Treatment of metal with derivative of poly-4-vinylphenol

• US 4,433,015 A
• Filed: 04/07/1982
• Issued: 02/21/1984
• Est. Priority Date: 04/07/1982
• Status: Expired due to Term

• Current Assignee: Parker Chemical Co. (Ford Motor Company)
• Original Assignee: Parker Chemical Co. (Ford Motor Company)
• Inventors: Lindert, Andreas
• Primary Examiner(s): Page, Thurman K.
• Application Number:
  US06/366,449
• Time in Patent Office: 685 Days
• Field of Search: 148/6.15 R, 427/388.2, 427/388.4, 427/207.1, 427/208.2, 427/409, 156/327, 156/330.9, 156/331.6, 524/555, 524/543, 524/551, 524/547
• US Class Current: 427/388.4
• CPC Class Codes: B05D 3/102 Pretreatment of metallic substrates C23C takes precedence
• CPC Class Codes: B05D 7/16 using synthetic lacquers or varnishes
• CPC Class Codes: C09D 5/08 Anti-corrosive paints
• CPC Class Codes: C23C 22/83 Chemical after-treatment

Abstract

An aqueous solution comprising an effective amount of a water soluble or water dispersible compound selected from the group consisting of a polymer having the following general formula, acid salts thereof and mixtures thereof: ##STR1## where: n=from 2 up to a number at which the polymer is not water soluble or water dispersible;

X=H or Z; ##STR2## Y=H, Z, Cr₅ R₆ OR₇, or CH₂ Cl; R₁ through R₇ =H, or an alkyl, aryl, hydroxy-alkyl, amino-alkyl, mercaptoalkyl or phospho-alkyl moiety, said R₁ through R₇ being of carbon chain lengths up to a length at which the compound is not water soluble or dispersible;

wherein at least one of X or Y=Z and the Z moieties are present in sufficient amount that the compound is water soluble or water dispersible.

This solution is useful in the treatment of metal surfaces to impart corrosion resistance and paint adhesion characteristics thereto.

Claims

1. A stable aqueous composition comprising an effective amount of a water soluble or water dispersible compound selected from the group consisting of a polymer having the following general formula, acid salts thereof and mixtures thereof:

##STR8## where;

n=from 2 up to a number at which the polymer is not water soluble or water dispersible;

X=H or Z;

##STR9## Y=H, Z, CR₅ R₆ OR₇, or CH₂ Cl;

R₁ through R₇ =H, or an alkyl, aryl, hydroxy-alkyl, amino-alkyl, mercapto-alkyl or phospho-alkyl moiety, said R₁ through R₇ being of carbon chain lengths up to a length at which the compound is not water soluble or dispersible;

wherein at least one of X or Y=Z and the Z moieties are present in sufficient amount that the compound is water soluble or water dispersible to form such stable aqueous composition.

2. The aqueous composition of claim 1 wherein the molar percent of Z per monomer is from about 10% to about 200%.

3. The aqueous composition of claim 1 wherein the molar percent of Z per monomer is from about 50% to about 150%.

4. The aqueous composition of claim 1 wherein the pH is from about 0.5 to about 12.

5. The aqueous composition of claim 4 wherein the pH is from about 2.0 to about 8.0.

6. The aqueous composition of claim 4 wherein said compound is present in an amount of from about 0.01% to about 5%.

7. The aqueous composition of claim 6 wherein said compound is present in an amount of from about 0.1% to about 1%.

8. The aqueous composition of claim 1 wherein said compound is present in an amount of from about 5% to about 30%.

9. The aqueous composition of claim 1 wherein Z is ##STR10##

10. The aqueous composition of claim 1 wherein Z is ##STR11##

11. The aqueous composition of claim 1 wherein said compound is the reaction product of a poly-4-vinylphenol, formaldehyde and a secondary amine.

12. The process of treating a metal surface comprising contacting a metal surface with a composition of any of claims 2 through 11 for a period of time sufficient to impart improved corrosion resistance and/or paint adhesion characteristics to the metal surface and, thereafter, drying the thus-treated surface.