Multiple electrode submerged arc welding method

• US 4,214,141 A
• Filed: 12/29/1978
• Issued: 07/22/1980
• Est. Priority Date: 12/29/1977
• Status: Expired due to Term

• Current Assignee: Kobe Steel Limited
• Original Assignee: Kobe Steel Limited
• Inventors: Okuda, Naoki, Nakano, Akira
• Primary Examiner(s): Kucia, Richard R.
• Application Number:
  US05/974,546
• Time in Patent Office: 571 Days
• Field of Search: 219/73 R, 219/137 R, 148/26
• US Class Current: 219/73
• CPC Class Codes: B23K 35/362 Selection of compositions of fluxes B23K35/365, B23K35/368 take precedence
• CPC Class Codes: B23K 9/188 making use of several electrodes

Abstract

A submerged arc welding method and more specifically, a multiple electrode welding method is disclosed wherein welding is performed by arranging electrodes in such a manner that the distance becomes at least 300 mm between a first molten pool formed by multilayer welding or by a single or plural electrodes preceding along the weld line and a subsequent molten pool formed by a single subsequent electrode or plural subsequent electrodes, as well as a submerged arc welding method which is characterized in that there is formed a slag having the components listed below on the weld metal formed by an electrode or a preceding electrode forming a preceding layer, and welding is carried out as such, without removing the slag, using an electrode or a subsequent electrode forming a subsequent layer;

TiO₂ : 20-65% by weight (up to 60% by weight, based on the total TiO₂ amount, of which may be substituted by ZrO₂);

CaF₂ : 9.6-40% by weight, and

Al₂ O₃ : 10-56% by weight.

Claims

1. A multiple electrode welding method which comprises:

arranging a plurality of electrodes in such a manner that the distance is at least 300 mm between a first molten pool formed by multilayer welding by a single or a plurality of electrodes preceding along a weld line and a subsequent molten pool formed by a single subsequent electrode or plurality of subsequent electrodes;

forming slag having a composition which comprises;

TiO₂ ;

20-65% by weight

CaF₂ ;

9.6-40% by weight, and

Al₂ O₃ ;

10-56% by weight

on weld metal formed by an electrode or a preceding electrode forming a preceding layer, and

welding along said weld line, without removing said slag, using said single subsequent electrode or said subsequent plurality of electrodes for forming said subsequent molten pool layer.

2. The submerged arc welding method as defined in claim 1 wherein the total of said composition of TiO₂, CaF₂ and Al₂ O₃, comprises 60-90% by weight of the whole slag-forming agent.

3. The submerged arc welding method as defined in claim 1 wherein logK(Ω

^-1 cm^-1) at 500°

C. is at least -0.2 when electric conductivity of the slag formed by the preceding electrode is expressed in terms of K(Ω

^-1 cm^-1).

4. The submerged arc welding method as defined in claim 1 which further comprises forming a preceding layer of flux having a composition which comprises:

TiO₂ ;

20-65% by weight (based on the whole flux amount),

CaF₂ ;

12-45% by weight (based on the whole flux amount), and

Al₂ O₃ ;

10-56% by weight (based on the whole flux amount),

as a slag-forming agent and the total of said composition comprises 65-90% by weight of the whole slag-forming agent.

5. The submerged arc welding method as defined in claim 4 wherein said flux comprises a sintered type flux having a bulk density of 0.6-1.5.

6. The submerged arc welding method as defined in claim 4 wherein said flux comprises a molten type flux having a bulk density of 0.6-1.7.

7. The submerged arc welding method as defined in claim 4 wherein said flux includes iron powder as a component other than the slag-forming agent.

8. The submerged arc welding method as defined in claim 1 which further comprises:

performing one-side, submerged arc welding using at least two electrodes under the welding conditions;

groove width;

1/2 (thickness)≦

groove width≦

(thickness+diameter of subsequent wire) and thickiness ≦

20 mm, and

1/2 (thickness)≦

groove width≦

thickness when thickness≦

20 mm;

welding current;

800-1350A at a preceding electrode, and 600-1200A at a second or subsequent electrodes;

welding voltage;

30-36V at a preceding electrode, and 37-50V at said second or subsequent electrodes;

welding heat input;

up to 70K Joule/cm to an electrode or electrodes other than a final electrode, and

up to 60K Joule/cm to said final electrode; and

distance between the electrodes;

at least 500 mm

and;

using said subsequent electrodes without peeling off and removing a weld slag formed by a preceding electrode or electrodes after the weld slag is solidified.

9. The submerged arc welding method as defined in claim 8 which further comprises oscillating all electrodes other than a first electrode in a direction at right-angles to the weld line with a frequency of at least one reciprocation per centimeter of weld length.

10. The submerged arc welding method as defined in claim 8 which further comprises oscillating only the final electrode in a direction at a right angle to the weld line with a frequency of at least one reciprocation per centimeter weld length.

11. The submerged arc welding method as defined in claim 1 or 4 which further comprises substituting ZrO₂ for up to 60% by weight of said 20-65% by weight of TiO₂.