Etching of optical fibers

• US 4,265,699 A
• Filed: 05/04/1979
• Issued: 05/05/1981
• Est. Priority Date: 05/04/1979
• Status: Expired due to Term

• Current Assignee: L-3 Communications Corporation (L3Harris Technologies, Inc.)
• Original Assignee: RCA Corporation
• Inventors: Ladany, Ivan
• Primary Examiner(s): Powell, William A.
• Application Number:
  US06/036,058
• Time in Patent Office: 732 Days
• Field of Search: 156/639, 156/645, 156/655, 156/657, 156/663, 156/667, 65/31, 65/4 B, 350/96.18, 350/96.20, 350/96.29, 350/96.32, 350/96.33, 252/79.3
• US Class Current: 216/97
• CPC Class Codes: C03C 25/68 by etching
• CPC Class Codes: G02B 6/4203 Optical features

Abstract

A method for reducing the diameter of the end of an optical fiber while leaving the fiber end flat or slightly concave so that a lens can be formed thereon. The fiber end is etched in a solution of aqueous hydrofluoric acid to which is added ammonium fluoride, ammonium bifluoride or a combination thereof.

Claims

1. A method of etching a single mode optical fiber comprising a fused silica core with a borosilicate glass cladding and having a flat end face whereby a portion of the cladding is removed while leaving the end face flat or slightly concave which consists essentially of etching an end portion of the fiber in a concentrated aqueous hydrofluoric acid solution containing an amount of ammonium fluoride, ammonium bifluoride or mixtures thereof effective for reducing the diameter of the fiber while leaving the end face flat or slightly concave.

3. A method according to claim 1 or 2 wherein said etching solution consists of about 0.40 to about 0.46 gram of ammonium bifluoride per cubic centimeter of concentrated aqueous hydrofluoric acid solution.

4. A method according to claim 1 or 2 wherein said etching solution consists of about 0.17 to about 0.25 gram of ammonium fluoride per cubic centimeter of a concentrated aqueous hydrofluoric acid solution.

5. A method according to claim 1 or 2 wherein said concentrated aqueous hydrofluoric acid solution consists of about 48 to 51% by weight hydrofluoric acid.

2. In a method for forming a lens on the end of a single mode optical fiber comprising a fused silica core and a borosilicate glass cladding having a flat end face which comprises removing a portion of the cladding by chemical etching of an end portion of said fiber, cutting said end portion to form a flat end face thereon and forming a lens on the flat end face of said fiber, the improvement which consists essentially of etching said end portion in a concentrated aqueous hydrofluoric acid solution containing an effective amount of ammonium fluoride, ammonium bifluoride or mixtures thereof whereby a portion of said cladding is removed while leaving said end face flat or slightly concave thereby eliminating the step of cutting said end portion to form a flat end face thereon.