Ceramifiable silicone adhesives
First Claim
1. A silicone adhesive composition ceramifiable to a quartz-free ceramic and suitable for adhering a plurality of greenware components together to provide a composite greenware article which can be fired to a unitary ceramic article, said composition consisting essentially of(I) a silicone pressure-sensitive adhesive consisting essentially of(A) 45 to 55 parts by weight of a polydiorganosiloxane fluid having the average formula YO(R2 SiO)n Y wherein each R denotes, independently, a monovalent hydrocarbon radical having from 1 to 6 inclusive carbon atoms, at least 90 percent of all R radicals being methyl radicals, y denotes an endblocking radical and n has an average value so that the polydiorganosiloxane fluid has a viscosity of from 1 to 1000 pascal-seconds at 25°
- C., and(B) 45 to 55 parts by weight of a xylene-soluble resin copolymer consisting essentially of R3 SiO1/2 siloxane units and SiO4/2 siloxane units in a mol ratio of from 0.6 to 0.9 R3 SiO1/2 units for each SiO4/2 unit, wherein each R denotes, independently, a monovalent hydrocarbon radical having from 1 to 6 inclusive carbon atoms, the total of (A) plus (B) being 100 parts by weight, and(II) 100 to 400 parts by weight, for every 100 parts by weight of (A) plus (B), of a volatile-free ceramifiable filler having a softening point above 800°
C. and consisting of a mixture of 55.6 percent by weight SiO2, 22.2 percent by weight Al2 O3 and 22.2 percent by weight MgO.
1 Assignment
0 Petitions
Accused Products
Abstract
Ceramifiable silicone adhesives having tack and green strength are provided by mixing a ceramifiable filler with certain silicone pressure-sensitive adhesives. The silicone pressure-sensitive adhesive comprises approximately equal weights, plus or minus five percent, of a polydiorganosiloxane having a viscosity of from 1 to 1000 Pa·s and a xylene-soluble resin copolymer of R3 SiO1/2 siloxane units and SiO4/2 siloxane units. High loadings (80 weight percent of the ceramifiale adhesive) of ceramifiable filler are attainable without loss of tack and green strength when the polydiorganosiloxane is a mixture of a low-viscosity fluid and a high-viscosity fluid. These ceramifiable silicone adhesives are useful for assembling and adhering a plurality of ceramifiable greenware components to form a ceramifiable composite greenware article.
-
Citations
3 Claims
-
1. A silicone adhesive composition ceramifiable to a quartz-free ceramic and suitable for adhering a plurality of greenware components together to provide a composite greenware article which can be fired to a unitary ceramic article, said composition consisting essentially of
(I) a silicone pressure-sensitive adhesive consisting essentially of (A) 45 to 55 parts by weight of a polydiorganosiloxane fluid having the average formula YO(R2 SiO)n Y wherein each R denotes, independently, a monovalent hydrocarbon radical having from 1 to 6 inclusive carbon atoms, at least 90 percent of all R radicals being methyl radicals, y denotes an endblocking radical and n has an average value so that the polydiorganosiloxane fluid has a viscosity of from 1 to 1000 pascal-seconds at 25° - C., and
(B) 45 to 55 parts by weight of a xylene-soluble resin copolymer consisting essentially of R3 SiO1/2 siloxane units and SiO4/2 siloxane units in a mol ratio of from 0.6 to 0.9 R3 SiO1/2 units for each SiO4/2 unit, wherein each R denotes, independently, a monovalent hydrocarbon radical having from 1 to 6 inclusive carbon atoms, the total of (A) plus (B) being 100 parts by weight, and (II) 100 to 400 parts by weight, for every 100 parts by weight of (A) plus (B), of a volatile-free ceramifiable filler having a softening point above 800°
C. and consisting of a mixture of 55.6 percent by weight SiO2, 22.2 percent by weight Al2 O3 and 22.2 percent by weight MgO. - View Dependent Claims (2, 3)
- C., and
Specification