Process for preparing shear degradable particle-containing resin powders

• US 4,057,607 A
• Filed: 12/19/1975
• Issued: 11/08/1977
• Est. Priority Date: 12/19/1975
• Status: Expired due to Term

• Current Assignee: Celanese Corporation
• Original Assignee: Celanese Corporation
• Inventors: Hannon, Martin J., Soehngen, John W.
• Primary Examiner(s): Thurlow, Jeffrey R.
• Application Number:
  US05/642,415
• Time in Patent Office: 690 Days
• Field of Search: 264/140, 264/141, 264/73, 264/75, 264/6, 264/108, 264/109, 264/111, 264/118, 264/175, 264/240, 264/245, 264/211, 264/349, 264/171, 264/323, 264/28, 260/42.22, 425/207, 425/205, 427/195
• US Class Current: 264/28
• CPC Class Codes: C08J 3/226 using a polymer as a carrier
• CPC Class Codes: C08K 3/08 Metals
• CPC Class Codes: C09D 5/03 Powdery paints

Abstract

There is disclosed a process for preparing shear degradable particle-containing resin powders. This process comprises (a) preparing a first composition comprising shear degradable particles and molten resin in the absence of high shearing forces on the particles, (b) intimately blending the first composition with a second composition comprising molten resin and curing agent to form a shear degradable particle-containing molten resin mixture in the absence of high shearing forces on the shear degradable particles, (c) solidifying this shear degradable particle-containing molten resin mixture, and (d) grinding the solidified mixture to desired particle size. The particles may then be classified according to particle size.

The final powder particles contain shear degradable particles or flakes in substantially undegraded form. The powder particles are especially useful in powder coating applications such as in automobile and appliance topcoats.

Claims

1. An improved process for preparing shear degradable particle-containing resin powders which process comprises (a) preparing a first composition consisting essentially of shear degradable particles and molten resin in the absence of high shearing forces on the particles, (b) intimately blending said first composition with a second composition consisting essentially of molten resin and curing agent to form a shear degradable particle-containing molten resin mixture in the absence of high shearing forces on the shear degradable particles and without activating the curing agent, (c) solidifying the shear degradable particle-containing molten resin mixture, and (d) grinding the solidified mixture to desired particle size.

2. The process of claim 1 wherein said first composition is intimately blended with said second composition by extruding the first composition from a piston extruder into a static mixer where the first composition is intimately mixed with the second composition.

3. The process of claim 2 wherein both the first and second compositions each contain a pigment which is added in the form of a pigment concentrate comprising about 50 percent by weight pigments and about 50 percent by weight resin.

4. The composition of claim 3 wherein the final powder particles are classified according to particle size.

5. The process of claim 4 wherein said blending step takes place at a temperature of from about 100°

to about 135°

C, and wherein said process is carried out at substantially atmospheric pressure.

6. The process of claim 1 wherein the final powder particles have a mean average diameter of from about 30 to about 100 microns.

7. The process of claim 6 wherein said first composition comprises from about 50 to about 95 percent by weight resin and from about 5 to about 50 percent by weight shear degradable particles and wherein said second composition comprises from about 55 to about 95 percent resin, and from about 2 to about 60 percent by weight curing agent.

8. A process for preparing shear degradable particle-containing resin powders which process comprises (a) preparing a first composition consisting essentially of (1) shear degradable metal particles, (2) molten resin, and (3) a pigment concentrate comprising about 50 percent by weight pigment and about 50 percent by weight molten resin, (b) intimately blending said first composition with a second composition consisting essentially of a curing agent and molten resin mixture in the absence of high shearing forces on the shear degradable metal particles and without activating the curing agent, (c) solidifying this shear degradable metal particle-containing molten resin mixture, and (d) grinding the solidified mixture to desired particle size.

9. The process of claim 8 wherein the resin is poly (methyl methacrylate) and the shear degradable metal particles are aluminum flake.

10. The process of claim 8 wherein the final powder particles have a mean average diameter of from about 40 to about 80 mcirons.

11. The process of claim 9 wherein said blending step takes place at a temperature of from about 105°

to about 130°

C and wherein said process is carried out at substantially atmospheric pressure.

12. The process of claim 11 wherein both the first and the second compositions contain a pigment which is added in the form of a pigment concentrate comprising about 50 percent by weight pigment and about 50 percent by weight resin.

13. The process of claim 12 wherein said first composition comprises from about 60 to about 90 percent by weight resin and from about 10 to about 40 percent by weight shear degradable metal particles and wherein said second composition comprises from about 60 to about 90 percent resin, and from about 10 to about 40 percent by weight curing agent.

14. A process for preparing shear degradable metal particle-containing resin powders which process comprises (a) preparing a first composition consisting essentially of from about 15 to about 25 percent by weight shear degradable aluminum flake and from about 75 to about 85 percent by weight polymeric acrylic resin in the absence of high shearing forces on the shear degradable aluminum flake, (b) intimately blending at a temperature of from about 110°

to about 125°

C, and at substantially atmospheric pressure, said first composition with a second composition consisting essentially of from about 65 to about 85 percent by weight polymeric acrylic resin, and from about 15 to about 35 percent by weight curing agent to form a shear degradable aluminum flake-containing molten resin mixture, in the absence of high shearing forces on the shear degradable aluminum flake and without activating the curing agent, (c) solidifying this shear degradable aluminum flake-containing molten resin, at a temperature of from about 0°

to about 60°

C, and (d) grinding the solidified mixture to particles having a mean average diameter of from about 50 to about 65 microns.

15. The process of claim 14 wherein said first composition is intimately blended with said second composition by extruding the first composition from a piston extruder into a static mixer where the first composition is intimately mixed with the second composition.