High lead solder corrosion inhibitors

• US 4,402,847 A
• Filed: 05/19/1982
• Issued: 09/06/1983
• Est. Priority Date: 05/19/1982
• Status: Expired due to Term

• Current Assignee: Ashland Licensing and Intellectual Property Llc
• Original Assignee: BASF Wyandotte Corporation
• Inventors: Wilson, Joe C., Hirozawa, Stanley T.
• Primary Examiner(s): Gluck, Irwin
• Application Number:
  US06/379,641
• Time in Patent Office: 475 Days
• Field of Search: 252/389 R, 252/389 A, 252/68, 252/73, 252/75, 252/76, 252/78.3, 252/181, 106/14.12, 106/14.15, 106/14.16, 106/14.44, 106/14.45, 422/13, 422/16, 422/18, 62/DIG. 20, 62/83
• US Class Current: 252/75
• CPC Class Codes: C09K 5/20 Antifreeze additives therefor, e.g. for radiator liquids for application to surfaces C09K3/18; inhibiting corrosion by liquids C23F11/00
• CPC Class Codes: C23F 11/10 using organic inhibitors
• CPC Class Codes: Y10S 62/20 Materials used to prevent corrosion in refrigeration system

Abstract

Compositions and method of using said compositions for inhibiting mineral scale and the corrosion of high lead solder and the cavitation-erosion corrosion of aluminum in aqueous systems are disclosed. Unexpectedly, a mixture of a siloxane-silicate copolymer with an azole is effective in reducing the corrosion of high lead solder and aluminum, particularly the cavitation-erosion corrosion of aluminum in contact with aqueous liquids, such as aqueous alcohol solutions used as heat transfer media. Antifreeze concentrates and a process for inhibiting corrosion are also disclosed.

Claims

1. A composition for inhibiting mineral scale and the corrosion of metals in the presence of an aqueous liquid and particularly the corrosion of high lead solder and the cavitation-erosion corrosion of aluminum, comprising:

A. an effective metal corrosion inhibiting amount of a siloxane-silicate copolymer containing about 0.1 to about 99.9 parts by weight, per 100 parts by weight of said copolymer, of (a) at least one siloxane group represented by the formula;

space="preserve" listing-type="equation">RSiO.sub.1.5

wherein R is selected from the group consisting of a monovalent aliphatic hydrocarbon having 1 to about 18 carbon atoms, a phenyl group, and a vinyl group and 0.1 to 99.9 parts by weight, per 100 parts by weight of said copolymer, of (b) at least one silicate group represented by the formula;

##EQU2## wherein M is a cation which forms a water-soluble silicate, d is the valence of the cation represented by M and has a value of at least 1 and e has a value of 1 to 3 and

B. an effective metal corrosion inhibiting amount of an azole.

2. The composition of claim 1 additionally comprising an effective corrosion inhibiting amount of a water-soluble metal salt nitrate and a pH buffering compound capable of providing a pH of about 8 to about 11 in the presence of said aqueous liquid.

3. The composition of claim 2 wherein said siloxane is selected from the group consisting of methyl, ethyl, and phenyl siloxane, said aqueous liquid comprises water, a water-soluble alcohol, or a water-miscible organic liquid;

and said azole is selected from the group consisting of at least one of an alkali metal mercaptobenzothiazole and an alkali metal tolyltriazole.

4. The composition of claim 3 wherein said copolymer is a copolymer of methyl siloxane and an alkali metal silicate.

5. The composition of claim 4 wherein said composition additionally comprises a pH buffer compound selected from the group consisting of alkali metal benzoate, alkali metal hydroxybenzoates, alkali metal phosphates, and alkali metal carbonates.

6. A corrosion inhibiting alcohol-based antifreeze concentrate adapted to inhibit the corrosion of metals in contact with aqueous liquids, includingy cavitation-erosion corrosion of aluminum and the corrosion of high lead solder, comprising a water-soluble alcohol, a metal corrosion inhibiting amount of the siloxane-silicate copolymer of claim 1, and an azole.

7. The concentrate of claim 6 wherein said concentrate additionally comprises a water-soluble metal salt nitrate, a pH buffering compound capable of maintaining the pH of said alcohol-based antifreeze in the range of about 8 to about 11 and wherein said water-soluble alcohol has 1 to 4 carbon atoms and 1 to 3 hydroxy groups.

8. The concentrate of claim 7 wherein said azole is selected from at least one of the group consisting of an alkali metal mercaptobenzoate and an alkali metal tolyltriazole and said alcohol is ethylene glycol.

9. The concentrate of claim 8 wherein said pH buffer is selected from at least one of the group consisting of alkali metal benzoate, alkali metal hydroxybenzoates, alkali metal phosphates, and alkali metal carbonates, and wherein said siloxane silicate copolymer is the reaction product of methyl siloxane and an alkali metal silicate.

10. A corrosion-resistant aqueous liquid useful for inhibiting the corrosion of high lead solder in contact with aqueous compositions and for inhibiting the cavitation-erosion corrosion of aluminum in contact with aqueous liquids comprising an aqueous liquids and a minor but effective metal corrosion inhibiting amount, sufficient to inhibit the corrosion of high lead solder and the cavitation-erosion corrosion of aluminum in contact with aqueous liquids, comprising a mixture of water, the siloxane-silicate copolymer of claim 1, an azole selected from at least one of the group consisting of an alkali metal mercaptobenzothiazole, and an alkali metal tolyltriazole.

11. The compositin of claim 10 wherein said alkai metal mercaptobenzothiazole is sodium mercaptobenzothiazole which is present in the proportion of at least about 0.05 percent by weight of said aqueous liquid and said aqueous liquid comprises ethylene glycol.

12. The composition of claim 11 additionally comprising a water-soluble metal salt nitrate and a buffer compound capable of maintaining the pH of said ethylene glycol at about 8 to about 11.

13. The composition of claim 12 wherein said siloxane-silicate copolymer is the reaction product of methyl siloxane and an alkali metal silicate.

14. In a process for inhibiting the corrosion of high lead solder and the cavitation-erosion corrosion of aluminum in contact with an aqueous liquid, the improvement wherein said aqueous liquid comprises a water-miscible glycol, a minor but effective metal corrosion inhibiting amount of the siloxane-silicate copolymer of claim 1, and an azole.

15. The process of claim 14 wherein said water-miscible glycol has 1 to about 4 carbon atoms and 1 to about 3 hydroxy groups and said siloxane-silicate copolymer is the reaction product of methyl siloxane and an alkali metal silicate.

16. The process of claim 15 wherein said azole is selected from the group consisting of at least one of an alkali metal mercaptobenzothiazole and an alkali metal tolyltriazole.

17. The process of claim 16 wherein said aqueous liquid additionally comprises a water-soluble metal salt nitrate and a pH buffer compound capable of maintaining the pH of said aqueous liquid at about 8 to about 11.