Slow-curing water-curable urethane prepolymer composition

• US 4,322,327 A
• Filed: 10/14/1980
• Issued: 03/30/1982
• Est. Priority Date: 10/19/1979
• Status: Expired due to Term

• Current Assignee: Mitsubishi Petrochemical Co., Ltd. (Mitsubishi Chemical Group Corp.)
• Original Assignee: Mitsubishi Petrochemical Co., Ltd. (Mitsubishi Chemical Group Corp.)
• Inventors: Hosokawa, Noritaka, Hijikata, Kenji, Yoshimura, Naoki
• Primary Examiner(s): Welsh, Maurice J.
• Application Number:
  US06/196,831
• Time in Patent Office: 532 Days
• Field of Search: 260/28 R, 260/29.2 TN, 260/29.6 NR, 260/29.7 NR, 525/329, 525/437, 525/440, 525/452, 528/45, 528/49, 528/59, 528/73
• US Class Current: 524/507
• CPC Class Codes: C08G 18/0819 containing anionic or anionogenic groups
• CPC Class Codes: C08G 18/10 Prepolymer processes involving reaction of isocyanates or isothiocyanates with compounds having active hydrogen in a first reaction step
• CPC Class Codes: C08G 18/2805 Compounds having only one group containing active hydrogen vinylpolymers having terminal groups containing active hydrogen C08G18/62
• CPC Class Codes: C08G 18/302 Water
• CPC Class Codes: C08G 18/4833 Polyethers containing oxyethylene units
• CPC Class Codes: C08G 2210/00 Compositions for preparing hydrogels
• CPC Class Codes: Y10S 524/916 Hydrogel compositions
• CPC Class Codes: Y10S 528/904 Isocyanate polymer having stated hydrophilic or hydrophobic property

Abstract

A novel slow-curing water-curable urethane prepolymer composition obtained by reacting (A) a hydrophilic urethane prepolymer which is a reaction product of a polyisocyanate and a hydrophilic polyol prepolymer and has at least two --NCO groups and (B) a blocking agent selected from a class consisting of heterocyclic compounds having an ##STR1## structure in the molecule thereof, hydroxypyridines and hydroxyquinolines in the proportion that the equivalent ratio of the ═NH groups of the --OH groups in the blocking agent (B) to the --NCO groups in the hydrophilic urethane prepolymer (A), that is, --OH or ═NH/--NCO ratio, is 0.05 to 2 is disclosed. This composition is remarkably useful as a grouting material, for forming hydrogel which is effective as a fixative or carrier of various materials, as a vehicle for coating materials, and as a stabilizer and thickener for aqueous resin emulsions.

Claims

1. A slow-curing water-curable urethane prepolymer composition obtained by reacting (A) a hydrophilic urethane prepolymer which is the reaction product of a polyisocyanate and a hydrophilic polyol prepolymer and has at least two free --NCO groups and (B) a blocking agent selected from a class consisting of heterocyclic compounds having an ##STR8## structure in the molecule thereof, hydroxypyridines and hydroxyquinolines in such a proportion that the equivalent ratio of the ═

NH groups or the --OH groups in the blocking agent (B) to the --NCO groups in the hydrophilic urethane prepolymer (A) (═

NH or --OH/--NCO) is 0.05 to 2.

2. The composition as claimed in claim 1, wherein the hydrophilic polyol prepolymer is one selected from the class consisting of:

(a) addition polymerization products of ethylene oxide the molecular weight of which is 1,000 to 20,000;

(b) polyether-polyols which are copolymers of ethylene oxide and an alkylene oxide having 3-6 carbon atoms in an amount of not more than 50 mole percent of said copolymer and has molecular weight of 1,000 to 20,000;

(c) addition products of an aliphatic amine, an aliphatic amide, a dicarboxylic acid or a multifunctional alcohol and ethylene oxide;

(d) polyester-polyols;

(e) copolymers of one of styrene, acrylic esters, methacrylic esters, with one of hydroxyethyl acrylate and hydroxyethyl methacrylate; and

(f) polyols having at least one of --OSO₃ M group, --SO₃ M group, ##STR9## wherein M is a monovalent alkali metal, quaternary ammonium radicals and at least two --OH groups in their molecule.

3. The composition as claimed in claim 2, wherein the hydrophilic polyol prepolymer of the component (A) is selected from the class consisting of:

(a) addition polymerization products of ethylene oxide, the molecular weight of which is 1,000 to 20,000;

(b) polyether-polyols which are copolymers of ethylene oxide and an alkylene oxide having 3-6 carbon atoms in an amount of not more than 50 mole percent of said copolymer, and has molecular weight 1,000 to 20,000;

(c) ethylene oxide addition products of a member selected from a class consisting of coco amine, soy bean amine, tallow amine, stearyl amine, ethylene diamine, tetramethylene diamine, hexamethylene diamine, piperadine, hydrogenated tallow amide, oleylamide, phthalic acid, maleic acid, succinic acid, malonic acid, adipic acid, trimethylol propane and glycerine;

(d) polyester-polyols selected from a class consisting of ethylene oxide addition products of copolyesters of one of tetramethylene glycol and polyethylene glycol and one of phthalic acid, maleic acid, succinic acid, malonic acid and adipic acid; and

polyester-polyols which are coesters of polyethylene glycol having molecular weight not less than 200 and one of phthalic acid, maleic acid, succinic acid, malonic acid with adipic acid and have at least two --OH groups at the ends of the molecule;

(e) copolymers of one of styrene, acrylic esters, methacrylic esters and one of hydroxyethyl acrylate and hydroxyethyl methacrylate;

(f) polyols which have at least one of --OSO₃ M group, --SO₃ M group, ##STR10## wherein M is a monovalent alkali metal, and quaternary ammonium radicals and at least two --OH groups.

4. The composition as claimed in any of claims 1-3, wherein the polyisocyanate of the component (A) is selected from the class consisting of ethylene diisocyanate, 1,4-tetramethylene diisocyanate, 1,6-hexamethylene diisocyanate, 1,3-dodecane diisocyanate, cyclobutane-1,3-diisocyanate;

cyclohexane-1,3- or 1,4-diisocyanate, or mixtures of these isomers;

1-isocyanato-2-isocyanato-methylcyclopentane, 1-isocyanato-3,3,5-trimethyl-5-isocyanato-methylcyclohexane;

perhydro-2,4'"'"'- or -4,4'"'"'-diphenylmethane isocyanate of mixtures thereof;

1,3- or 1,4-phenylene diisocyanate or mixtures thereof;

1,2-xylylene diisocyanate, 1,3-xylylene diisocyanate, 1,4-xylylene diisocyanate or mixtures thereof;

2,4- or 2,6-tolylene diisocyanate or mixtures thereof;

diphenylmethane-2,4- or 4,4'"'"'-diisocyanate or mixtures thereof, naphthalene-1,5-diisocyanate, triphenylmethane-4,4'"'"',4"-triisocyanate;

polyphenylpolymethylene polyisocyanate obtained by condensing aniline with formaldehyde followed by phosgenizing, and various mixtures of the above-mentioned compounds.

5. The composition as claimed in claim 4, wherein the polyisocyanate of the component (A) is selected from a class consisting of 2,6-tolylene diisocyanate, 2,4-tolylene diisocyanate, diphenylmethane-4,4'"'"'-diisocyanate, 1,2-xylylene diisocyanate, 1,3-xylylene diisocyanate, 1,4-xylylene diisocyanate, naphthalene diisocyanate, polyphenylene diisocyanate, 1,6-hexamethylene diisocyanate and mixtures thereof.

6. The composition as claimed in any of claims 1-5, wherein the component (B) is a heterocyclic compound which has an ##STR11## structure.

7. The composition as claimed in claim 6, wherein the equivalent ratio of the ═

NH group in the component (B) to the --NCO group in the component (A) is 0.2-2.

8. The composition as claimed in claim 6, wherein a conventional blocking agent selected from phenols, ε

-caprolactam and benzophenone-oxim in an amount not more than 3 times the molar amount of the component (B) is used in combination with the component (B).

9. The composition as claimed in any of claims 6-8, wherein the component (B) is selected from the compounds represented by the general formulas:

##STR12## wherein R¹ is selected from H, C_n H_2n+1, C₆ H₅ and CH₂ C₆ H₅ ;

R² is selected from Cl, OCH₃, and SCH₃ ;

R³ is selected from CH₃, C₂ H₅ and CH(CH₃)₂ ;

n is an integer of 1-6.

10. The composition as claimed in claim 9, wherein the component (B) is selected from a class consisting of imidazole, benzimidazole, 2-methylimidazole, 2-ethylimidazole, 2-phenylimidazoline, 2-chloro-4,6-bis-ethylamino-S-triazine, 2-methoxy-4,6-bis-ethylamino-S-triazine.

11. The composition claimed in any of claims 1-5, wherein the component (B) is selected from a class consisting of 2-hydroxypyridine, 3-hydroxypyridine, 4-hydroxypyridine, 2-hydroxyquinoline, 4-hydroxyquinoline and 8-hydroxyquinoline.

12. An improved aqueous resin emulsion composition, which contains a slow-curing water-curable urethane prepolymer composition obtained by reacting (A) a hydrophilic urethane prepolymer composition which is a reaction product of a polyisocyanate and a hydrophilic polyol prepolymer and has at least 2 free --NCO groups and (B) a blocking agent selected from a class consisting of heterocyclic compounds having an ##STR13## structure in the molecule thereof, hydroxypyridines, and hydroxyquinolines, in such a proportion that the equivalent ratio of the ═

NH groups or --OH groups of the component (B) to the --NCO groups of the component (A) is 0.05-2, in an amount of 0.05-10 parts by weight per 100 parts of the solid ingredient content of said emulsion.

13. The composition as claimed in claim 12, wherein said aqueous resin emulsion is selected from a class consisting of aqueous resin emulsions of ethylene-vinyl acetate copolymer, atactic polypropylene, bitumen materials, poly(vinyl acetate), poly(acrylic ester), acrylic ester-vinyl acetate copolymers, acrylic ester-styrene copolymers, vinyl chloride-vinylidene chloride copolymers, chloroprene rubber and styrene butadiene rubber.

14. The composition claimed in claim 12 or 13, which is thickened by containing said slow-curing water-curable urethane prepolymer composition in an amount of 0.05-2 parts by weight per 100 parts of the solid ingredients of said aqueous resin emulsion.

15. The composition claimed in claim 12 or 13, which is stabilized against re-emulsification by containing said slow-curing water-curable urethane prepolymer composition in an amount of 2-10 parts by weight per 100 parts of the solid ingredient of said aqueous resin emulsion.