Method of coating hot glass contacting surfaces

• US 4,271,212 A
• Filed: 05/21/1979
• Issued: 06/02/1981
• Est. Priority Date: 05/21/1979
• Status: Expired due to Term

• Current Assignee: Dura TEMP Corporation
• Original Assignee: Owens-Illinois Incorporated (O-I Glass, Inc.)
• Inventors: Stengle, Edward J.
• Primary Examiner(s): LAWRENCE, EVAN
• Application Number:
  US06/041,213
• Time in Patent Office: 743 Days
• Field of Search: 65/26, 65/169, 65/304, 427/202, 427/203, 428/323, 428/44
• US Class Current: 427/203
• CPC Class Codes: C03B 40/02 by lubrication; Use of materials as release or lubricating compositions
• CPC Class Codes: C03B 7/16 using deflector chutes

Abstract

An improved method is provided for forming surfaces for handling hot glass charges and newly-formed glass articles without detrimental marring or marking of the same. The method comprises priming a relatively-smooth metallic substrate with a silicone resin, applying a coating of a solventless curable thermosetting silicone resin binder over the primer, depositing at least one layer of a heat-resistant granular solid lubricant carbonaceous material over the binder coating and allowing the binder to wet and embed the granular material, and heat-curing the binder to permanently affix the granular carbonaceous material to the substrate to provide a lubricated durable wear-resistant surface for handling hot glass charges or gobs as well as newly-formed glass articles.

Claims

1. The method of coating a metallic substrate for long-term use in handling hot glass charges or articles comprising the steps of thoroughly cleaning the metallic substrate, applying a primer coating of monomeric/polymeric first silicone resin to said substrate and air drying the same, applying a coating of solventless curable thermosetting second silicone resin binder over said primer coating, depositing at least one layer of granular heat-resistant solid lubricant carbonaceous material over said binder coating and allowing said binder to wet and embed said granular carbonaceous material to firmly retain the same, and heat-curing said binder into thermoset further-hardened condition to permanently affix said granular carbonaceous material to said substrate.

2. The method in accordance with claim 1, wherein said granular heat-resistant carbonaceous material comprises a particulate mixture of activated charcoal and graphite having a particle size ranging from about 10 to 100 US mesh.

3. The method in accordance with claim 1, wherein said binder coating of solventless silicone resin comprises a clear liquid methoxy functional intermediate silicone resin having an average molecular weight of about 600.

4. The method in accordance with claim 1, wherein said primer coating and said binder coating are successively applied as continuous co-extensive layers over said substrate by brushing.

5. The method in accordance with claim 1, wherein the step of heat-curing of said binder coating is preformed at a temperature of about 500°

to 550°

F., for a period of about 11/2 hours.

6. The method in accordance with claim 1, including the steps of applying a second coating of said binder on top of the heat-cured first coating, depositing and embedding a second layer of granular heat-resistant solid lubricant carbonaceous material in said second binder coating, and heat-curing said binder to permanently affix said granular material thereto.

7. The method of coating a metallic substrate to provide a heat and abrasion-resistant surface for long-term use in repeated handling of hot glass charges or newly-formed glass articles comprising the steps of cleaning and grit blasting selected surfaces of the metallic substrate, applying an essentially-uniform coating of a monomeric/polymeric silicone resin primer over said selected surfaces of said metallic substrate, applying a binder coating consisting of a solventless curable silicone resin over said primer coating on said substrate, depositing an essentially-uniform heavy layer of heat-resistant solid lubricant carbonaceous material over said binder coating and allowing said binder coating to wet and embed said granular material, removing the excess unadhered granular material from the coating surface, and heating said binder into thermoset further-cured hardened condition to permanently affix said granular carbonaceous material to said substrate.

8. The method in accordance with claim 7, wherein the said steps of applying said binder, depositing said granular material, and heat-curing said binder are repeated to provide a second layer of said granular carbonaceous material and binder on said granular-binder layer previously deposited and affixed to said substrate.

9. The method in accordance with claim 7, wherein said granular heat-resistant material has a particle size ranging from about 10 to 100 US mesh, and is selected from the group consisting of graphite, carbon, activated charcoal, and high-melting metallic oxide.