Composite aluminum-containing workpieces

• US 4,241,148 A
• Filed: 11/21/1977
• Issued: 12/23/1980
• Est. Priority Date: 12/15/1969
• Status: Expired due to Term

• Current Assignee: Vereinigte Aluminium-Werke AG
• Original Assignee: Vereinigte Aluminium-Werke AG
• Inventors: Schultze, Werner, Schoer, Heinz
• Primary Examiner(s): Dean, R.
• Application Number:
  US05/853,768
• Time in Patent Office: 1,128 Days
• Field of Search: 428/469, 428/654, 428/457, 75/148, 75/178 A
• US Class Current: 428/654
• CPC Class Codes: B23K 35/282 Zn as the principal constituent
• CPC Class Codes: B23K 35/286 Al as the principal constituent
• CPC Class Codes: B23K 35/288 with Sn or Zn
• CPC Class Codes: Y10T 428/12764 Next to Al-base component

Abstract

Processes and compositions for soldering aluminum-containing workpieces wherein the solder contains components which lower the surface tension and the viscosity of the molten solder, and which lower the interfacial tension between the solder and the aluminum-containing workpieces. Useful components are bismuth, strontium, barium and antimony. The solder may be used with or without flux.

Claims

1. A bonded article comprising a pair of spaced apart workpieces consisting of aluminum and bearing an aluminum oxide surface layer,

an aluminum silicon filler metal interposed between said oxide surface layers to form a joint between said workpieces, said filler metal consisting essentially of aluminum containing from 6 to 20% by weight of silicon and from 0.01 to 10.0% by weight of said filler metal of at least one substance selected from the group consisting of bismuth, antimony, strontium and barium remainder aluminum and impurities, said filler metal having a melting temperature substantially below that of aluminum and said joint being free of any fluoride or chloride flux residue.

5. The bonded article of claim 1 wherein said substance comprises bismuth.

6. The bonded article of claim 5 wherein said bismuth is present in the range between about 0.05 to 2% by weight.

2. A clad brazing material comprising a core consisting essentially of aluminum, a flux-free filler metal clad on the surface of said core and consisting essentially of 6 to 20% by weight of silicon and from 0.01 to about 10% by weight of at least one substance selected from the group consisting of bismuth, antimony, strontium and barium, the balance aluminum and impurities, the viscosity and surface tension of said filler metal in the molten condition being less than the viscosity and surface tension of said molten filler metal in the absence of said substance and the interfacial tension between said filler metal and an aluminum workpiece being lower than the interfacial tension in the absence of said substance, and said filler metal having a melting temperature substantially below that of aluminum.

7. The clad brazing material of claim 2 wherein said substance comprises bismuth.

3. An article comprising a first aluminum alloy, said first alloy consisting essentially of from 6 to 20% by weight of silicon and from 0.01 to 10% by weight of at least one substance selected from the group consisting of bismuth, antimony, strontium, and barium, the remainder aluminum and its alloys, the surface tension of said first alloy in the molten condition being less than the surface tension of said molten alloy in the absence of said substance, and

workpieces comprising aluminum and aluminum alloys having melting points higher than that of said first alloy, said workpieces joined together by said first alloy in a flux-free bond.

4. A clad article comprising a core selected from aluminum and its alloys:

a cladding on said core, said cladding comprising a flux-free filler metal consisting essentially of from about 6 to about 20% by weight of silicon, from about 0.01 to 10% by weight of at least one substance selected from the group consisting of bismuth, strontium, barium and antimony, remainder aluminum and its alloys and said cladding having a melting temperature substantially below that of said core materials.

8. The clad brazing material of claim 48 wherein said bismuth is present in the range from about 0.05 to about 2% by weight.