• US 4,209,481 A
• Filed: 01/24/1979
• Issued: 06/24/1980
• Est. Priority Date: 04/19/1976
• Status: Expired due to Term

• Current Assignee: Toray Industries Incorporated
• Original Assignee: Toray Industries Incorporated
• Inventors: Kataoka, Shunro, Kashiro, Yoshikazu, Matsugasako, Kenji
• Primary Examiner(s): Hoag, W. E.
• Application Number:
  US06/006,009
• Time in Patent Office: 517 Days
• Field of Search: 428/389, 428/900, 428/294, 264/108, 264/24, 264/299, 264/338, 264/271, 264/272, 425/174.8 R, 425/174.8 E, 29/629, 29/630 B
• US Class Current: 264/437
• CPC Class Codes: B29C 70/14 oriented
• CPC Class Codes: B29C 70/882 partly or totally electrically conductive, e.g. for EMI shielding conductive floors or floor coverings H05F3/025; EMI shielding in general H05K9/00
• CPC Class Codes: B29K 2995/0005 Conductive
• CPC Class Codes: B29K 2995/0044 Anisotropic
• CPC Class Codes: B29L 2007/002 Panels; Plates; Sheets
• CPC Class Codes: H01B 5/16 comprising conductive material in insulating or poorly conductive material, e.g. conductive rubber H01B1/14, H01B1/20 take precedence; insulating bodies with conductive admixtures H01B17/64; conductive paints C09D5/24
• CPC Class Codes: H01R 13/2414 conductive elastomers
• CPC Class Codes: Y10T 29/4921 with bonding

Abstract

An anisotropically electroconductive sheet of a non-electroconductive elastomer and electroconductive wires which have a length substantially the thickness of the sheet. The electroconductive wires are oriented from each other and are formed into patterned wire groupings, which are in turn formed into patterns. The wires in the groupings are parallel in the directions of the sheet thickness, and the wires are spaced from each other in the wire groupings, and are thereby electrically insulated from each other.

Claims

1. A process for producing an anisotropically electroconductive sheet which comprises;

(a) mixing magnetic electroconductive wires having a substantially uniform length into a non-electroconductive liquid matrix.

(b) pouring the mixture into a cavity formed between two parallel planes, the distance between the planes being greater than the length of the electroconductive wires;

(c) generating a magnetic field in the direction perpendicular to said parallel planes and orienting the electroconductive wires in the matrix to the magnetic field direction then;

(d) decreasing the distance between said planes to a length not longer than that of the electroconductive wires, and

(e) hardening the liquid matrix.

2. The process as defined in claim 1, wherein the surfaces of said two planes in contact with said mixture are coated with a layer of a soft, inert material.

3. The process as defined in claim 1, wherein the matrix is a prepolymer of a polymer selected from the group consisting of polyurethane and silicone.

4. The process as defined in claim 1, wherein said electroconductive wires comprise a magnetic metal selected from the group consisting of iron, nickel, cobalt, and an alloy composed of at least one of said metals as a main component.

5. A process as defined in claim 1, wherein said electroconductive wires comprise a non-conductive material coated with a magnetic metal.

6. The process as defined in claim 1, wherein the magnetic field is arranged in a direction at an incline to the normal to the two parallel planes prior to said step (c).

7. The process as defined in claim 6, including the step of varying the inclination of said magnetic field.

8. The process as defined in claim 6, wherein the degree of inclination is at least 5°

from the normal.

9. The process as defined in claim 6 wherein, the degree of inclination is at least 10°

from the normal.

10. A process for producing an anisotropically electroconductive sheet which comprises:

(a) mixing a plurality of magnetic electroconductive wires having substantially uniform lengths into a non-electroconductive hardenable fluid matrix;

(b) maintaining the mixture as a sheet-like form;

(c) placing a magnetic plate having a multiplicity of protrusions formed on its surface against said sheet-like mixture;

(d) generating a magnetic field so that the electroconductive wires are caused to gather to the protrusions on the magnetic plate and to be oriented in the thickness direction of the sheet, and

(e) hardening the fluid matrix.