Flatted water-reducible coating compositions and method for producing same

• US 4,285,846 A
• Filed: 04/28/1980
• Issued: 08/25/1981
• Est. Priority Date: 04/28/1980
• Status: Expired due to Term

• Current Assignee: Cabot Corporation
• Original Assignee: Cabot Corporation
• Inventors: Kintz, Donald P., Hardy, John F., Taylor, Vaughn W.
• Primary Examiner(s): Pertilla, Theodore E.
• Application Number:
  US06/144,345
• Time in Patent Office: 484 Days
• Field of Search: 260/29.2 E, 260/29.2 EP, 260/29.2 TN, 260/29.2 N, 260/42.55, 260/29.6 PM, 260/29.6 RB, 106/288 B
• US Class Current: 524/492
• CPC Class Codes: C08K 3/22 of metals
• CPC Class Codes: C08K 3/36 Silica
• CPC Class Codes: C08L 2666/54 Inorganic substances
• CPC Class Codes: C08L 67/08 Polyesters modified with higher fatty oils or their acids, or with resins or resin acids
• CPC Class Codes: C09D 167/08 Polyesters modified with higher fatty oils or their acids, or with natural resins or resin acids
• CPC Class Codes: C09D 7/42 Gloss-reducing agents

Abstract

Disclosed herein are flatted water-reducible coating compositions of the varnish, paint or enamel types, which compositions comprise a water-miscible film forming resin, water as the predominant solvent and a particulate finely-divided silica flatting agent. The method of the invention involves the initial production of a mill paste formulation containing the film forming resin followed by a let-down step employing water as the predominant solvent. The silica flatting agent is introduced into the composition as an aqueous dispersion thereof during or after said let-down step.

Claims

1. In a method for preparing a water-reducible coating composition comprising the steps of preparing a mill paste of the coating solids, including a water-miscible film forming resin, and thereafter letting down said mill paste with a predominantly aqueous solvent comprising at least 75 percent by weight of water, the improvement which comprises:

flatting the composition by admixing therewith an aqueous dispersion of a finely-divided particulate silica flatting agent during or subsequent to said let-down of said mill paste, the quantity of said silica flatting agent so admixed being between about 0.25 and about 5 percent by weight of the total composition.

2. The method of claim 1 wherein said silica flatting agent is a pyrogenic silica.

3. The method of claim 2 wherein said pyrogenic silica is produced by vapor phase flame hydrolysis of silicon halide feedstock.

4. The method of claim 3 wherein the quantity of pyrogenic silica flatting agent employed is sufficient to provide a concentration thereof of from 0.3 to 2 percent by weight of the total composition.

5. The method of claim 1 wherein said aqueous dispersion of finely-divided particulate silica flatting agent is prepared by intensive mixing of said silica flatting agent with a volume of water.

6. The method of claim 1 wherein, in addition, there is incorporated into the water-reducible coating composition a minor amount of a nonionic surfactant.

7. The method of claim 1 wherein the amount of said nonionic surfactant is between about 10 and about 30% of the dry weight of the silica flatting agent.

8. A flatted water-reducible coating composition comprising a water-miscible film forming resin, water as the predominant solvent therefor and finely-divided particulate silica flatting agent, said composition having been prepared by forming a mill paste of the composition solids, including said water-miscible film forming resin, thereafter letting down said mill paste with an aqueous solvent comprising at least 75% by weight water and during said let-down, or later, admixing said composition with an aqueous dispersion of said silica flatting agent, the quantity of said silica flatting agent so admixed being sufficient to provide a concentration thereof of between about 0.25 and about 5% by weight of the total composition.

9. The flatted composition of claim 8 in the nature of a pigmented paint or enamel.

10. The flatted composition of claim 8 in the nature of an unpigmented varnish.

11. The flatted composition of claim 8 wherein said silica flatting agent is a pyrogenic silica.

12. The flatted composition of claim 11 wherein said pyrogenic silica is produced by vapor phase flame hydrolysis of silicon halide feedstock.

13. The flatted composition of claim 11 wherein said pyrogenic silica flatting agent is present in the amount of between 0.3 to 2 percent by weight of the total composition.

14. The flatted composition of claim 8 comprising, in addition, a minor amount of a nonionic surfactant.

15. The flatted composition of claim 8 wherein the amount of said nonionic surfactant is between about 10 and about 30% of the dry weight of said silica flatting agent.