Method for making perforations or depressions in a glass work piece

• US 4,326,872 A
• Filed: 06/30/1980
• Issued: 04/27/1982
• Est. Priority Date: 06/30/1980
• Status: Expired due to Term

• Current Assignee: Technology Glass Corporation
• Original Assignee: Technology Glass Corporation
• Inventors: Schreier, Ulrich, Miltenberger, Charles W., Lucas, Edward J.
• Primary Examiner(s): Kellogg, Arthur D.
• Application Number:
  US06/164,699
• Time in Patent Office: 666 Days
• Field of Search: 65/23, 65/56, 65/87, 65/105, 65/112, 65/22
• US Class Current: 65/112
• CPC Class Codes: C03B 21/04 by punching out
• CPC Class Codes: C03B 23/26 Punching reheated glass

Abstract

A method for making perforations or forming depressions in a glass work piece is described. Pursuant to the method, a two piece housing for the work piece is provided. The housing when assembled has a cavity conforming in size and shape to the work piece. The lower housing piece has a continuous upper surface and the upper housing piece has a smooth lower surface and openings in the housing piece conforming in size and position to the perforations or depressions desired to be made in the work piece. The work piece is enclosed in the housing and then plugs are inserted in the openings in the upper housing piece. The plugs snugly fit the openings and extend above the upper surface of the upper housing piece. A weight is then disposed on the upper surface of the plugs. The weight may be a flat metal sheet and is of sufficient weight to cause the plugs to exert a pressure of at least about one half pound per square inch on the work piece. The resulting assembly is then subjected to a temperature intermediate the softening point and the working point of the work piece and the temperature is maintained until descent of the plugs into the work piece ceases. The assembly is then cooled to ambient temperature, the work piece is removed from the housing and then the plugs are removed from the work piece.

Claims

1. The method of opening holes or forming depressions in a glass workpiece which comprises:

(1) providing a two piece housing for said workpiece, said housing when assembled having a cavity conforming in size and shape to said workpiece, the lower housing piece having a continuous upper surface and the upper housing piece having a smooth surface and openings in said housing piece conforming in size and position to the holes or depressions desired to be made in said workpiece,

(2) placing said workpiece on the upper surface of the housing piece and covering the upper surface of workpiece with the upper housing piece so that the upper surface of said workpiece and the lower surface of the upper housing piece are in contact with each other,

(3) inserting in the openings in said upper housing piece plugs snugly fitting said openings and extending above the upper surface of said housing piece,

(4) disposing on the upper surface of said plugs a weight sufficient to cause said plugs to exert a pressure of at least 0.2 pounds per square inch on said workpiece,

(5) heating the assembly resulting from steps 1 to 4 to a temperature intermediate the softening point and the working point of the workpiece and maintaining such temperature until the plug'"'"'s descent into the workpiece ceases and the glass displaced by the descent of the plugs flows into the body of the workpiece causing a slight thickening of the workpiece,

(6) cooling said assembly to ambient temperature, and

(7) removing the workpiece from the housing and removing the plugs from the workpiece.

2. The method defined in claim 1 wherein the housing and the plugs are formed from graphite.

3. The method defined in claim 1 wherein the housing is formed from graphite and the plugs are formed from graphite-clay mixtures.

4. The method defined in claims 2 or 3 wherein the assembly is heated in a non-oxidizing atmosphere.

5. The method defined in claim 1 wherein the upper surfaces of the lower housing piece has raised or depressed areas in its surface to produce depressions or raised areas respectively on the lower surface of the workpiece.

6. The method defined in claim 1 wherein the lower surface of the upper housing piece has raised or depressed areas in its surface to produce depressions or raised areas respectively on the upper surface of the workpiece.

7. The method of simultaneously opening a large number of very small diameter holes in a glass plate which comprises:

(1) providing a two piece housing for said glass plate said housing when assembled having a cavity conforming in size and shape to said plate, the lower housing piece having a continuous upper surface and the upper housing piece having a smooth surface and dozens to hundreds of openings in said housing piece conforming in size and position to the holes desired to be made in said plate,

(2) placing said plate on the upper surface of the lower housing piece and covering the upper surface of the plate with the upper housing piece so that the upper surface of the plate and the lower surface of the upper housing piece are in contact with each other,

(3) inserting in the openings in said upper housing piece graphite pins snugly fitting said openings and extending above the upper surface of said housing piece,

(4) disposing on the upper surface of said pins a weight sufficient to cause said pins to exert a pressure of at least 0.2 pound per square inch on said plate,

(5) heating the entire assembly resulting from steps (1) to (4) in a furnace to a temperature intermediate the softening point and the working point of the glass plate and maintaining such temperature until the pins'"'"' descent into the plate ceases and the glass displaced by the descent of the pins flows into the body of the plate causing a slight thickening of the plate,

(6) cooling said assembly to ambient temperature,

(7) removing the plate from the housing and removing the pins from the plate,

(8) annealing the plate and then lapping and polishing it.

8. The method defined in claim 7 in which the diameter of the holes produced in the plate is about 0.04 of an inch.