Aqueous dispersion for metal coating from colloidal silica, alkoxy silane, and polymer

• US 4,330,446 A
• Filed: 05/17/1979
• Issued: 05/18/1982
• Est. Priority Date: 07/20/1976
• Status: Expired due to Term

• Current Assignee: Kansai Paint Company Limited
• Original Assignee: Kansai Paint Company Limited
• Inventors: Miyosawa, Yoshiaki
• Primary Examiner(s): Bleutge, John C.
• Assistant Examiner(s): KOECKERT JR, ARTHUR
• Application Number:
  US06/039,954
• Time in Patent Office: 1,097 Days
• Field of Search: 260/29.2 M, 260/29.6 NR, 260/29.6 H, 260/29.7 AT, 260/22 CQ, 260/22 S
• US Class Current: 523/409
• CPC Class Codes: B05D 7/14 to metal, e.g. car bodies involving a chemical reaction between the metal and the coating C23
• CPC Class Codes: C09D 5/08 Anti-corrosive paints
• CPC Class Codes: Y10T 428/31529 Next to metal
• CPC Class Codes: Y10T 428/31663 As siloxane, silicone or silane

Abstract

A silica complex composition suitable for the surface treatment of metals is disclosed, which comprises a water dispersible silica, an organic polymer soluble or dispersible in water and a di- or trialkoxy (or alkoxy-alkoxy) silane compound.

Claims

1. A composition for surface treatment of metals which comprises an aqueous dispersion of a silica-organic polymer complex which is the reaction product of ingredients consisting essentially of colloidal silica wherein the silica is of 7 to 100 mμ

particle size, water soluble or water dispersible organic polymer having both hydroxyl and carboxyl groups and an acid value of 20-200 selected from the group consisting of acrylic copolymer resin, alkyd resin, epoxyester resin and polybutadiene resin, the compounding ratio on a solids basis of said colloidal silica and said organic polymer being in the range of 5;

95 to 95;

5 by weight, and 0.5-15% by weight based on the solid weight of said colloidal silica and said organic polymer of silane compound selected from the group consisting of divinyl dimethoxy silane, divinyl di-β

-methoxyethoxy silane, di(γ

-glycidoxy propyl)dimethoxy silane, vinyl triethoxy silane, vinyl tris-β

-methoxyethoxy silane, γ

-glycidoxy propyl trimethoxy silane, γ

-methacryloxypropyl trimethoxy silane, β

-(3,4-epoxycyclohexyl)ethyl trimethoxy silane, N-β

-aminoethyl-γ

-propylmethyl dimethoxy silane, N-β

-aminoethyl-γ

-propyl trimethoxy silane, and γ

-aminopropyl triethoxy silane.

2. A composition as claimed in claim 1, wherein said colloidal silica, said water soluble or water dispersible organic polymer and said silane compound are mixed together in the form of an aqueous solution or aqueous dispersion and reacted with each other at a temperature between 10°

C. and 110°

C.

3. A composition as claimed in claim 1, wherein said silica has a particle size in the range from 10 to 50 mμ

and said organic polymer has an acid value of 45-150.

4. A composition as claimed in claim 1, wherein said silane compound is added in the amount of 1-10%.

5. A composition as claimed in claim 1, wherein said silane compound is γ

-methacryloxypropyl trimethoxy silane.

6. A composition as claimed in claim 2, wherein said silica has a particle size of 10-50 mμ

, said organic polymer has an acid value of 45-150, the compounding ratio on a solids basis of said silica and said polymer is in the range of 5;

95 to 95;

5 by weight, said silane is added in an amount of 1-10% by weight based on the solid weight of both said silica and said organic polymer, wherein said mixture has a solid content of 10-40%, and wherein said reaction is continued until the viscosity approaches a constant value.

7. A composition as claimed in claim 6, wherein said compounding ratio is from 20:

80 to 50;

50.

8. A composition as claimed in claim 6, wherein said compounding ratio is from 50:

50 to 95;

5.