Manufacture of polymers of acrylic acid or methacrylic acid

• US 4,301,266 A
• Filed: 12/01/1978
• Issued: 11/17/1981
• Est. Priority Date: 12/22/1977
• Status: Expired due to Term

• Current Assignee: BASF AG (BASF SE)
• Original Assignee: BASF AG (BASF SE)
• Inventors: Rohmann, Michael, Muenster, Alfred
• Primary Examiner(s): Garner, Vivian
• Application Number:
  US05/965,264
• Time in Patent Office: 1,082 Days
• Field of Search: 562/595, 562/565, 562/590, 560/190, 260/465.4, 526/212, 526/912, 526/303, 526/317, 526/318
• US Class Current: 526/212
• CPC Class Codes: C08F 20/06 Acrylic acid; Methacrylic acid; Metal salts or ammonium salts thereof
• CPC Class Codes: Y10S 526/912 Reaction medium purification

Abstract

An improved process for the production of polymers of acrylic acid or methacrylic acid by polymerizing acrylic acid or methacrylic acid in isopropanol or in a water-isopropanol mixture containing at least 40% by weight of isopropanol in the presence of polymerization initiators at a temperature of from 120° to 200° C. under pressure. The polymers obtained are used as dispersing agents for inorganic pigments.

Claims

1. In the process for the production of low molecular weight water soluble polymers of acrylic or methacrylic acid by polymerizing acrylic acid or methacrylic acid with up to 10% by weight of a comonomer selected from the group consisting of esters of acrylic acid or of methacrylic acid, fumaric acid, maleic acid, monoesters or diesters of fumaric acid, monoesters or diesters of maleic acid, acrylonitrile, methacrylonitrile, acrylamide and methacrylamide, in a solvent selected from the group consisting of isopropanol and mixtures of isopropanol and water containing at least 40% by weight of isopropanol, in the presence of polymerization initiators, the improvement comprising carrying out the polymerization at a temperature of from 120°

to 200°

C. under a pressure of at least about 2 bars.

2. The process of claim 1, wherein the solvent is recovered and reused in a subsequent said polymerization.

3. The process of claim 1, wherein homopolymers of acrylic acid are produced.

4. The process of claim 1, wherein homopolymers of methacrylic acid are produced.

5. The process of claim 1 wherein the pressure is about 2 to 20 bar.