Preparation of highly active copper-silica catalysts
First Claim
Patent Images
1. In a method for preparing highly active and selective linolenate-reducing, copper-silica catalysts including the steps of:
- a. reacting sodium silicate from an aqueous solution with a water-soluble copper salt to form a precipitate;
b. recovering said precipitate from said aqueous solution;
c. drying said recovered precipitate from step (b); and
d. heat treating said dried precipitate from step (c) at a temperature in the range of 350°
-625°
C. to yield said catalyst,the improvement comprising conducting said drying in step (c) under a vacuum at room temperature or less.
0 Assignments
0 Petitions
Accused Products
Abstract
Highly active and selective linolenate-reducing, copper catalysts are prepared by vacuum drying copper-silica coprecipitates, and then activating the precipitates by heat treatment. The resultant catalysts are characterized by activities 2-3.5 times those of commercial copper chromites and also possess comparable linolenate selectivities.
-
Citations
6 Claims
-
1. In a method for preparing highly active and selective linolenate-reducing, copper-silica catalysts including the steps of:
-
a. reacting sodium silicate from an aqueous solution with a water-soluble copper salt to form a precipitate; b. recovering said precipitate from said aqueous solution; c. drying said recovered precipitate from step (b); and d. heat treating said dried precipitate from step (c) at a temperature in the range of 350°
-625°
C. to yield said catalyst,the improvement comprising conducting said drying in step (c) under a vacuum at room temperature or less. - View Dependent Claims (2, 3, 4, 5, 6)
-
Specification