Ungelled polyepoxide-polyoxyalkylenepolyamine resins, aqueous dispersions thereof, and their use in cationic electrodeposition

• US 4,420,574 A
• Filed: 09/20/1982
• Issued: 12/13/1983
• Est. Priority Date: 07/20/1981
• Status: Expired due to Term

• Current Assignee: PPG Industries Incorporated (Nouryon BV)
• Original Assignee: PPG Industries Incorporated (Nouryon BV)
• Inventors: Moriarity, Thomas C., Geiger, William J.
• Primary Examiner(s): Pertilla, Theodore E.
• Application Number:
  US06/420,551
• Time in Patent Office: 449 Days
• Field of Search: 523/404, 523/415, 523/416, 523/417, 523/420, 524/901, 204/181 C, 525/113, 525/526
• US Class Current: 523/404
• CPC Class Codes: C08L 2666/22 Macromolecular compounds not provided for in C08L2666/16 - C08L2666/20
• CPC Class Codes: C08L 63/00 Compositions of epoxy resins; Compositions of derivatives of epoxy resins
• CPC Class Codes: C09D 5/443 Polyepoxides
• CPC Class Codes: Y10S 524/901 Electrodepositable compositions

Abstract

Ungelled resins, aqueous dispersions of cationic resins, coating compositions, and electrodeposition using the resinous coating compositions are disclosed. The resins are formed from reacting polyepoxides with polyoxyalkylenepolyamines. The aqueous dispersions are prepared by at least partially neutralizing the resins to provide cationic groups and dispersing the cationic resins in aqueous medium. When added to cationic electrode-positable coating compositions, such as high throwpower compositions, the ungelled cationic resins provide better appearing, more flexible and water-resistant electrodeposited coatings.

Claims

1. An aqueous resinous dispersion which contains from:

(A) 0.5 to 40 percent by weight of an ungelled resin formed from reacting;

(i) a polyepoxide with

(ii) a polyoxyalkylenepolyamine;

the ratio of equivalents of active hydrogens in (ii), with primary amine groups being considered monofunctional, to equivalents of epoxy in (i) being within the range of 1.20 to 1.70;

1, the reaction product being at least partially neutralized with acid to provide cationic groups,

(B) 60 to 99.5 percent by weight of an additional cationic resin different from (A) and which is electrodepositable on a cathode;

the percentages by weight being based on total weight of (A) plus (B).

2. The aqueous dispersion of claim 1 wherein the polyepoxide is a polyglycidyl ether of a cyclic polyol.

3. The aqueous dispersion of claim 2 wherein the cyclic polyol is a diol.

4. The aqueous dispersion of claim 3 wherein the polyglycidyl ether of the cyclic diol is a polyglycidyl ether of bisphenol A or hydrogenated bisphenol A having a molecular weight within the range of 340 to 2000.

5. The aqueous dispersion of claim 1 in which the polyoxyalkylenepolyamine is a polyoxypropylenepolyamine.

6. The aqueous dispersion of claim 5 in which the polyoxypropylenepolyamine is a diamine.

7. The aqueous dispersion of claim 1 in which the polyoxyalkylenepolyamine has a molecular weight within the range of 137 to 3600.

8. The aqueous dispersion of claim 7 in which the polyoxyalkylenepolyamine has an amine equivalent weight of about 69 to 1800.

9. The aqueous dispersion of claim 1 containing 0.5 to 50 percent by weight of (A) plus (B) based on total weight of the aqueous dispersion.