Inhibition of corrosion of aluminium tubes by toothpastes

• US 4,328,205 A
• Filed: 02/02/1981
• Issued: 05/04/1982
• Est. Priority Date: 07/12/1978
• Status: Expired due to Fees

• Current Assignee: Beecham Group PLC (GSK plc)
• Original Assignee: Beecham Group PLC (GSK plc)
• Inventors: Taylor, Charles J.
• Primary Examiner(s): Rose, Shep K.
• Application Number:
  US06/230,688
• Time in Patent Office: 456 Days
• Field of Search: 424/49-58, 206/524.4, 206/524.5
• US Class Current: 424/52
• CPC Class Codes: A61K 2800/526 Corrosion inhibitors
• CPC Class Codes: A61K 8/19 containing inorganic ingredients
• CPC Class Codes: A61K 8/21 Fluorides; Derivatives thereof
• CPC Class Codes: A61K 8/25 Silicon; Compounds thereof
• CPC Class Codes: A61Q 11/00 Preparations for care of the teeth, of the oral cavity or of dentures; Dentifrices, e.g. toothpastes; Mouth rinses

Abstract

The tendency of gel toothpastes comprising silica thickeners, such as silica aerogel or precipitated silica, and a fluoride source, such as sodium monofluorophosphate or fluoride, to corrode aluminium tubes can be reduced by incorporating at least 0.01% by weight sodium or potassium hydroxide or carbonate, so that the pH of the toothpaste is at least 8.5.

Claims

1. A method of inhibiting corrosion of unlined aluminium tubes by clear or translucent gel toothpastes comprising a fluoride source and a silica thickener, which method comprises the incorporation in the toothpaste of at least 0.01% by weight, based on the weight of toothpaste, of sodium or potassium hydroxide or sodium or potassium carbonate, so that the pH of the toothpaste is at least 8.5.

2. A method as claimed in claim 1 wherein sodium or potassium hydroxide is incorporated at a level of up to 1% by weight of the toothpaste.

3. A method as claimed in claim 2 wherein sodium or potassium hydroxide is incorporated at a level of from 0.05 to 0.4% by weight of the toothpaste.

4. A method as claimed in claim 1 wherein sodium or potassium carbonate is incorporated at a level of up to 1.5% by weight of the toothpaste.

5. A method as claimed in claim 4 wherein sodium or potassium carbonate is incorporated at a level of from 0.1 to 1.0% by weight of the toothpaste.

6. A method as claimed in claim 1 wherein the toothpaste in which the hydroxide or carbonate is incorporated contains sodium or ammonium monofluorophosphate or sodium, ammonium or stannous fluoride as fluoride source.

7. A method as claimed in claim 1 wherein the toothpaste in which the hydroxide or carbonate is incorporated contains a silica aerogel or precipitated silica thickener.

8. A method as claimed in claim 1 wherein the toothpaste in which the hydroxide or carbonate is incorporated contains a calcium carbonate dental polishing agent applied as one or more stripes on the surface of the gel.

9. A method as claimed in claim 1 wherein the toothpaste in which the hydroxide or carbonate is incorporated contains a silica xerogen dental polishing agent dispersed throughout the gel.

10. In a clear or translucent gel toothpaste comprising a fluoride source and a silica thickener packed in a collapsible unlined aluminum tube susceptible to corrosion, the improvement of including in said toothpaste as inhibitor of corrosion of aluminum an amount of sodium or potassium hydroxide or sodium or potassium carbonate sufficient to raise the pH of said toothpaste to at least pH 8.5, said amount being at least 0.01% of the weight of said toothpaste.

11. A toothpaste according to claim 10, wherein the fluoride source is sodium or ammonium monofluorophosphate or sodium, ammonium or stannous fluoride.