Resin impregnated aromatic polyamide covered glass based slot wedge for large dynamoelectric machines

• US 4,200,818 A
• Filed: 08/01/1978
• Issued: 04/29/1980
• Est. Priority Date: 08/01/1978
• Status: Expired due to Term

• Current Assignee: Westinghouse Electric Company LLC (Brookfield Asset Management Incorporated)
• Original Assignee: Westinghouse Electric Company LLC (Brookfield Asset Management Incorporated)
• Inventors: Gause, Smith A., Ruffing, Charles R., Smith, Harry E., Botts, John C.
• Primary Examiner(s): Dixon, Jr., William R.
• Application Number:
  US05/930,090
• Time in Patent Office: 637 Days
• Field of Search: 310/214, 310/215, 428/37, 428/74, 428/213, 428/215, 428/267, 428/268
• US Class Current: 310/214
• CPC Class Codes: H02K 15/0018 Applying slot closure means in the core; Manufacture of slot closure means
• CPC Class Codes: H02K 3/487 Slot-closing devices
• CPC Class Codes: H02K 3/493 magnetic
• CPC Class Codes: Y10S 174/19 in a dynamo-electric machine
• CPC Class Codes: Y10T 428/2495 Thickness [relative or absolute]
• CPC Class Codes: Y10T 428/24967 Absolute thicknesses specified

Abstract

An iron engaging slot wedge, for use in coil slots of dynamoelectric machines is made of a glass fiber core impregnated with a cured thermoset resin, and covered on at least two sides with a facing layer of a porous aromatic polyamide mat, impregnated with a cured thermoset resin.

Claims

1. An iron engaging slot wedge adapted to be positioned in the coil slots of a dynamoelectric machine comprising a glass fiber core impregnated with a cured thermoset resin, and covered, on at least two sides, with a facing layer of a mat of aromatic polyamide fiber, impregnated with a cured thermoset resin.

2. The slot wedge of claim 1, having an interlaminar shear strength of over about 2,500 lb./in. of length at 100°

C.

3. The slot wedge of claim 1, wherein the glass fiber core is in spiral form, and the facing layer covers the iron engaging sides of the wedge.

4. The slot wedge of claim 1, wherein the facing layer is a single layer in non-woven form and the thickness ratio of glass fiber core:

facing layer is between about 10;

1 to about 100;

1.

5. The slot wedge of claim 1, wherein the glass fiber core is between about 0.2 inch to 0.5 inch thick and impregnated between about 40 wt.% to about 60 wt.% with a cured resin selected from the group consisting of epoxy resin and phenolic resin.

6. The slot wedge of claim 1, wherein the facing layer is between 0.005 inch to about 0.025 inch thick, impregnated with a cured resin selected from the group consisting of epoxy resin and phenolic resin, and the aromatic polyamide consists essentially of a poly (phenylenephthalamide) having about 95% to 100% resiliency against compaction.

7. The slot wedge of claim 6, wherein the facing layer consists essentially of a poly (phenylenephthalamide) having a tensile strength of over about 250,000 lb./sq.in.

8. The slot wedge of claim 6, wherein the aromatic polyamide consists essentially of poly (1,4-phenyleneterephthalamide).

9. The slot wedge of claim 6 wherein the core resin impregnant is an epoxy resin and the facing layer resin impregnant is a phenolic resin.

10. A generator comprising a stator containing a plurality of slot wedges having the construction of claim 6.

11. In the coil slot of a dynamoelectric machine, a laminated, slot wedge facing wound coils consisting essentially of a glass fiber core impregnated between about 40 wt.% to about 60 wt.% with a cured thermoset resin, and covered, on at least two sides, with a resilient facing layer consisting essentially of a poly (phenylenephthalamide) fiber matrix of at least 70% porosity, impregnated with about 60 wt.% to about 80 wt.% of a cured thermoset resin, said slot wedge having an interlaminar shear strength of over about 2,500 lb./in. of length at 100°

C.

12. The slot wedge of claim 11, wherein the facing layer consists essentially of poly (1,4-phenyleneterephthalamide), the core resin impregnant is an epoxy resin, the covering layer resin impregnant is a phenolic resin, the thickness ratio of glass fiber core:

facing layer is between about 10;

1 to about 100;

1; and

the thickness of the core is between about 0.2 inch to about 0.5 inch.