Polyurethane adhesives having high peel strength at 70.degree. C

• US 4,098,747 A
• Filed: 05/24/1976
• Issued: 07/04/1978
• Est. Priority Date: 06/20/1975
• Status: Expired due to Term

• Current Assignee: Interox Chemical Limited
• Original Assignee: Interox Chemical Limited
• Inventors: Bunker, Anthony John, Bailey, Brian Edward
• Primary Examiner(s): Cockeram, H.S.
• Application Number:
  US05/688,946
• Time in Patent Office: 771 Days
• Field of Search: 260/77.5 AN, 260/77.5 TB, 260/32.8 N, 260/30.4 N, 260/32.6 N
• US Class Current: 524/98
• CPC Class Codes: C08G 18/12 using two or more compounds having active hydrogen in the first polymerisation step
• CPC Class Codes: C08G 18/2805 Compounds having only one group containing active hydrogen vinylpolymers having terminal groups containing active hydrogen C08G18/62
• CPC Class Codes: C08G 18/664 with compounds of group C08G18/3203
• CPC Class Codes: C08G 2170/20 Compositions for hot melt adhesives
• CPC Class Codes: C08G 2250/00 Compositions for preparing crystalline polymers
• CPC Class Codes: C09J 175/06 from polyesters

Abstract

An adhesive composition which comprises a polyurethane comprising (a) units derived from a diisocyanate, (b) units derived from a poly (ε-caprolactone) diol having a hydroxyl value of from 25 to less than 30, and (c) units derived from an alkane diol chain lengthening agent containing at least 2 carbon atoms, the mole ratio of alkane diol:poly (ε-caprolactone) diol being from greater than 0.7:1.0 to less than 1.2:1.0. The adhesive may be used in solid form or dissolved in an organic solvent. The adhesive has improved hot bond strength and is particularly useful for bonding shoe soles to shoe uppers.

Claims

1. An adhesive composition having a peel strength at 70°

C. of at least about 2.4 Kg/cm which comprises a polyurethane comprising (a) units derived from a diisocyanate, (b) units derived from a poly (ε

-caprolactone) diol having a hydroxyl value of from 25 to less than 30, and (c) units derived from an alkane diol chain lengthening agent containing at least 2 carbon atoms, the mole ratio of alkane diol;

poly(ε

-caprolactone) diol being from greater than 0.7;

1.0 to less than 1.2;

1.0 and the ratio of moles of diisocyanate to the total of the number of moles of poly(ε

-caporlactone) diol and the number of moles of alkane diol in the polyurethane is from 1.0;

1.0 to 1.04;

1.00.

2. An adhesive composition according to claim 1 wherein the alkane diol is butane 1,4 diol.

3. An adhesive composition according to claim 1 wherein the poly(ε

-caprolactone) diol, from which the said units are derived, is prepared by reacting together in the presence of a catalyst at a temperature not exceeding 160°

C., ε

-caprolactone and a glycol containing from 2 to 10 carbon atoms.

4. An adhesive composition according to claim 3 wherein the glycol is tetramethylene glycol.

5. An adhesive composition according to claim 1 wherein the diisocyanate, from which the said units are derived is 4,4'"'"'-di-isocyanato-diphenylmethane.

6. An adhesive composition according to claim 1 which additionally contains an isocyanate blocking agent in an amount of from 0.1% to 10.0% by weight based on the weight of polyurethane.

7. An adhesive composition according to claim 6 wherein the blocking agent is ε

-caprolactam.

8. An adhesive composition according to claim 1 which additionally contains an organic solvent for the polyurethane, selected from the group consisting of acetone, methyl ethyl ketone, tetrahydrofuran, dioxane and dimethylformamide.

9. An adhesive composition according to claim 8 which additionally contains a trifunctional isocyanate compound present in an amount of from 15% to 25% by weight, on weight of polyurethane.

10. A process for the preparation of an adhesive composition according to claim 1 comprising reacting together, at a temperature of from 100°

to 140°

C. for a period of 1/2 hour to 24 hours, a diisocyanate, a poly(ε

-caprolactone) diol having a hydroxyl value of from 25 to less than 30, and from greater than 0.7 to less than 1.2 moles per mol of the poly(ε

-caprolactone) diol of an alkane diol chain lengthening agent containing at least 2 carbon atoms.

11. A process according to claim 10 wherein the ratio of moles of diisocyanate to the total of the number of moles of poly(ε

-caprolactone) diol and moles of alkane diol in the polyurethane is from 1.00;

1.00 to 1.04;

1.00.

12. A process according to claim 10 wherein the alkane diol is butane 1,4 diol.

13. A process according to claim 10 wherein the poly(ε

-caprolactone) diol used is prepared by reacting together in the presence of a catalyst at a temperature not exceeding 160°

C., ε

-caprolactone and a glycol containing from 2 to 10 carbon atoms.

14. A process according to claim 13 wherein the glycol is tetramethylene glycol.

15. A process according to claim 10 wherein the diisocyanate is 4,4'"'"'-di-isocyanato-diphenylmethane.