Conformal coating and potting system

• US 4,415,604 A
• Filed: 11/12/1982
• Issued: 11/15/1983
• Est. Priority Date: 11/12/1982
• Status: Expired due to Term

• Current Assignee: Loctite Corporation (Henkel AG & Co KGaA)
• Original Assignee: Loctite Corporation (Henkel AG & Co KGaA)
• Inventors: Nativi, Larry A.
• Primary Examiner(s): Newsome, John H.
• Application Number:
  US06/441,164
• Time in Patent Office: 368 Days
• Field of Search: 427/54.1, 427/44, 204/159.16, 204/159.19, 204/159.15, 525/455
• US Class Current: 427/510
• CPC Class Codes: C08F 283/006 on to polymers provided for in C08G18/00 C08F283/004 takes precedence
• CPC Class Codes: C08G 18/10 Prepolymer processes involving reaction of isocyanates or isothiocyanates with compounds having active hydrogen in a first reaction step
• CPC Class Codes: C08G 18/307 Atmospheric humidity
• CPC Class Codes: C08G 18/4812 Mixtures of polyetherdiols with polyetherpolyols having at least three hydroxy groups
• CPC Class Codes: H05K 2201/09872 Insulating conformal coating foil encapsulation H05K2203/1311

Abstract

Ultraviolet curable polymerizable coating system having a built-in secondary curing mechanism is disclosed. The polymerizable coating system is a one component system comprising at least one isocyanate-capped polyether diol and triol, an acrylate or methacrylate reactive diluent, and a polymerization initiator of the photo-initiator type. The coating system is also moisture curable.

Claims

1. A one-part coating composition, especially useful for conformal coating and potting, comprising:

(1) At least one isocyanate-capped polyether diol and triol;

(2) An acrylate or methacrylate reactive diluent; and

(3) A polymerization initiator of the photo-initiator type.

2. The coating and potting composition of claim 1, wherein said isocyanate-capped polyether diol and triol comprises the reaction product of a blend of at least one polyether diol and at least one polyether triol with excess diisocyanate.

3. The coating and potting composition of claim 2, where the polyether diol portion comprises a polyether diol of molecular weight in the range of about 300 to about 5,000 average.

4. The coating composition of claim 2, wherein the polyether triol portion comprises a polyether triol of molecular weight in the range of about 200 to about 3,000 average.

5. The coating and potting composition of claim 2, where said polyether diol has a molecular weight of about 400 to about 1,000 average, and said polyether triol has a molecular weight of about 700 average.

6. The coating and potting composition of claim 2, where said polyether diol and polyether triol blend comprises said polyether diol in major proportion.

7. The coating and potting composition of claim 2, where said isocyanate-capped polyether diol and triol comprises the reaction product about 1.0 equivalents of said polyether diol and polyether triol blend with about 1.6 to about 2.2 equivalents of diisocyanate.

8. The coating and potting composition of claim 6, and comprising about 1.0 equivalents of said polyether diol and polyether triol blend with about 2.0 equivalents of diisocyanate.

9. The coating and potting composition of claim 8, and comprising about 0.916 equivalents of polyether diol of molecular weight of about 400 to about 1000 average, 0.084 equivalents of a polyether triol of molecular weight of about 700 average, and 2.0 equivalents of diphenyl methane diisocyanate.

10. The coating and potting composition of claim 2, wherein said acrylate or methacrylate reactive diluent is selected from the group consisting of trimethylol propane ethoxylate triacrylate, dicyclopentadiene methacrylate, dicyclopentadiene acrylate, isobutyl methacrylate, isobornyl methacrylate, lauryl methacrylate and cyclohexylmethacrylate.

11. The coating and potting composition of claim 2, and further comprising an anionic surfactant.

12. A coating composition of claim 2, wherein said acrylate or methacrylate reactive diluent comprises about 25 to about 50% by weight of said coating composition.

13. A coating composition of claim 12, wherein said acrylate or methacrylate reactive diluent comprises about 35% by weight of said coating composition.

17. A printed circuit board having one or more components mounted thereon, and covered at least in part with the cured coating composition of claim 1.

18. An electrical or electronic component covered at least in part with the cured coating of claim 1.

14. A method of forming a uv curing polymerizable conformal coating or potting on a substrate wherein said substrate has one or more shadow areas, comprising the steps in sequence of:

(1) providing a polymerizable coating composition which comprises at least one isocyanate-capped polyether diol and triol, an acrylate or methacrylate reactive diluent, and a polymerization initiator of the photo-initiator part;

(2) applying said coating composition to said substrate;

(3) exposing the coated substrate to uv light of wave length and intensity to effect uv cure of exposed areas of said coating; and

(4) storing said coated substrate under conditions of temperature and humidity such as to promote curing of unexposed (shadow) areas of said coating through a built-in secondary cure mechanism.

15. A method according to claim 14, wherein said substrate comprises a circuit board having one or more components mounted thereon.

16. A method according to claim 14, wherein said substrate comprises an electrical or electronic component.