Fiberglass reinforced plastic insulating member submitted to mechanical efforts within a high-voltage switching enclosure containing sulphur-hexafluoride gas
First Claim
Patent Images
1. A fiberglass-reinforced plastic electric-insulating member which is subject to mechanical forces and in contact with decomposition products of SF6 gas which comprises a fiberglass reinforcement made of a low alkali glass containing neither boron nor boron-containing compounds, said glass having the following composition in percentages by weight:
- 50-65% SiO220-30% Al2 O25-20% MgO2-10% CaOthe sum of the weight percentages of CaO and MgO lying in the range of 15 to 25%,the ratio of the weight percentage of SiO2 to that of Al2 O3 being at least 2 and at the most 2.5, andthe ratio of the weight percentage of MgO to that of SiO2 not exceeding 0.3.
1 Assignment
0 Petitions
Accused Products
Abstract
The resistance of insulating pieces made of fiberglass reinforced plastics against the decay products of SF6, such as occur within sealed high-voltage switching devices is unexpectedly enhanced by the use of a reinforcing fiberglass made of a low-alkali silicate glass containing neither boron nor boron-compounds.
35 Citations
1 Claim
-
1. A fiberglass-reinforced plastic electric-insulating member which is subject to mechanical forces and in contact with decomposition products of SF6 gas which comprises a fiberglass reinforcement made of a low alkali glass containing neither boron nor boron-containing compounds, said glass having the following composition in percentages by weight:
-
50-65% SiO2 20-30% Al2 O2 5-20% MgO 2-10% CaO the sum of the weight percentages of CaO and MgO lying in the range of 15 to 25%, the ratio of the weight percentage of SiO2 to that of Al2 O3 being at least 2 and at the most 2.5, and the ratio of the weight percentage of MgO to that of SiO2 not exceeding 0.3.
-