Methods for producing adhesive bonds between substrate and polymer employing an intermediate oxide layer

• US 4,364,731 A
• Filed: 01/29/1981
• Issued: 12/21/1982
• Est. Priority Date: 01/29/1981
• Status: Expired due to Term

• Current Assignee: Board of Regents of the University of Texas System (University of Texas System)
• Original Assignee: Board of Regents of the University of Texas System (University of Texas System)
• Inventors: Norling, Barry K., Bugg, James L. Jr.
• Primary Examiner(s): Robinson, Ellis P.
• Application Number:
  US06/229,752
• Time in Patent Office: 691 Days
• Field of Search: 428/457, 428/447, 428/448, 428/451, 428/446, 428/472, 428/688, 428/432, 428/428, 433/222, 433/223, 433/212, 433/218, 264/19, 523/109, 427/387, 427/407.1, 427/409, 427/412.1, 427/419.2, 204/192 C
• US Class Current: 433/218
• CPC Class Codes: A61C 13/0003 Making bridge-work, inlays, implants or the like
• CPC Class Codes: A61C 5/77 Methods or devices for making crowns
• CPC Class Codes: A61K 6/30 Compositions for temporarily or permanently fixing teeth or palates, e.g. primers for dental adhesives
• CPC Class Codes: C08L 43/04 Homopolymers or copolymers of monomers containing silicon
• CPC Class Codes: Y10T 428/31663 As siloxane, silicone or silane
• CPC Class Codes: Y10T 428/31667 Next to addition polymer from unsaturated monomers, or aldehyde or ketone condensation product
• CPC Class Codes: Y10T 428/31678 Of metal

Abstract

Methods and compositions are provided for enhancing the bonding of polymeric materials to substrates via silane coupling agents. The methods involve depositing an oxide layer, such as alumina or silica, to a substrate, for example stainless steel. Next a silane coupling agent is applied which forms a strong chemical bond with the oxide layer. This layer is then coated or contacted with a polymeric substance. The resulting composite provides a strong adhesive bonding of substrate to polymer.

Claims

1. A method for producing a dental crown composite comprising the steps of:

(a) providing a clean dental crown substrate surface;

(b) depositing onto the substrate surface an exogenous coating of inorganic oxide to a desired thickness on the substrate surface to enhance adhesion between the substrate and subsequently applied silane coupling agent;

(c) bonding a layer of silane coupling agent to the oxide coating; and

(d) applying a polymeric resin to the exposed silane coupling layer.

2. The method according to claim 1 wherein the exogenous inorganic metal oxide coating is selected from the group consisting of alumina, silica, aluminates, silicates, alumino-silicates, and silica-rich glasses.

3. The method according to claim 1 wherein the exogenous inorganic metal oxide coating is alumina or silica.

4. The method according to claim 1 wherein the dental crown substrate is selected from the group consisting of metallic, ceramic, and polymeric materials.

5. The method according to claim 1 wherein the substrate is a metallic material.

6. The method according to claim 1 wherein the substrate is stainless steel.

7. The method according to claim 1 wherein the oxide coating is deposited by sputter deposition.

8. A dental crown composite comprising

a dental crown substrate;

a layer of exogenous inorganic oxide applied to a desired thickness to the surface of the substrate

a layer of silane coupling agent bonded to the layer of oxide; and

a coating of polymeric resin applied to the surface of the silane coupling layer.

9. The dental crown composite according to claim 8 wherein the exogenous oxide is selected from the group consisting of alumina, silica, aluminate, silicates, alumino-silicates and silica-rich glasses.

10. The dental crown composite according to claim 8 wherein the exogenous oxide is alumina or silica.

11. The dental crown composite according to claim 8 wherein the dental crown substrate is selected from the group consisting of metallic, ceramic and polymeric materials.

12. The dental crown composite of claim 8 wherein the substrate is a metallic material.

13. The dental crown composite of claim 8 wherein the substrate is stainless steel.