First Claim
Patent Images
1. A process for injection molding a thermoplastic composition comprising:
- (a) intimately blending (i) from 80 to 97% by weight of a polyethylene terephthalate having an intrinsic viscosity of at least 0.3 dl/g measured as a 0.5% by solution in in a 1;
1 mixture of phenol and tetrachloroethane at 25°
C.; and
(ii) from 3 to 20% by weight of an organic compound containing at least one imide group and having a melting point greater than 240°
C., and(b) injecting molding said blend into a mold held at a temperature of no more than 110°
C. and of no less than 80°
C.
0 Assignments
0 Petitions
Accused Products
Abstract
This disclosure is concerned with a process for injection molding polyethylene terephthalate into colder molds, i.e., less than 120° C., and still obtaining crystalline parts by incorporating an organic imide containing compound having a melting point in excess of 240° C. into the composition. The presence of this additive enhances the crystallization velocity of the composition and permits the achievement of crystalline parts with optimum properties with colder molds and shorter molding cycles than are conventional for polyethylene terephthalate molding compositions.
-
Citations
1 Claim
-
1. A process for injection molding a thermoplastic composition comprising:
-
(a) intimately blending (i) from 80 to 97% by weight of a polyethylene terephthalate having an intrinsic viscosity of at least 0.3 dl/g measured as a 0.5% by solution in in a 1;
1 mixture of phenol and tetrachloroethane at 25°
C.; and
(ii) from 3 to 20% by weight of an organic compound containing at least one imide group and having a melting point greater than 240°
C., and(b) injecting molding said blend into a mold held at a temperature of no more than 110°
C. and of no less than 80°
C.
-
Specification