Purification of exhaust gases

• US 4,061,713 A
• Filed: 08/30/1976
• Issued: 12/06/1977
• Est. Priority Date: 08/30/1975
• Status: Expired due to Term

• Current Assignee: Kali-Chemie AG
• Original Assignee: Kali-Chemie AG
• Inventors: Lecloux, Andre, Weidenbach, Guenter, Gobillon, Yves
• Primary Examiner(s): Peters, G. O.
• Application Number:
  US05/718,512
• Time in Patent Office: 463 Days
• Field of Search: 423/213.2, 423/213.5
• US Class Current: 423/213.5
• CPC Class Codes: B01D 53/945 characterised by a specific catalyst
• CPC Class Codes: B01J 23/6525 Molybdenum
• CPC Class Codes: Y02A 50/20 Air quality improvement or preservation, e.g. vehicle emission control or emission reduction by using catalytic converters
• CPC Class Codes: Y02T 10/12 Improving ICE efficiencies

Abstract

Disclosed is a method of purifying exhaust gases from an internal combustion engine operated with a substantially stoichiometric fuel-to-air mixture, the gases having an L-value of from about 0.8 to 1.2, wherein the exhaust gases are brought into contact with a catalyst comprising molybdenum, rhodium and, optionally, platinum supported on a carrier.

Claims

1. In a process for purifying exhaust gases from an internal combustion engine being operated with a substantially stoichiometric fuel-to-air mixture, said exhaust gases containing hydrocarbons (C_n H_2n+2), carbon monoxide and nitric oxide and having an L-value of between about 0.8 and 1.2 where ##EQU5## and n is an integer, comprising the step of contacting said exhaust gases at an elevated temperature with a catalyst supported on a carrier which has been calcined at a temperature of at least about 800°

C, whereby said hydrocarbons, carbon monoxide and nitric oxide are simultaneously removed from said exhaust gases, the improvement comprising said catalyst essentially consisting of said carrier having distributed thereon a mixture from about 0.01 to 0.1% by weight each of molybdenum and rhodium and from 0 to about 0.1% by weight of platinum.

2. The process as defined by claim 1, wherein said molybdenum and rhodium are present in said catalyst in an atomic ratio of from about 1:

1 to 4;

1.

3. The process as defined by claim 1, wherein said catalyst contains from about 0.02 and 0.08% by weight of molybdenum and from about 0.02 to 0.04% by weight of rhodium.

4. The process as defined in claim 1, wherein said catalyst further comprises platinum.

5. The process as defined by claim 4, wherein said catalyst contains between about 0.01 and 0.1% by weight of platinum.

6. The process as defined by claim 3, wherein said catalyst further comprises from about 0.04 to 0.08% by weight of platinum.

7. The process as defined by claim 2, wherein said ratio is about 2:

1.

8. The process as defined by claim 1, wherein the temperature of the exhaust gas is in the range of 300°

to 1000°

C.