Energy absorbing elastomers and composites

• US 4,346,205 A
• Filed: 05/19/1980
• Issued: 08/24/1982
• Est. Priority Date: 07/23/1976
• Status: Expired due to Term

• Current Assignee: British Technology Group Ltd. (Boston Scientific Corporation)
• Original Assignee: National Research Development Corporation
• Inventors: Hiles, Maurice A. F.
• Primary Examiner(s): Cockeram, H. S.
• Application Number:
  US06/150,951
• Time in Patent Office: 827 Days
• Field of Search: 521/110, 521/51, 521/112, 521/174, 528/48, 528/53, 528/76, 528/77, 528/906
• US Class Current: 528/53
• CPC Class Codes: B60R 19/22 containing mainly cellular material, e.g. solid foam
• CPC Class Codes: C08G 18/4825 Polyethers containing two hydroxy groups C08G18/4833 - C08G18/5096 take precedence
• CPC Class Codes: C08G 2350/00 Acoustic or vibration damping material
• CPC Class Codes: C08L 2666/14 Macromolecular compounds according to C08L59/00 - C08L87/00; Derivatives thereof
• CPC Class Codes: C08L 75/04 Polyurethanes
• CPC Class Codes: Y10S 528/906 Fiber or elastomer prepared from an isocyanate reactant
• CPC Class Codes: Y10T 428/233 Foamed or expanded material encased
• CPC Class Codes: Y10T 428/249991 Synthetic resin or natural rubbers
• CPC Class Codes: Y10T 428/31554 Next to second layer of polyamidoester
• CPC Class Codes: Y10T 428/31573 Next to addition polymer of ethylenically unsaturated monomer

Abstract

A novel elastomer having a very low compression set and a very slow recovery from compression comprises a flexible polyurethane of essentially linear structure containing unsatisfied hydroxyl groups, and is the reaction product of substantially linear polyols having hydroxyl end groups and an average molecular weight in the range 600 to 1200, with an aromatic isocyanate in less than stoichiometric amount. This elastomer can be used as one layer of an energy-absorbing material, in combination with a more difficultly compressible layer comprising a tough flexible polymeric matrix having a plurality of rigid hollow bodies embedded therein.

Claims

1. An elastomer comprising a flexible polyurethane of essentially linear structure containing unsatisfied hydroxyl groups, and having a compression set less than 15%, an elongation at break of at least 500%, and a recovery which is delayed after compression by at least 0.7 sec, said elastomer comprising the reaction product of substantially linear polyols based on polyalkylene glycol and having an average molecular weight in the range of 600 to 1200, and an aromatic diisocyanate.

2. An elastomer as claimed in claim 1 having a compression set at room temperature less than 5%.

3. An elastomer as claimed in claim 1 having a Shore (0 0) hardness in the range 0 to 50.

4. An elastomer as claimed in claim 3 having a hardness in the range 0 to 20.

5. An elastomer as claimed in claim 1, having a recovery delay of at least 2 secs.

6. An elastomer as claimed in claim 1, wherein the diisocyanate is 4,4'"'"'-diphenylmethane diisocyanate.

7. An elastomer as claimed in claim 1 containing 0.002 to 0.004 gram of unsatisfied OH groups per gram.

8. An elastomer as claimed in claim 7 containing 0.0023 to 0.0034 gram of unsatisfied OH groups per gram.

9. An elastomer as claimed in claim 1 containing an anti-tack agent.

10. An elastomer as claimed in claim 9 wherein said agent is a silicone polycarbinol.

11. An elastomer as claimed in claim 10 wherein said agent is a polypropylene oxide-siloxane copolymer.

12. An elastomer as claimed in claim 10 in which the proportion of said agent is not more than 2% by weight.

14. An elastomer as claimed in claim 1 wherein said substantially linear polyols based on polyalkylene glycol have an average molecular weight in the range of 700 to 900.

15. An elastomer as claimed in claim 1 wherein said substantially linear polyols based on polyalkylene glycol are a blend of a major amount of polyol having an average molecular weight above 1500 and a minor amount of polyol having an average molecular weight below 500.

16. An elastomer as claimed in claim 1 wherein said substantially linear polyols based on polyalkylene glycol are a blend of about 75 percent by weight of polyol having an average molecular weight above 1500 and about 25 percent by weight of polyol having an average molecular weight below 500.

13. A method of making a flexible polyurethane elastomer of essentially linear structure containing unsatisfied hydroxyl groups and having a compression set less than 15%, an elongation at break of at least 500%, and a recovery which is delayed after compression by at least 0.7 sec, which method comprises reacting substantially linear polyols based on polyalkylene glycol and having an average molecular weight in the range 600 to 1200 with an aromatic diisocyanate which is in less than stoichiometric amount.

17. A method as claimed in claim 13 wherein said substantially linear polyols based on polyalkylene glycol have an average molecular weight in the range of 700 to 900.

18. A method as claimed in claim 13 wherein the reaction is catalyzed by a tertiary amine.

19. A method as claimed in claim 13 further comprising admixing a silicone polycarbinol in an amount not exceeding 2% by weight of the polyol.

20. A method as claimed in claim 19 wherein the amount of silicone polycarbinol is 0.5 to 1% by weight of the polyol.

21. A method as claimed in claim 13 wherein the reaction is carried out under superatmospheric pressure.

22. A method as claimed in claim 21 wherein the pressure is in the range 50 to 150 p.s.i.

23. A method as claimed in claim 13 wherein said substantially linear polyols based on polyalkylene glycol are a blend of a major amount of polyol having an average molecular weight above 1500 and a minor amount of polyol having an average molecular weight below 500.

24. A method as claimed in claim 13 wherein said substantially linear polyols based on polyalkylene glycol are a blend of about 75 percent by weight of polyol having an average molecular weight above 1500 and about 25 percent by weight of polyol having an average molecular weight below 500.