• US 4,224,736 A
• Filed: 08/07/1978
• Issued: 09/30/1980
• Est. Priority Date: 08/07/1978
• Status: Expired due to Term

• Current Assignee: Spectrum Brands, Inc. (Spectrum Brands Holdings, Inc.)
• Original Assignee: ESB, Inc.
• Inventors: Feldhake, Ralph H.
• Primary Examiner(s): Crane, Daniel C.
• Application Number:
  US05/931,641
• Time in Patent Office: 785 Days
• Field of Search: 29/623.2, 29/623.4, 29/623.5, 29/447, 29/446, 29/450, 429/174, 429/173, 429/175, 429/185, 429/167, 264/343, 264/342 R, 264/230, 264/268, 264/272, 264/101
• US Class Current: 29/623.2
• CPC Class Codes: H01M 50/169 by welding, brazing or soldering
• CPC Class Codes: Y02E 60/10 Energy storage using batteries
• CPC Class Codes: Y10T 29/4911 including sealing
• CPC Class Codes: Y10T 29/49114 including adhesively bonding
• CPC Class Codes: Y10T 29/49863 with prestressing of part

Abstract

A process for improving leakage resistant in a galvanic cell is provided. This is done by making an improved grommet and metal cover. The process comprises swelling a grommet which has been placed tightly around the periphery of a metal cover until the grommet is loose upon the metal cover, forcing a sealant solution between the swollen grommet and metal cover and then shrinking the grommet to substantially its original size to trap the sealant compound between the grommet and metal cover.

Claims

1. A process for manufacturing an improved grommet and metal cover for use in a galvanic cell, the process comprising:

(a) swelling the grommet which is comprised of a polyolefin or a nylon and which has been placed tightly around the periphery of the metal cover until the grommet is loose upon the metal cover,

(b) forcing a sealant solution between the swollen grommet and metal cover, the sealant solution comprising solvent and sealant material of rosin, polystyrene, polyolefin ethylene vinyl acetate, polyamine, bitumin or thermoplastic elastomer and,

(c) shrinking the grommet to substantially its original size to trap the sealant material between the grommet and metal cover.

2. The process of claim 1 wherein the grommet is made from a material which is a polyolefin.

3. The process of claim 1 wherein the grommet is a nylon, wherein the nylon is 6, 6 nylon;

6, 12 nylon, 6 nylon or 11 nylon.

4. The process of claim 1 wherein the grommet has been placed around the periphery of the metal cover by injection molding.

5. The process of claim 1 wherein a liquid swells the grommet and the liquid is methylene chloride or perchloroethylene.

6. The process of claim 1 wherein the swelling is by placing the grommet and covers into methylene chloride and subjecting the grommet and covers to a temperature of 39°

-250°

C. for time sufficient to swell the grommet.

7. The process of claim 6 wherein the time is 0.5 to 3 hours and the temperature is 90°

-110°

C.

8. The process of claim 1 wherein the sealant of the sealant solution is bitumen.

9. The process of claim 8 wherein the bitumen has

(a) a softening point, measured by ASTM P36-26 of 180°

to 185°

F.,

(b) a penetration measured by ASTM D5-52 at 77°

F. of 15 to 20,

(c) a specific gravity at 60°

F. of 1.00 +, and

(d) a viscosity, at 350°

F. of 65 seconds, at 375°

F. of 39 seconds, and at 400°

F. of 29 seconds.

10. The process of claim 9 wherein the sealant solution is 35 to 45% by weight bitumen, and the solvent is methylene chloride.