Insulated wire and method for producing same

• US 4,186,241 A
• Filed: 12/04/1978
• Issued: 01/29/1980
• Est. Priority Date: 12/03/1977
• Status: Expired due to Term

• Current Assignee: Dr BECK & Company AG
• Original Assignee: Dr BECK & Company AG
• Inventors: Janssen, Harald
• Primary Examiner(s): Simmons, David A.
• Application Number:
  US05/965,919
• Time in Patent Office: 421 Days
• Field of Search: 156/51, 156/52, 156/244.11, 174/110 SR, 174/110 N, 264/174, 428/458, 260/842, 260/850, 528/340, 427/117, 427/118, 427/120
• US Class Current: 428/458
• CPC Class Codes: H01B 13/14 by extrusion extrusion in general B29C48/00
• CPC Class Codes: H01B 3/305 Polyamides or polyesteramides
• CPC Class Codes: Y10T 428/31681 Next to polyester, polyamide or polyimide [e.g., alkyd, glue, or nylon, etc.]

Abstract

A partially crystalline thermoplastic polyamide for use in the preparation of insulated wires through the extrusion of a thermoplastic coating, consisting of terephthalic acid or a functional derivative thereof, hexamethylenediamine and isophoronediamine; also disclosed are a process for the preparation of insulated wires using the above polyamine; and an insulated wire employing such polyamide as the thermoplastic coating.

Claims

1. A partially crystalline thermoplastic polyamide for use in the preparation of insulated wires through the extrusion of a thermoplastic coating, said polyamide comprising an acid component and an amine component in a ratio of 1:

1 to 1;

1.1, wherein said acid component is terephthalic acid or a functional derivative thereof, and said amine component consists of hexamethylenediamine and isophoronediamine, said isophoronediamine comprising at least 5 Mol % of the total amine component.

2. The polyamide of claim 1, wherein the ratio of said acid component to said amine component is about 1:

1.

3. The polyamide of claim 1, wherein said isophoronediamine comprises between 5 and 20 Mol % of the total amine component.

4. The polyamide of claim 1, wherein said isophoronediamine comprises between 8 and 15 Mol % of the total amine component.

5. The polyamide of claim 1, wherein said isophoronediamine comprises about 12 Mol % of the total amine component.

6. A process for the preparation of insulated wires through the extrusion of a thermoplastic coating, involving the use of a partially crystalline thermoplastic polyamide, said polyamide comprising an acid component and an amine component in a ratio of 1:

1 to 1;

1.1, wherein said acid component is terephthalic acid or a functional derivative thereof, and said amine component consists of hexamethylenediamine and isophoronediamine, said isophoronediamine comprising at least 5 Mol % of the total amine component, said process comprising passing a conductor wire through a coating zone of an extruder to coat said wire; and

treating said wire to regulate the thickness of the applied coating.

7. The process of claim 6, wherein said conductor wire is preheated before passage through said coating zone of said extruder.

8. An insulated wire having an extruded thermoplastic coating of a partially crystalline thermoplastic polyamide, said polyamide comprising an acid component and an amine component in a ratio of 1:

1 to 1;

1.1, wherein said acid component is terephthalic acid or a functional derivative thereof, and said amine component consists of hexamethylenediamine and isophoronediamine, said isophoronediamine comprising at least 5 Mol % of the total amine component.