Grinding wheel containing grain-coated reinforcement fibers and method of making it

• US 4,259,089 A
• Filed: 11/09/1979
• Issued: 03/31/1981
• Est. Priority Date: 08/10/1978
• Status: Expired due to Term

• Current Assignee: Tyrolit - Schleifmittelwerke Swarovski KG (D Swarovski & Company)
• Original Assignee: Tyrolit - Schleifmittelwerke Swarovski KG (D Swarovski & Company)
• Inventors: Helletsberger, Harald, Waizer, Walter
• Primary Examiner(s): Arnold, Donald J.
• Application Number:
  US06/092,755
• Time in Patent Office: 508 Days
• Field of Search: 51/295, 51/298, 51/309, 51/308, 51/297
• US Class Current: 51/295
• CPC Class Codes: B24D 18/00 Manufacture of grinding tools or other grinding devices, e.g. wheels, not otherwise provided for
• CPC Class Codes: B24D 3/344 the bonding agent being organic

Abstract

In a grinding disc reinforcement fibres of high strength are used and such fibres or normal glass fibres are covered with a protective coating including fine grain.

Claims

1. A method of making a high-speed grinding disc having grinding grains and fibers of reinforcing material comprising:

coating the fibers which have a length of more than 10 mm with a resin based binder and fine grain particles having diameters much smaller than that of the fibers and made of material which has substantially the same hardness as the material making up the grinding grain to form fibers with a binder and fine grain coating;

mixing the coated fibers with additional binder and the grinding grain to form a mixture; and

pressing the mixture to form the grinding discs wherein the coated fibers are protected from being damaged by compression against the grinding grain.

2. A method according to claim 1 including first coating the fibers with the first-mentioned binder which has a good adhesion to the fibers and subsequently laying the fibers into the fine grain to attach the fine grain to and cover the fibers.

3. A method according to claim 2, wherein said fine grain includes reactive filler materials.

6. A method according to claim 1 wherein said coated fibers are mixed with the additional binders and grinding grain in a layer of coated fibers.

4. A high speed grinding disc comprising:

a synthetic resin matrix carrying abrasive grains and coated reinforced fibers, said coated reinforcement fibers having an outer coating of synthetic resin having embedded therein fine grain of a material having substantially the same hardness as said abrasive grain with a diameter substantially smaller than that of said fiber, said fine grain covering said fiber and protecting said fiber from damage from abrasive grain pressed against said fiber during the formation of said high-speed grinding disc.

5. A high-speed grinding disc according to claim 4, wherein said fine grain includes reactive filler material.

7. A grinding disc according to claim 4, wherein said fiber reinforcement is chosen from the group consisting of a single crystal whisker, polycrystalline metal whiskers, boron fibers, synthetic whiskers, glass fibers, and drawn metal wires.

8. A grinding disc according to claim 7, wherein said fiber reinforcement comprises drawn metal wires comprising high alloy carbon steel.

9. A grinding disc according to claim 4, wherein said fiber reinforcement is woven into a cloth with a weft having fibers of an E-modulus of more than 1×

10⁴ kg/mm² and whose warp is formed by more elastic and flexible fibers.

10. A grinding disc according to claim 9 comprising two of said cloths connected by said binding agent with the weft of one cloth extending parallel to the warp of the other cloth.