Method for the manufacture of biaxially orientation-stretched plastic film

• US 4,370,293 A
• Filed: 07/25/1980
• Issued: 01/25/1983
• Est. Priority Date: 07/26/1979
• Status: Expired due to Term

• Current Assignee: Tetra PAK Developpement SA
• Original Assignee: Tetra PAK Developpement SA
• Inventors: Petersen-Hoj, Peter
• Primary Examiner(s): Woo, Jay H.
• Application Number:
  US06/172,704
• Time in Patent Office: 914 Days
• Field of Search: 264/102, 264/290.2, 264/40.3, 264/567, 264/565, 425/66, 425/326.1, 428/220, 428/480
• US Class Current: 264/514
• CPC Class Codes: B29C 48/0018 combined with shaping by orienting, stretching or shrinking, e.g. film blowing B29C48/0017 takes precedence
• CPC Class Codes: B29C 48/0019 combined with shaping by flattening, folding or bending
• CPC Class Codes: B29C 48/03 characterised by the shape of the extruded material at extrusion
• CPC Class Codes: B29C 48/10 flexible, e.g. blown foils
• CPC Class Codes: B29C 48/21 the layers being joined at their surfaces

Abstract

The present invention relates to a method and apparatus for the manufacture of oriented plastic film, in particular polyester film, by the inflation in two steps of an extruded seamless tube of plastic material. The present invention also relates to the laminate manufactured in accordance with the method.

Claims

1. A method of manufacturing biaxially orientation-stretched plastic film, comprising the steps of extruding a plastic film through an annular die to form a seamless tube, simultaneously supplying a gas to the inside of the tube during forming to inflate the tube such that the diameter of the tube is at least doubled, simultaneously drawing out the tube at least to the same extent in its longitudinal direction, cooling the tube thus formed, flattening the tube, sealing the tube by conducting the tube between a first pair of driven rolls, expanding the tube formed in the first inflation operation after the flattening between the first pair of rolls by introducing gas, forming a gas reservoir or gas accumulator for continuously retaining a quantity of the introduced gas between the first and second pair of rolls, flattening the tube between the second pair of rolls, controlling the pressure of the gas in the gas reservoir by selectively moving two compression plates toward and away from one another which plates are arranged on either side of the gas reservoir, inflating the flattened tube again with the gas from the reservoir to increase the diameter to orientation stretch the tube, simultaneously further stretching the inflated tube in its longitudinal direction whereby the tube material is biaxially molecular-oriented, said pressure of the gas in the gas reservoir being controlled such that sufficient pressure is provided to ensure a proper subsequent inflation of the tube and to compensate for gas loss.

2. The method in accordance with claim 1, wherein the step of controlling the pressure of the gas further comprises the steps of opening and closing said first pair of rolls for supplying gas to the gas reservoir and opening and closing said second pair of rolls for withdrawing gas from the gas reservoir.

3. The method in accordance with claim 1, further comprising the steps of cutting the film which has been stretch-processed in three stages in a longitudinal direction of the tube, and spreading the film out to a plane web.

4. The method in accordance with claim 3, further comprising the steps of hardening off said web by heating the web to a temperature exceeding the softening temperature of the plastic material, and simultaneously retaining edge zones of the web at a fixed distance from each other to prevent shrinkage of the material.

5. The method in accordance with claim 1, wherein the plastic tube contains layers of polyester material.

6. The method in accordance with claim 1, wherein the plastic film comprises at least two layers of plastic material which are co-extruded.

7. The method in accordance with claim 1, wherein the plastic film comprises at least one layer of polyester and one layer of cyclohexane-modified polyester.

8. The method in accordance with claim 1, further comprising the step of heating the tube to orientation temperature prior to the orientation stretching.