Buffer overcoat for CO.sub.2 ion-selective electrodes

• US 4,272,328 A
• Filed: 12/05/1979
• Issued: 06/09/1981
• Est. Priority Date: 12/05/1979
• Status: Expired due to Term

• Current Assignee: Clinical Diagnostic Systems Inc.
• Original Assignee: Eastman Kodak Company
• Inventors: Kim, Sang H., Chang, Hao-jan
• Primary Examiner(s): Tung, T.
• Application Number:
  US06/100,588
• Time in Patent Office: 552 Days
• Field of Search: 204/1 T, 204/1 K, 204/195 R, 204/195 M, 427/123, 427/58, 427/402, 427/404, 427/419.1
• US Class Current: 205/782.5
• CPC Class Codes: G01N 27/3335 the membrane containing at least one organic component G01N27/3271 takes precedence; aspects concerning the enzyme reagent in enzyme electrodes C12Q1/001

Abstract

An ion-selective electrode for analyzing CO₂ concentration in a liquid sample comprises a support having thereon a metal zone, a metal halide zone, an electrolyte zone, a zone comprising a membrane comprising an ionophore and a zone comprising a hydrophilic binder and a buffer in an amount sufficient to provide a solution having a pH in the range of about 7.5 to 9.5 when wetted with about 5 μl of liquid.

Claims

1. In an ion-selective electrode for analyzing CO₂ concentration in a liquid comprising a support having thereon a layer or layers having sequentially metal/metal halide reference electrode zones, an electrolyte zone and a membrane zone containing an ionophore, the improvement wherein said membrane zone is positioned between said electrolyte zone and an adjacent zone comprising a hydrophilic binder and a buffer in an amount sufficient to provide a solution having a pH in the range of 7.5 to 9.5 when wetted with about 5 μ

l of liquid to be analyzed.

2. The ion-selective electrode of claim 1 wherein all of the zones are in one layer on the support.

3. The ion-selective electrode of claim 1 wherein each zone is a separate layer.

4. The ion-selective electrode of claim 3 wherein the metal/metal halide reference electrode layers are silver and silver halide layers, respectively.

5. The ion-selective electrode of claim 3 wherein the ionophore is 4'"'"'-alkyl-α

α

α

-trifluoroacetophenone.

6. The ion-selective electrode of claim 1 wherein the buffer is present in an amount sufficient to provide a solution having a pH in the range of 7.5 to 9.5 when wetted with about 5 μ

l of serum.

7. The ion-selective electrode of claim 3 wherein the buffer comprises a member selected from the group consisting of tris(hydroxymethyl)aminomethane, diethanolamine, 2-amino-2-methyl-1,3-propanediol and 2-amino-2-ethyl-1,3-propanediol.

8. The ion-selective electrode of claim 3 wherein the layer containing said buffer solution also comprises a surfactant.

9. The ion-selective electrode of claim 3 wherein said hydrophilic binder is selected from the group consisting of gelatin, poly(vinyl alcohol) and poly(2-hydroxyethyl acrylate-co-sodium acrylate-co-N-isopropylacrylamide) (36:

23;

41 by weight).

18. The process of assaying for CO₂ concentration in a liquid sample comprising contacting the sample with the buffer zone of the ion-selective electrode of claim 1.

10. In a process of preparing an ion-selective electrode for analyzing CO₂ concentration in a liquid comprising coating a support with, in succession, layers of metal, metal halide, electrolyte layer and a membrane layer comprising an ionophore, the improvement wherein the membrane layer is overcoated with a layer comprising a hydrophilic binder and a buffer in an amount sufficient to provide a solution having a pH in the range of from about 7.5 to 9.5 when wetted with 5 μ

l of liquid to be analyzed.

11. The process of claim 10 wherein the metal layer comprises silver.

12. The process of claim 10 wherein the metal halide layer is silver chloride.

13. The process of claim 10 wherein the ionophore is 4'"'"'-alkyl-α

α

α

-trifluoroacetophenone.

14. The process of claim 10 wherein the buffer comprises a member selected from the group consisting of tris(hydroxymethyl)aminomethane, diethanolamine, 2-amino-2-methyl-1,3-propanediol and 2-amino-2-ethyl-1,3-propanediol.

15. The process of claim 14 wherein the layer containing said buffer solution also comprises a surfactant.

16. The process of claim 10 wherein said hydrophilic binder is selected from the group consisting of gelatin, poly(vinyl alcohol) and poly(2-hydroxyethyl acrylate-co-sodium acrylate-co-N-isopropylacrylamide) (36:

23;

41 by weight).

17. The process of claim 10 wherein said buffer is present in an amount sufficient to provide a solution having a pH in the range of from about 7.5 to 9.5 when wetted with 5 μ

l of serum.