Process and heavy metal catalyst for the polymerization of .alpha.-olefins, particularly polyethylene

• US 4,363,902 A
• Filed: 12/10/1980
• Issued: 12/14/1982
• Est. Priority Date: 03/17/1980
• Status: Expired due to Term

• Current Assignee: Wacker-Chemie GmbH (Dr. Alexander Wacker Familiengesellschaft Mit Beschrã¤Nkter Haftung)
• Original Assignee: Wacker-Chemie GmbH (Dr. Alexander Wacker Familiengesellschaft Mit Beschrã¤Nkter Haftung)
• Inventors: Kurz, Dieter
• Primary Examiner(s): Smith, Edward J.
• Application Number:
  US06/214,704
• Time in Patent Office: 734 Days
• Field of Search: 526/114, 526/116, 526/119, 526/121, 526/122, 526/124, 526/125
• US Class Current: 526/114
• CPC Class Codes: C08F 10/00 Homopolymers and copolymers of unsaturated aliphatic hydrocarbons having only one carbon-to-carbon double bond
• CPC Class Codes: C08F 4/6383 and magnesium or compounds thereof

Abstract

Poly-α-olefins, particularly polyethylene, having a broad molecular-weight distribution, can be prepared in the presence of a catalyst solid which is manufactured in two reaction steps, from a primary solid containing magnesium and chlorine which has been reacted, in a reaction stage A, with alkoxy compounds of elements of Groups I to VI of the Mendeleev Periodic Table which contains at least one secondary or tertiary alkoxy group, and with halogen-containing metal compounds of elements of IV and/or V sub-group(s) of the Mendeleev Periodic Table and, in reaction stage B, with halogen-containing metal compounds of elements of IV and/or V sub-group(s) of the Mendeleev Periodic Table, and/or metal organyl compounds of metals of the II and/or III main group(s) of the Mendeleev Periodic Table. The sequence of the reaction stages A and B is not critical for the success of the process according to the invention.

Claims

1. An improvement in the process for the polymerization of an at least one α

-olefin comprising reacting said α

-olefin under elevated temperatures and pressures in the presence of a solid polymerization catalyst consisting essentially of a solid compound containing (1) element(s) of the IV and/or V sub-group(s) of the Mendeleev Periodic Table, (2) magnesium, (3) halogen, (4) oxygen, and possibly (5) element(s) of the II and/or III main group(s) of the Mendeleev Periodic Table, which solid compound is activated with at least one organometallic compound where said metal is from the II and/or III main group(s) of the Mendeleev Periodic Table, and recovering a polymerizate, the improvement consisting of preparing said solid compound prior to activation, by reacting a primary solid containing magnesium and halogen prepared from at least one hydrocarbon-soluble magnesium compound and at least one halogen compound selected from the group consisting of a chlorohydrocarbon having from 1 to 6 carbon atoms of which at least one carbon atom has at least two directly bonded chlorine atoms, a carbon chloride compound having from 1 to 6 carbon atoms, and mixtures thereof, in two successive and separate reacting stages A and B, in either order, where a solid based on magnesium compound(s) is reacted in reaction stage A in suspension in at least one liquid hydrocarbon with

(i) at least one alkoxy compound of a metal selected from the group consisting of potassium, sodium, magnesium, calcium, zinc, boron, aluminum, silicon, tin, titanium, zirconium, phosphorus, vanadium and sulfur, said compound containing at least one alkoxy group having from 3 to 18 carbon atoms selected from the group consisting of secondary alkoxy and tertiary alkoxy, and

(ii) at least one halogen-containing titanium compound of the formula

space="preserve" listing-type="equation">X.sub.a Ti(OR.sup.4).sub.4-a

wherein X represents halogen, R⁴ is a substituent selected from the group consisting of alkyl having 1 to 8 carbon atoms and hydrocarbon aryl having from 6 to 8 carbon atoms, and a is 2, 3 or 4,

and, in reaction stage B, a solid based on magnesium compound(s) in suspension in at least one liquid hydrocarbon is reacted with

(i) at least one halogen-containing titanium compound of the formula

space="preserve" listing-type="equation">X'"'"'.sub.b Ti(OR.sup.3).sub.4-b

wherein X'"'"' represents halogen, R³ represents a substituent selected from the group consisting of alkyl having from 1 to 8 carbon atoms and hydrocarbon aryl having from 6 to 8 carbon atoms, and b is 2, 3 or 4, and

(ii) at least one organoaluminum compound, whereby a polymerizate is recovered having a broad molecular-weight distribution.

2. The process of claim 1 wherein said at least one halogen compound is a chloroalkane having from 1 to 6 carbon atoms where at least one carbon atom has at least two directly bonded chlorine atoms.

3. The process of claim 1 wherein said reaction stage B occurs before said reaction stage A.

4. The process of claim 1 wherein said reaction stage A occurs before said reaction stage B.

5. The process of claim 1 wherein said metal in said alkoxy compound is selected from the group consisting of silicon, boron and aluminum.

6. The process of claim 1 wherein component (ii) in stage A is titanium tetrachloride.

7. The process of claim 1 wherein component (i) in stage B is titanium tetrachloride.

8. The process of claim 1 or 2 wherein said catalyst solid, after completion of reaction stages A and B, is further washed with at least one liquid hydrocarbon, dispersed in at least one liquid hydrocarbon and reacted with at least one organometallic compound of metals of the II and/or III main group(s) of the Mendeleev Periodic Table, dissolved in at least one liquid hydrocarbon.

9. The process of claim 8 wherein said at least one organometallic compound is at least one organoaluminum compound.

10. The process of claim 1 or 2 wherein said catalyst solid, after completion of reaction stages A and B, is further suspended in at least one liquid hydrocarbon, aged for at least one hour at a temperature of from 50°

C. to 100°

C., and then washed with at least one liquid hydrocarbon.

11. The process of claim 1 or 2 wherein said organoaluminum compound is at least one organoaluminum compound selected from the group consisting of (1) compounds of the formula

12. The process of claim 1 wherein said α

-olefin is a member selected from the group consisting of ethylene and mixtures of ethylene with up to 10 mol percent of α

-alkenes having from 3 to 6 carbon atoms.

14. The process of claim 1 or 13 wherein said primary solid containing magnesium and halogen is purified before further reaction and said solid based on magnesium compounds(s) resulting from stage A or stage B are each purified before further processing.

15. The process of claim 14 wherein said purification after each stage is by washing with liquid hydrocarbons.

16. The process of claim 15 wherein said washing with liquid hydrocarbons is continued until said catalyst is substantially freed from soluble compounds.

13. An improvement in the process for the polymerization of an at least one α

-olefin comprising reacting an α

-olefin selected from the group consisting of ethylene and mixtures of ethylene with up to 10 mol percent of α

-alkenes having from 3 to 6 carbon atoms under elevated temperatures and pressures in the presence of a solid polymerization catalyst consisting essentially of a solid compound containing (1) element(s) of the IV and/or V sub-group(s) of the Mendeleev Periodic Table, (2) magnesium, (3) halogen, (4) oxygen, and possibly (5) element(s) of the II and/or III main group(s) of the Mendeleev Periodic Table, which solid compound is activated with at least one organometallic compound where said metal is from the II and/or III main group(s) of the Mendeleev Periodic Table, and recovering a polymerizate, the improvement consisting of preparing said solid compound prior to activation, by reacting a primary solid containing magnesium and halogen prepared from at least one hydrocarbon-soluble magnesium compound and at least one halogen compound selected from the group consisting of a chlorohydrocarbon having from 1 to 6 carbon atoms of which at least one carbon atom has at least two directly bonded chlorine atoms, a carbon chloride compound having from 1 to 6 carbon atoms, and mixtures thereof, in two successive and separate reacting stages A and B, in either order, where a solid based on magnesium compound(s) is reacted in reaction stage A in suspension in at least one liquid hydrocarbon with

(i) at least one alkoxy compound of a metal selected from the group consisting of potassium, sodium, magnesium, calcium, zinc, boron, aluminum, silicon, tin, titanium, zirconium, phosphorus, vanadium and sulfur, said compound containing at least one alkoxy group having from 3 to 18 carbon atoms selected from the group consisting of secondary alkoxy and tertiary alkoxy, and

(ii) at least one halogen-containing titanium compound of the formula;

space="preserve" listing-type="equation">X.sub.a Ti(OR.sup.6).sub.4-a

wherein X represents halogen, R⁶ is a substituent selected from the group consisting of alkyl having from 1 to 8 carbon atoms and hydrocarbon aryl having from 6 to 8 carbon atoms, and a is 2, 3 or 4,

and, in reaction stage B, a solid based on magnesium compound(s) in suspension in at least one liquid hydrocarbon is reacted with

(i) at least one halogen-containing metal titanium compound of the formula;

space="preserve" listing-type="equation">X'"'"'.sub.b Ti(OR.sup.7).sub.4-b

wherein X'"'"' represents halogen, R⁷ represents a substituent selected from the group consisting of alkyl having from 1 to 8 carbon atoms and hydrocarbon aryl having from 6 to 8 carbon atoms, and b is 2, 3, or 4, and

(ii) at least one organoaluminum compound, whereby a polymerizate is recovered having a broad molecular-weight distribution.