Process for making thermoplastic elastomeric articles

• US 4,089,718 A
• Filed: 11/26/1975
• Issued: 05/16/1978
• Est. Priority Date: 11/26/1975
• Status: Expired due to Term

• Current Assignee: Gleason Corporation (Gleason)
• Original Assignee: Amerace Corporation (ABB Limited)
• Inventors: Triolo, Louis J., Morgan, Donald F.
• Primary Examiner(s): Thurlow, Jeffery R.
• Application Number:
  US05/635,697
• Time in Patent Office: 902 Days
• Field of Search: 264/176 R, 264/201, 264/315, 264/209, 264/326, 264/150, 264/94, 264/96, 264/98, 264/331, 260/33.6 AQ, 260/897 A, 152/330 R, 152/357 A, 156/118, 156/122, 156/503, 156/113
• US Class Current: 156/122
• CPC Class Codes: B29D 30/00 Producing pneumatic or solid tyres or parts thereof producing inner tubes B29D23/24; constructional form of tyres or parts thereof B60C; connection of valves to inflatable elastic bodies B60C29/00; testing of tyres G01M17/02
• CPC Class Codes: B29D 30/02 Solid tyres ; Moulds therefor
• CPC Class Codes: B60C 1/00 Tyres characterised by the chemical composition or the physical arrangement or mixture of the composition

Abstract

A process for producing thermoplastic, elastomeric articles such as, for example, semi-pneumatic tires, comprising the steps of admixing a thermoplastic, elastomeric molding composition including a vulcanizable or otherwise thermosetable elastomer, inert filler materials, a plasticizer and certain processing aids. The molding composition is then milled into a flat sheet, extruded into a tubular shape, cut, shaped and then molded at a temperature less than about 70° F into thermoplastic elastomeric articles such as, for example, semi-pneumatic tires.

Claims

1. A process for producing a useful thermoplastic, elastomeric article such as, for example, a semi-pneumatic tire, said process comprising the steps of:

a. forming a molding composition consisting essentially of;

i. a vulcanizable EPDM elastomeric terpolymer in an amount within the range of from about 25% to about 28% by weight of the total composition;

ii. an inert filler free from polyolefins in an amount within the range of from about 52% to about 56% by weight of the total composition, said filler comprising a blend of different filler materials; and

iii. the remainder of said composition being made up of plasticizers and processing aids;

b. extruding said molding composition into a tubular form;

c. shaping said tubularly formed composition into an unmolded article of a predetermined shape;

d. maintaining said unmolded article of predetermined shape at a temperature within a range from about 270°

F to about 300°

F to facilitate molding;

e. introducing said unmolded article at said temperature to facilitate molding, into a mold; and

f. molding said unmolded article of predetermined shape free from vulcanization at a temperature substantially below said temperature of said unmolded article into said useful thermoplastic, elastomeric article and wherein the step (f) of molding said unmolded article of predetermined shape further comprises the steps of maintaining said mold at a temperature within a range from about 50°

F to about 70°

F, sealing said mold and causing said outer tubular portion to expand and conform to the inner surface of said mold.

3. The process of claim 1 wherein the step of combining said molding composition comprises the step of admixing said molding composition in a Banbury mixer at a temperature in the range from about 290°

F to about 370°

F.

4. The process of claim 1 further including the step of milling said composition into sheet form after combining and prior to extruding.

5. The process of claim 1 wherein the step of extruding said molding composition comprises the step of extruding said molding composition in a heated, short barrel extruder at a temperature within the range of from about 270°

F to about 325°

F.

6. The process of claim 1 wherein the step of shaping said tubularly formed composition comprises the steps of cutting said tubularly formed composition into sections of predetermined length and joining the ends thereof to form a ring shaped unmolded article having an outer tubular portion.

7. The process of claim 1 wherein the step of maintaining said unmolded article of predetermined shape at said temperature includes the step of preheating said unmolded article to said temperature within said range from about 270°

F to about 300°

F.

8. The process of claim 6 wherein said outer tubular portion includes a hollow center and wherein the step of causing said outer tubular portion to expand comprises the step of introducing compressed air into the hollow center of said outer tubular portion with a means adapted to penetrate into said hollow center.

2. A process for producing a thermoplastic, elastomeric, semi-pneumatic tire, said process comprising the steps of:

a. combining in a Banbury mixer at a temperature of about 325°

a composition consisting essentially of the following;

i. vulcanizable elastomeric EPDM terpolymer in an amount within the range of from about 25% to about 28% by weight of the total composition, wherein the ethylene content of said elastomeric terpolymer is in the range from about 65% to about 85% by weight of the total terpolymer, wherein the diene content of said terpolymer is no greater than about 4% by weight of the total terpolymer and wherein the viscosity of said terpolymer is in the range of from about 50 to 80 Mooney;

ii. inert filler materials free from polyolefins in an amount within the range from about 52% to about 56% by weight of the total composition, said filler materials comprising a blend of different inert filler materials, said blend being selected from the group consisting of carbon black, coal dust, clay, calcium carbonate, silica, and phenolic resin;

iii. a plasticizer in an amount within the range from about 15% to about 18% by weight of the total composition, said plasticizers consisting of naphthenic oil; and

iv. processing aids in an amount within the range of up to about 3% by weight of the total composition, said processing aids being selected from the group consisting of antioxidants, and lubricants;

b. milling said composition into sheet form;

c. extruding said sheet-like composition at a temperature within the range of from about 280°

F to about 300°

F into a tubular form having a hollow center;

d. cutting said tubularly shaped composition into sections of predetermined length and mechanically splicing together the ends thereof to form a ring-shaped unmolded article;

e. introducing said ring-shaped, unmolded article, maintained at a temperature of about 270°

F into a compression mold maintained at a temperature below about 70°

F; and

f. molding said ring-shaped, unmolded article into a semi-pneumatic tire free from vulcanization by sealing said mold, inserting at least one needle into the hollow center of the tubular portion of said ring-shaped unmolded article, and introducing air pressure into said hollow center to expand the tubular portion of said ring-shaped unmolded article against the inner surface of said mold.