Electromagnetic wave-absorbing wall

• US 4,118,704 A
• Filed: 03/30/1977
• Issued: 10/03/1978
• Est. Priority Date: 04/07/1976
• Status: Expired due to Term

• Current Assignee: TDK Corporation
• Original Assignee: TDK Electronics (TDK Corporation)
• Inventors: Yamashita, Hiroshi, Ishino, Ken, Ono, Nobuyuki, Hashimoto, Yasuo
• Primary Examiner(s): Dixon, Jr., William R.
• Application Number:
  US05/782,779
• Time in Patent Office: 552 Days
• Field of Search: 343/18 A, 428/44, 428/47, 428/48, 428/49, 52/144, 52/145
• US Class Current: 342/4
• CPC Class Codes: H01Q 17/008 with a particular shape H01Q17/007 takes precedence
• CPC Class Codes: Y10S 428/90 Magnetic feature
• CPC Class Codes: Y10T 428/163 Next to unitary web or sheet of equal or greater extent
• CPC Class Codes: Y10T 428/164 Continuous two dimensionally sectional layer
• CPC Class Codes: Y10T 428/166 Glass, ceramic, or metal sections [e.g., floor or wall tile, etc.]

Abstract

Electromagnetic wave-absorbing wall comprising ferrimagnetic plates arranged at some intervals in the direction of the electric field of the electromagnetic wave said ferrimagnetic plates being plates of ferrite having the following general formula:

MFe.sub.2 O.sub.4

wherein M is a bivalent metal such as Mn, Ni, Co, Mg, Cu, Zn and Cd, or plates of a mixture of ferrite powders or carbonyl iron with organic high molecular weight compounds, and said plates having a specified thickness according to the interval.

Claims

1. An electromagnetic wave-absorbing wall comprising an array of ferrimagnetic plates affixed by one face to the surface of an electroconductive substrate arranged at spaced-apart intervals in the direction of the electric field of the electromagnetic wave and closely in the direction of the magnetic field thereof, in which the rate of interval and the thickness of ferrimagnetic plates are arranged according to the following relationship:

space="preserve" listing-type="tabular">______________________________________ Rate of Interval Thickness of ferrimagnetic plate ##STR21## (d) ______________________________________ <

20% 0.5d.sub.o ˜

1.5d.sub.o 20% ˜

40% 0.7d.sub.o ˜

2.0d.sub.o 40% ˜

60% 1.0d.sub.0 ˜

2.5d.sub.o 60% ˜

80% 1.5d.sub.o ˜

4.5d.sub.o ______________________________________

wherein "l" is the width of the ferrimagnetic plate, "g" is the interval between the ferrimagnetic plates, "d_o " is the thickness of ferrimagnetic plate which would result in maximum attenuation at no interval between plates, and "d" is the thickness of the ferrimagnetic plate at said interval.

2. An electromagnetic wave-absorbing wall according to claim 1, said ferrimagnetic plate being a plate of a ferrites having the general formula:

space="preserve" listing-type="equation">MFe.sub.2 O.sub.4

wherein M is bivalent metal such as Mn, Ni, Co, Mg, Cu, Zn and Cd.

3. An electromagnetic wave-absorbing wall according to claim 1 wherein said ferrimagnetic plate is a plate of a mixture of ferrite powders with an insulating organic high molecular weight compound.

4. An electromagnetic wave-absorbing wall according to claim 3 wherein said insulating organic high molecular weight compound is selected from the group consisting of synthetic rubber, thermoplastic resin and thermosetting resin.

5. An electromagnetic wave-absorbing wall according to claim 1 wherein said ferrimagnetic plate is a plate of a mixture of carbonyl iron with an insulating organic high molecular weight compound.

6. An electromagnetic wave-absorbing wall according to claim 5 wherein said insulating organic high molecular compound is selected from the group consisting of synthetic rubber, thermoplastic resin and thermosetting resin.

7. An electromagnetic wave-absorbing wall according to claim 1 wherein said ferrimagnetic plates are affixed directly to said substrate.

8. An electromagnetic wave-absorbing wall according to claim 1 wherein said ferrimagnetic plates are arrayed in uniform columns in the direction of said magnetic field.

9. An electromagnetic wave-absorbing wall according to claim 1 wherein said ferrimagnetic plates are arrayed in partially staggered rows in the direction of said magnetic field.