• US 4,410,385 A
• Filed: 04/07/1982
• Issued: 10/18/1983
• Est. Priority Date: 01/28/1981
• Status: Expired due to Fees

• Current Assignee: General Electric Company
• Original Assignee: General Electric Company
• Inventors: Jones, Jackie D., Murphy, Guy C., Salemme, Charles T.
• Primary Examiner(s): Bell, James J.
• Application Number:
  US06/366,410
• Time in Patent Office: 559 Days
• Field of Search: 156/290, 156/168, 156/181, 156/291, 156/307.1, 156/308.2, 418/196, 418/198, 418/246, 418/257, 418/258, 418/259, 418/296, 418/297, 418/298, 418/408
• US Class Current: 156/181
• CPC Class Codes: B29B 11/16 comprising fillers or reinforcement non-woven fabrics per se D04H1/00, D04H3/00
• CPC Class Codes: B29C 70/22 oriented in at least two directions forming a two dimensional structure woven fabrics per se D03D; knitted fabrics per se D04D; braid per se D04C
• CPC Class Codes: D06M 23/06 Processes in which the treating agent is dispersed in a gas, e.g. aerosols aerosol compositions C09K3/30

Abstract

A composite fabric preform and article made of both structural and thermoplastic fibrous materials and a method of making such preform and article, the method improving the handling properties of the composite. A plurality of layers of fabric made from structural fibrous material are disposed in a stacked assembly with layers sequentially adjacent each other. At least each of alternate layers of the alternate layers of fabric include within its weave thermoplastic fibrous material intermixed with the structural fibrous material. The layers of fabric, preferably under pressure, are heated at a temperature sufficient to promote bonding action by the thermoplastic fibers at junctures between fibrous materials.

Claims

1. In a method of making a substantially dry composite fabric preform the steps of:

providing a plurality of layers of a first fabric which includes within its weave a thermoplastic fibrous material intermixed with a structural fibrous material selected from the group consisting of carbon, graphite, glass, boron, silicon, refractories and their combinations;

disposing the plurality of layers in a stacked assembly with the layers sequentially adjacent each other; and

heating the layers at a temperature sufficient to promote a bonding action by the thermoplastic fibrous material at junctures between the fibrous materials.

2. The method of claim 1 in which pressure is applied to the stacked assembly to provide compacted layers during heating.

3. The method of claim 1 wherein a layer of a second fabric substantially of a structural fibrous material is disposed between at least one pair of the plurality of adjacent layers of the first fabric in the stacked assembly prior to application of heat.

4. The method of claim 1 in which the thermoplastic fibrous material is provided in a range of from a small but effective amount sufficient to provide the bonding action up to about 60 volume percent of the total volume of the layer.

5. The method of claim 4 in which the thermoplastic fibrous material is provided in the range of about 2-25 volume percent.

7. The method of claim 4 in which each layer includes thermoplastic fibrous material.

6. In a method of making a composite article the steps of:

providing a plurality of layers of woven fabric each including structural fibrous yarn made of fibers of materials selected from the group consisting of carbon, graphite, glass, boron, silicon, refractories and their combinations;

disposing the plurality of layers in a stacked assembly with the layers sequentially adjacent and in contact with each other;

at least each alternating of the layers in the stacked assembly including within its weave a thermoplastic fibrous material intermixed with the structural fibrous material and selected from the group consisting of heat softenable polyamide, polyacrylic, polyester, polyolefins, derivatives of the foregoing, and mixtures thereof;

the thermoplastic fibrous material, in the layers in which it is included, comprising from a small but effective amount sufficient to promote a bonding action up to about 60 volume percent of the total volume of the layer;

applying pressure to the stacked assembly to provide compacted layers, while

heating the compacted layers at a temperature sufficient to promote a bonding action by the thermoplastic fibrous material at junctures between the fibrous material to provide a substantially dry composite fabric preform; and

impregnating the preform with a resin.