High yield fiber sheets

• US 4,247,362 A
• Filed: 05/21/1979
• Issued: 01/27/1981
• Est. Priority Date: 05/21/1979
• Status: Expired due to Term

• Current Assignee: BKI Holding Corp. (KOCH Industries Incorporated)
• Original Assignee: Buckeye Cellulose Corp (KOCH Industries Incorporated)
• Inventors: Williams, James C.
• Primary Examiner(s): Chin, Peter
• Application Number:
  US06/041,043
• Time in Patent Office: 617 Days
• Field of Search: 162/13, 162/23-28, 162/83, 162/100, 162/141, 162/142, 162/150, 162/159, 162/201, 162/17, 162/64, 264/121
• US Class Current: 162/13
• CPC Class Codes: A61L 15/28 Polysaccharides or their derivatives A61L15/225 takes precedence
• CPC Class Codes: A61L 15/40 containing ingredients of undetermined constitution or reaction products thereof , e.g. plant or animal extracts
• CPC Class Codes: C08L 1/02 Cellulose; Modified cellulose
• CPC Class Codes: D21H 17/71 Mixtures of material D21H17/69 takes precedence; Pulp or paper comprising several different materials not incorporated by special processes D21H23/10, D21H23/70, D21H23/76 take precedence
• CPC Class Codes: D21H 23/10 at least two kinds of compounds being added
• CPC Class Codes: D21H 5/2628 Formation of a product from several constituents, e.g. blends of various types of fibres, fillers and/or binders or formation from various sources and/or streams or fibres mixing non-fibrous materials with fibres as a preliminary treatment of fibres, e.g. for spinning D01G13/00

Abstract

Wet-laid sheets of softwood high yield fibers in combination with hardwood high yield fibers. The sheets, which are strong enough to be handled by commercial equipment, are formed on conventional papermaking machines using a furnish comprising a major proportion of softwood high yield fibers in admixture with a minor proportion of hardwood high yield fibers. The hardwood high yield fibers are specially prepared by a procedure comprising treating hardwood with relatively high levels of chemicals under relative stringent conditions and defibrating the treated hardwood with relatively high levels of power input. Airfelts made from these sheets exhibit low wet densities. Processes for making the sheets and the airfelts are also provided.

Claims

1. A process for preparing sheets of high yield wood pulp fibers comprising the steps of:

(A) providing substantially non-delignified and relatively undamaged softwood high yield fibers having a Canadian standard freeness value greater than about 700 ml;

(B) providing hardwood high yield fibers wherein said hardwood fibers;

(i) have a Canadian standard freeness value of from about 50 ml to about 400 ml;

(ii) have been prepared separately from said softwood fibers; and

(iii) have been prepared by a process comprising the steps of;

(a) treating hardwood with an aqueous solution comprising from about 2% to about 40% by weight of a treating agent selected from the group consisting of alkali metal sulfite, alkali metal bisulfite, sulphur dioxide with alkali metal hydroxide, and mixtures thereof at a temperaure of from about 130°

C. to about 190°

C. for from about 1 minute to about 60 minutes; and

(b) defibrating said treated hardwood;

(C) mixing said softwood and hardwood fibers to form a papermaking furnish comprising at least about 75% by weight said softwood and hardwood fibers and wherein the weight ratio of said softwood fibers to said hardwood fibers is from about 2.33;

1 to about 19;

1; and

(D) wet forming said sheets from said papermaking furnish.

2. The process of claim 1 wherein the weight ratio of said softwood fibers to said hardwood fibers is from about 5.67:

1 to about 19;

1.

3. The process of claim 1 or 2 wherein the power input during said defibrating step is from about 155 to about 500 kilowatt hours per metric ton of treated hardwood.

4. The process of claim 1 or 2 wherein said aqueous solution comprises from about 2% to about 20% by weight sodium sulfite and from about 2% to about 20% by weight sodium bisulfite.

5. The process of claim 4 wherein the power input during said defibrating step is from about 155 to about 500 kilowatt hours per metric ton of treated hardwood.

6. The wet formed sheet of the process of claims 1 or 2.

7. The wet formed sheet of the process of claim 3.

8. The wet formed sheet of the process of claim 3.

9. The wet formed sheet of the process of claim 5.

10. A process for preparing airfelts comprising the steps of:

(A) comminuting sheets of high yield wood pulp fibers; and

(B) airlaying said comminuted high yield wood pulp fibers wherein;

(i) said sheets of high yield wood pulp fibers comprise at least about 75% by weight substantially non-delignified and relatively undamaged softwood high yield fibers and hardwood high yield fibers and wherein the weight ratio of said softwood fibers to said hardwood fibers is from about 2.33;

1 to about 19;

1;

(ii) said softwood high yield fibers have a Canadian standard freeness value greater than about 700 ml;

(iii) said hardwood high yield fibers;

(a) have a Canadian standard freeness value of from about 50 ml to about 400 ml; and

(b) have been prepared by a process comprising the steps of;

(aa) treating hardwood with an aqueous solution comprising from about 2% to about 40% by weight of a treating agent selected from the group consisting of alkali metal sulfite, alkali metal bisulfite, sulphur dioxide with alkali metal hydroxide, and mixtures thereof at a temperature of from about 130°

C. to about 190°

C. for from about 1 minute to about 60 minutes; and

(bb) defibrating said treated hardwood.

11. The process of claim 10 wherein the weight ratio of softwood fibers to hardwood fibers is from about 5.67:

1 to about 19;

1.

12. The process of claims 10 or 11 wherein the power input during said defibrating step is from about 155 to about 500 kilowatt hours per metric ton of treated hardwood.

13. The process of claims 10 or 11 wherein said aqueous solution comprises from about 2% to about 20% by weight sodium sulfite and from about 2% to about 20% by weight sodium bisulfite.

14. The process of claim 13 wherein the power input during said defibrating step is from about 155 to about 500 kilowatt hours per metric ton of treated hardwood.

15. The airfelt of the process of claims 10 or 11.

16. The airfelt of the process of claim 12.

17. The airfelt of the process of claim 13.

18. The airfelt of the process of claim 14.