0.5% P and the balance essentially copper.
0 Assignments
0 Petitions
Accused Products
Abstract
A quinary silver alloy containing copper, zinc and tin as essential elements and also including effective amounts of silicon, is provided capable of a variety of uses and having particular utility as a solder or brazing alloy, the alloy having the following composition by weight:
35 -- 48% Ag
25 -- 35% Zn
0.5 -- 3.5% Sn
0.01 -- 0.4% Si
0 --1% Ni
0 --1% Pd
0 -- 0.5% P
balance -- essentially Cu.
-
Citations
10 Claims
- 1. A quinary Ag-Cu-Zn-Sn-Si alloy having the following composition consisting essentially by weight of about 35 to 48% Ag, about 25 to 35% Zn, about 0.5 to 3.5% Sn, about 0.01 to 0.4% Si, 0 to about 1% Ni, 0 to 1% Pd, 0 to 0.5% P and the balance essentially copper.
- 6. As an article of manufacture, a casting made of a quinary Ag-Cu-Zn-Sn-Si alloy consisting essentially by weight of about 35 to 48% Ag, about 25 to 35% Zn, about 0.5 to 3.5% Sn, about 0.01 to 0.4% Si, 0 to about 1% Ni, 0 to 1% Pd, 0 to 0.5% P and the balance essentially copper.
- 8. A brazed joint comprising metal parts joined together with a braze alloy consisting essentially by weight of about 35 to 48% Ag, about 25 to 35% Zn, about 0.5 to 3.5% Sn, about 0.01 to 0.4% Si, 0 to about 1% Ni, 0 to 1% Pd, 0 to 0.5% P and the balance essentially copper.
Specification