Process for the manufacture of fine propellant powders by granulation, and powders thus obtained
First Claim
1. Process for the manufacture of fine granular, completely gelatinized porous propellant powders from at least one solid base material which consists of an energy producing material, wherein said base material is ground to a particle size of less than 300 microns, containing about 20% water, is disintegrated, fed into a rotating apparatus while a solvent for said at least one solid base is sprayed thereon, the solvent being insoluble or little soluble in water, whereby the material is agglomerated and formed into granules, the granules thus obtained are subjected to a first partial drying at room temperature, the product is again shaped in a rotating apparatus, the total wetting level in respect of the solvent is between 60% and 140% with respect to the weight of the dry base material and the granules are dried.
1 Assignment
0 Petitions
Accused Products
Abstract
The present invention relates to a process for the manufacture of fine propellant powders by granulation, and, by way of products, to the fine powders thus obtained.
The process according to the invention consists in granulating the base materials, wetted with solvent, in a granulating tray 11, in subsequently subjecting the granules thus obtained to a first partial drying in a drier 14, and in completing the finishing of the said granules in a rounder 16, optionally in the presence of solvent.
The process according to the invention can be carried out continuously or batchwise, with a very high degree of operational safety. The propellant powders thus obtained possess a good activity and are suitable for small-caliber and medium-caliber weapons.
11 Citations
14 Claims
- 1. Process for the manufacture of fine granular, completely gelatinized porous propellant powders from at least one solid base material which consists of an energy producing material, wherein said base material is ground to a particle size of less than 300 microns, containing about 20% water, is disintegrated, fed into a rotating apparatus while a solvent for said at least one solid base is sprayed thereon, the solvent being insoluble or little soluble in water, whereby the material is agglomerated and formed into granules, the granules thus obtained are subjected to a first partial drying at room temperature, the product is again shaped in a rotating apparatus, the total wetting level in respect of the solvent is between 60% and 140% with respect to the weight of the dry base material and the granules are dried.
-
13. A propellant in the form of granules of ballistic properties adequate for small caliber weapons which consists of a porous, completely gelatinized heterogeneous mass obtained by grinding at least one solid base material which consists of an energy producing material, containing about 20% water, to a particle size of less than 300 microns, disintegrating the ground material, feeding it into a rotating apparatus while a solvent for said at least one solid base material is sprayed thereon, the solvent being insoluble or little soluble in water, whereby the material is agglomerated and formed into granules, the granules thus obtained are subjected to a first partial drying at room temperature, the product is again shaped in a rotating apparatus, the total wetting level in respect of the solvent is between 60% and 140% with respect to the weight of the dry base material, and drying the granules.
Specification
-
- Resources
-
Current AssigneeSociete Nationale Des Poudres Et Explosifs
-
Original AssigneeSociete Nationale Des Poudres Et Explosifs
-
InventorsBertrand, Yves, Wiedemann, Bernard, Gaudilliere, Pierre, Perennou, Jean-Charles, Favrot, Remy
-
Primary Examiner(s)Sebastian, Leland A.
-
Application NumberUS06/321,096Time in Patent Office893 DaysField of Search102/292, 149/96, 149/2, 149/118, 264/3 CUS Class Current149/2CPC Class CodesC06B 21/0066 by granulation, e.g. flakingY10S 149/118 Gel contains resin