Thermally stable sulfur dioxide-ethylene-vinyl ester terpolymers and process for preparing same

• US 4,215,035 A
• Filed: 04/11/1979
• Issued: 07/29/1980
• Est. Priority Date: 04/11/1979
• Status: Expired due to Term

• Current Assignee: Equistar Chemicals LP (Lyondellbasell Industries NV)
• Original Assignee: National Distillers and Chemical Corporation
• Inventors: Pyle, Lorrin W., Memering, Leroy J.
• Primary Examiner(s): Hoke, V. P.
• Application Number:
  US06/028,958
• Time in Patent Office: 475 Days
• Field of Search: 260/45.7 SW, 260/45.75 R, 260/42.52, 260/23 AR, 260/45.95 R, 260/45.95 C, 528/364
• US Class Current: 524/331
• CPC Class Codes: C08G 75/22 Copolymers of sulfur dioxide with unsaturated aliphatic compounds
• CPC Class Codes: C08L 81/06 Polysulfones; Polyethersulfones

Abstract

Sulfur dioxide-ethylene-vinyl ester terpolymers exhibiting improved thermal stability are prepared by substantially uniformly incorporating therein a thermal stability-imparting amount of at least one inorganic oxygen-containing metal compound in which the metal is an alkali metal, alkaline earth metal or zinc.

Claims

1. A sulfur dioxide-ethylene-vinyl ester terpolymer having improved thermal stability observed as a reduction in the level of malador of the terpolymer and/or an improvement in the color stability of the terpolymer, said terpolymer containing substantially uniformly distributed therein a thermal stability imparting amount of at least one inorganic oxygen-containing metal compound in which the metal is an alkali metal, alkaline earth metal or zinc.

2. The terpolymer of claim 1 containing from about 0.5 to about 10.0 weight percent inorganic oxygen-containing metal compound.

3. The terpolymer of claim 2 containing from about 1 to about 5 weight percent inorganic oxygen-containing metal compound.

4. The terpolymer of claim 1 in which the inorganic oxygen-containing metal compound is an oxide, carbonate, sulfate, phosphate, borate or silicate.

5. The terpolymer of claim 4 in which the inorganic oxygen-containing metal compound is at least one member of the group consisting of zinc oxide, magnesium oxide, sodium sulfate, calcium hydroxide, sodium carbonate, zinc carbonate, calcium carbonate, magnesium hydroxide, lithium carbonate, barium hydroxide, barium oxide, barium carbonate, potassium borate, magnesium borate, potassium silicate and potassium carbonate.

6. The terpolymer of claim 1 additionally containing an organic antioxidant.

7. The terpolymer of claim 6 containing from about 0.05 to about 1.0 weight percent organic antioxidant.

8. The terpolymer of claim 7 containing from about 0.1 to about 0.5 weight percent organic antioxidant.

9. The terpolymer of claim 6 in which the organic antioxidant is [dialkyl phenol sulfide 4,4'"'"'thio-bis(6-t-butyl-5m-cresol)].

10. The terpolymer of claim 1 containing magnesium oxide in combination with [dialkyl phenol sulfide 4,4'"'"'thio-bis (6-t-butyl-m-cresol)].

11. A process for imparting improved thermal stability to a sulfur dioxide-ethylene-vinyl acetate terpolymer observed as a reduction in the level of malodor of the terpolymer and/or an improvement in the color stability of the terpolymer which comprises incorporating substantially uniformly in said terpolymer a thermal stability-imparting amount of at least one inorganic oxygen-containing metal compound in which the metal is an alkali metal, alkaline earth metal or zinc.

12. The process of claim 11 in which is added from about 0.5 to about 10.0 weight percent inorganic oxygen-containing metal compound.

13. The process of claim 12 in which is added from about 1 to about 5 weight percent inorganic oxygen-containing metal compound.

14. The process of claim 11 in which the inorganic oxygen-containing metal compound is an oxide, carbonate, sulfate, phosphate, borate or silicate.

15. The process of claim 14 in which the inorganic oxygen-containing metal compound is at least one member of the group consisting of zinc oxide, magnesium oxide, sodium sulfate, calcium hydroxide, sodium carbonate, zinc carbonate, calcium carbonate, magnesium hydroxide, lithium carbonate, barium hydroxide, barium oxide, barium carbonate, potassium borate, magnesium borate, potassium silicate and potassium carbonate.

16. The process of claim 11 in which is additionally added an organic antioxidant.

17. The process of claim 16 in which is added from about 0.05 to about 1.0 weight percent organic antioxidant.

18. The process of claim 17 in which is added from about 0.1 to about 0.5 weight percent organic antioxidant.

19. The process of claim 16 in which the organic antioxidant is [dialkyl phenol sulfide 4,4'"'"'thio-bis(6-t-butyl-m-cresol)].

20. The process of claim 11 in which is added magnesium oxide in combination with [dialkyl phenol sulfide 4,4'"'"'thio-bis(6-t-butyl-m-cresol)].