Uninflammable dynamoelectric machine having coil windings and core encapsulated with unsaturated polyester resin-filler composition

• US 4,387,311 A
• Filed: 03/25/1981
• Issued: 06/07/1983
• Est. Priority Date: 09/09/1977
• Status: Expired due to Term

• Current Assignee: Hitachi, Ltd.
• Original Assignee: Hitachi, Ltd.
• Inventors: Ishikawa, Tetsuo, Ogata, Masatsugu, Yokono, Hitoshi, Hironaka, Kenichi, Kobayashi, Tsuguo, Umetsu, Hideo
• Primary Examiner(s): Lieberman, Paul
• Assistant Examiner(s): SELLERS, ROBERT E
• Application Number:
  US06/247,269
• Time in Patent Office: 804 Days
• Field of Search: 260/40 R, 260/42.8, 310/43, 310/45, 428/920, 428/921, 428/268, 428/480, 428/482
• US Class Current: 310/43
• CPC Class Codes: H02K 5/08 Insulating casings
• CPC Class Codes: Y10S 428/921 Fire or flameproofing
• CPC Class Codes: Y10T 428/31794 Of cross-linked polyester

Abstract

In a dynamoelectric machine having a stator assembly of coil windings and a core, a heat-dissipating, uninflammable, electro-insulative housing encapsulates the coil windings and the core. The housing is made of a cured molded article or material formed of a resin-filler composition which comprises a liquid unsaturated polyester resin, a finely divided calcium carbonate powder, an inorganic mineral particulate having a particle size larger than that of the calcium carbonate powder, a chopped glass fiber and an aluminum hydroxide powder, wherein the ratio by weight of the calcium carbonate to the mineral particulate is 0.3 to 4, the ratio of the weight of glass fiber to the total weight of the composition is 0.05 to 0.25, the ratio of the weight of the polyester resin to the total weight of the composition is 0.1 to 0.4, the weight ratio of the calcium carbonate powder, the mineral particulate and the glass fiber to the total weight of the composition is 0.15 to 0.80, and the weight ratio of the aluminum hydroxide powder to the total weight of the composition is 0.1 to 0.6.

Claims

1. A dynamoelectric machine comprising a stator assembly including coil windings and a core encapsulated with a heat-dissipating, electro-insulative housing, a rotor assembly including a shaft centrally disposed thereto, and a bearing assembly disposed to the stator assembly, for rotatably supporting the shaft, wherein the housing is made of a cured resin-filler composition comprising:

(I) a liquid unsaturated polyester resin containing an ethylenically unsaturated compound monomer and a curing catalyst, which has a viscosity of from 50 to 50,000 centipoises at 25°

C.; and

(II) an inorganic, electro-insulative filler consisting essentially of

(a) a calcium carbonate powder having a particle size corresponding to that of particles which can pass a 325 mesh sieve,

(b) an inorganic mineral particulate having a particle size corresponding to that of particles which can pass a 12 mesh sieve and is retained on a 200 mesh sieve,

(c) a chopped glass fiber having a length larger than 200 μ

m and a diameter less than 150 μ

m after the composition has been kneaded, and

(III) an aluminum hydroxide powder which passes a 250 mesh sieve,

wherein the ratios by weight of the respective ingredients are as follows;

(a)/(b)=0.3 to 4, (c)/total weight of the composition=0.05 to 0.25, and ((a)+(b))/total weight of the composition=0.1 to 0.5,

(I)/total weight of the composition=0.1 to 0.4, and

III/total weight of the composition=0.2 to 0.6,

whereby said aluminum hydroxide powder acts to cool said resin and inhibit pyrolysis and combustion of said resin by releasing water of crystallization contained in the aluminum hydroxide powder when the cured resin-filler composition is heated excessively.

2. A dynamoelectric machine according to claim 1, wherein the mineral particulate is silica sand.

3. A dynamoelectric machine according to claim 1, wherein the length of the glass fibers is within a range of 200 to 5,000 μ

m after the resin filler composition system has thoroughly been kneaded.

4. A dynamoelectric machine according to claim 1, wherein the unsaturated polyester resin comprises a mixture of vinyl esters of a bisphenol A type epoxy compound or a novolac type epoxy compound with dimethacrylate or acrylate.

10. A dynamoelectric machine according to claim 1, wherein the unsaturated compound monomer is styrene.

11. A dynamoelectric machine according to claim 10, wherein the curing catalyst is dicumyl peroxide.

12. A dynamoelectric machine according to claim 1, wherein the unsaturated compound monomer is contained in an amount of 20% to 50% by weight of the total weight of the monomer and unsaturated polyester resin.

13. A dynamoelectric machine according to claim 1, wherein the calcium carbonate powder has a particle size less than 20 μ

m.

14. A dynamoelectric machine according to claim 1, wherein the glass fibers have a diameter of from 5 to 20 μ

m.

5. A dynamoelectric machine comprising a stator assembly including coil windings and a core encapsulated with a heat-dissipating, electro-insulative housing, a rotor assembly including a shaft centrally disposed thereto, and a bearing assembly, disposed to the stator assembly, for rotatably supporting the shaft, in which interstices between the coil windings and cavities are rigidly and voidlessly filled with a cured article and the outer surface of the housing is exposed to the atmosphere so as to dissipate heat generated by operation of the dynamoelectric machine, wherein the cured article has a coefficient of linear thermal expansion less than 3×

10^-5 cm/cm/°

C. and is made of a resin-filler composition comprising;

(I) a liquid unsaturated polyester resin composition containing an ethylenically unsaturated compound monomer and a curing catalyst, which has a viscosity of from 50,000 to 50 centipoises at 25°

C.;

(II) an inorganic, electro-insulative filler consisting essentially of,

(a) a calcium carbonate powder which passes a 325 mesh sieve,

(b) an inorganic mineral particulate, at least 95% of which passes a 12 mesh sieve and is retained on a 200 mesh sieve, and

(c) a glass fiber having a length larger than 200 μ

m and a diameter less than 150 μ

m; and

(III) an aluminum hydroxide powder which passes a 250 mesh sieve,

wherein the ratios by weight of the respective ingredients are as follows;

(a)/(b)=0.3 to 4, (c)/total weight of the composition system=0.05 to 0.25, and ((a)+(b))/total weight of the composition=0.1 to 0.5,

(I)/total weight of the composition system=0.1 to 0.4, and

(III)/total weight of the composition system=0.2 to 0.4,

whereby said aluminum hydroxide powder acts to cool said resin and inhibit pyrolysis and combustion of said resin by releasing water of crystallization contained in the aluminum hydroxide powder when the cured resin-filler composition is heated excessively.

6. A dynamoelectric machine according to claim 5, wherein the calcium carbonate powder is a finely divided powder of limestone.

7. A dynamoelectric machine according to claim 5, wherein the mineral particulate is a silica sand powder which passes a 12 mesh sieve and is retained on a 150 mesh sieve.

8. A dynamoelectric machine according to claim 5, wherein the mineral particulate is a member selected from the group consisting of river sand, mountain sand, beach sand, limestone powder and combinations thereof.

9. A dynamoelectric machine according to claim 5, wherein the filler consists essentially of,

(a) a calcium carbonate powder having a mean particle size less than 5 μ

m,

(b) a mineral particulate, at least 95% of which passes a 12 mesh sieve and is retained on a 150 mesh sieve, the particulate being a member selected from the group consisting of river sand, mountain sand, beach sand, limestone powder and combinations thereof, and

(c) a chopped glass fiber having a length of from 200 to 50,000 μ

m, and a diameter of 5 to 20 μ

m.