Polyester diol extended uralkyd resin and coating compositions containing the same

• US 4,222,911 A
• Filed: 08/07/1978
• Issued: 09/16/1980
• Est. Priority Date: 08/07/1978
• Status: Expired due to Term

• Current Assignee: PPG Industries Incorporated (Nouryon BV)
• Original Assignee: PPG Industries Incorporated (Nouryon BV)
• Inventors: Erikson, J. Alden, Christenson, Roger M.
• Primary Examiner(s): Griffin, Ronald W.
• Application Number:
  US05/931,632
• Time in Patent Office: 771 Days
• Field of Search: 260/22 TN, 260/22 CQ, 260/21
• US Class Current: 528/295.5
• CPC Class Codes: C08G 18/4202 Two or more polyesters of different physical or chemical nature C08G18/44 takes precedence
• CPC Class Codes: C08G 18/4288 modified by higher fatty oils or their acids or by resin acids

Abstract

Coating compositions containing polyester diol extended uralkyd resins form flexible coatings. Such uralkyd resins are prepared by reacting oil modified alkyd resin, polyester diol having a number average molecular weight in the range of from about 800 to about 4000, and diisocyanate.

Claims

1. A polyester diol extended, ungelled, isocyanate-free uralkyd resin comprising the reaction product of

a. from about 60 to about 94 percent by weight of oil modified alkyd resin having an oil length of from about 30 to about 65 percent;

b. from about 3 to about 20 percent by weight of essentially nitrogen-free polyester diol having a number average molecular weight in the range of from about 800 to about 4000; and

c. from about 3 to about 20 percent by weight of diisocyanate.

2. The polyester diol extended, ungelled, isocyanate-free uralkyd resin of claim 1 wherein said oil modified alkyd resin comprises the reaction product of

a. polyfunctional alcohol;

b. polyfunctional acid or acid anhydride; and

c. the polyol alcoholysis reaction product of drying oil, semi-drying oil, non-drying oil or a mixture thereof.

3. A polyester diol extended, ungelled, isocyanate-free uralkyd resin comprising the reaction product of

a. from about 80 to about 94 percent by weight of air drying oil modified alkyd resin having an oil length of from about 30 to about 65 percent;

b. from about 3 to about 10 percent by weight of essentially nitrogen-free polyester diol having a number average molecular weight in the range of from about 800 to about 4000; and

c. from about 3 to about 10 percent by weight of diisocyanate.

4. The polyester diol extended uralkyd resin of claim 3 wherein said air drying, oil modified alkyd resin comprises the reaction product of

a. polyfunctional alcohol;

b. polyfunctional acid or acid anhydride; and

c. the polyol alcoholysis reaction product of drying oil, semi-drying oil or a mixture thereof.

5. The polyester diol extended uralkyd resin of claim 4 wherein the polyol used in preparing said polyol alcoholysis product has an average functionality of about 3 hydroxyl groups per molecule.

6. The polyester diol extended uralkyd resin of claim 5 wherein said polyol is the reaction product of polyol having an average functionality greater than 3 hydroxyl groups per molecule and fatty acid.

7. The polyester diol extended uralkyd resin of claim 5 wherein said polyol is glycerine.

8. The polyester diol extended uralkyd resin of claim 3 wherein said air drying, oil modified alkyd resin comprises the reaction product of

a. polyfunctional alcohol;

b. polyfunctional acid or acid anhydride; and

c. polyol having an average functionality of about 2 hydroxyl groups per molecule comprising the reaction product of polyol having an average functionality greater than 2 hydroxyl groups per molecule and fatty acid.

9. The polyester diol extended uralkyd resin of claim 3 wherein said polyester diol is the reaction product of a diol and a diacid.

10. The polyester diol extended uralkyd resin of claim 3 wherein said polyester diol is the reaction product of 1,4-butanediol and adipic acid.

11. The polyester diol extended uralkyd resin of claim 3 wherein said polyester diol is polylactone diol.

12. The polyester diol extended uralkyd resin of claim 11 wherein said polylactone diol is poly-ε

-caprolactone diol.

13. The polyester diol extended uralkyd resin of claim 12 wherein said poly-ε

-caprolactone diol is the reaction product of ε

-caprolactone and diethylene glycol.

14. The polyester diol extended uralkyd resin of claim 3 wherein said diisocyanate is 1-isocyanatomethyl-5-isocyanato-1,3,3-trimethylcyclohexane, 2,4-diisocyanatotoluene, 2,6-diisocyanatotoluene, bis(4-isocyanatocyclohexyl)-methane, bis(4-isocyanatophenyl)methane, 1,6-diisocyanatohexane or mixtures thereof.

15. The polyester diol extended uralkyd resin of claim 3 wherein said diisocyanate comprises a mixture of 2,4-diisocyanatotoluene and 2,6-diisocyanatotoluene.

16. A method of preparing a polyester diol extended, ungelled, isocyanate-free uralkyd resin comprising reacting

a. from about 60 to about 94 percent by weight of oil modified alkyd resin having an oil length of from about 30 to about 65 percent;

b. from about 3 to about 20 percent by weight of essentially nitrogen-free polyester diol having a number average molecular weight in the range of from about 800 to about 4000; and

c. from about 3 to about 20 percent by weight of diisocyanate.

17. A method of preparing a polyester diol extended, ungelled, isocyanate-free uralkyd resin comprising reacting

a. from about 80 to about 94 percent by weight of air drying, oil modified alkyd resin having an oil length of from about 30 to about 65 percent;

b. from about 3 to about 10 percent by weight of essentially nitrogen-free polyester diol having a number average molecular weight in the range of from about 800 to about 4000; and

c. from about 3 to about 10 percent by weight of diisocyanate.

18. In a coating composition having a binder, the improvement wherein said binder comprises from about 25 to about 100 percent by weight of a polyester diol extended, ungelled, isocyanate-free uralkyd resin comprising the reaction product of

a. from about 60 to about 94 percent by weight of oil modified alkyd resin having an oil length of from about 30 to about 65 percent;

b. from about 3 to about 20 percent by weight of essentially nitrogen-free polyester diol having a number average molecular weight in the range of from about 800 to about 4000; and

c. from about 3 to about 20 percent by weight of diisocyanate.

19. The coating composition of claim 18 wherein

a. said oil modified alkyd resin comprises the reaction product of

(1) polyfunctional alcohol,

(2) polyfunctional acid or acid anhydride, and

(3) the glycerine alcoholysis reaction product of a drying oil, semi-drying oil, non-drying oil or a mixture thereof.

20. The coating composition of claim 18 wherein said binder comprises from about 25 percent to about 95 percent by weight of said polyester diol extended uralkyd resin and from about 5 percent to about 40 percent by weight of crosslinking agent.

21. In a coating composition having a binder, the improvement wherein said binder comprises from about 25 to about 100 percent by weight of a polyester diol extended, ungelled, isocyanate-free uralkyd resin comprising the reaction product of

a. from about 80 to about 94 percent by weight of air drying, oil modified alkyd resin having an oil length of from about 30 to about 64 percent;

b. from about 3 to about 10 percent by weight of essentially nitrogen-free polyester diol having a number average molecular weight in the range of from about 800 to about 4000; and

c. from about 3 to about 10 percent by weight of diisocyanate.

22. The coating composition of claim 21 wherein

a. said air drying, oil modified alkyd resin comprises the reaction product of

(1) polyfunctional alcohol,

(2) polyfunctional acid or acid anhydride, and

(3) the glycerine alcoholysis reaction product of a drying oil, semi-drying oil or a mixture thereof;

b. said polyester diol is poly-ε

-caprolactone diol; and

c. said diisocyanate is toluene diisocyanate.

23. The coating composition of claim 22 wherein said poly-ε

-caprolactone diol is poly-ε

-caprolactone-diethylene glycol diol.