Silicone gel filled prosthesis

• US 4,455,691 A
• Filed: 10/03/1979
• Issued: 06/26/1984
• Est. Priority Date: 10/03/1979
• Status: Expired due to Term

• Current Assignee: McGhan Medical Corporation (Abbvie Incorporated)
• Original Assignee: 3M Company
• Inventors: Compton, Richard A., Van Aken Redinger, Peter
• Primary Examiner(s): Crowder, Clifford D.
• Application Number:
  US06/081,379
• Time in Patent Office: 1,728 Days
• Field of Search: 3/36, 428/447, 426/127, 528/42, 528/901
• US Class Current: 623/8
• CPC Class Codes: A61F 2/12 Mammary prostheses and implants
• CPC Class Codes: A61L 27/18 obtained otherwise than by reactions only involving carbon-to-carbon unsaturated bonds
• CPC Class Codes: B29C 41/14 Dipping a core B29C41/10 takes precedence
• CPC Class Codes: C08L 83/04 Polysiloxanes
• CPC Class Codes: Y10S 528/901 Room temperature curable silicon-containing polymer
• CPC Class Codes: Y10T 428/31663 As siloxane, silicone or silane

Abstract

A prosthesis for subcutaneous implantation in a patient comprising a flexible sac and a silicone gel contained within the sac. The wall of the sac is comprised of at least one continuous layer of silicone elastomer which substantially impedes the migration of said silicone gel from the sac.

Claims

1. A prosthesis for subcutaneous implantation in a patient comprising a flexible sac and a silicone gel contained within said sac, said sac being comprised of a silicone elastomer wall between 0.05 mm and about 0.2 mm in thickness, said wall comprising a layer of silicone elastomer which substantially impedes the migration of said silicone gel through said wall and has a weight increase of less than 10% when tested in accordance with ASTM D471 using a dimethylpolysiloxane test gel having 300 centistoke viscosity, and being at least 0.025 mm in thickness.

2. The prosthesis of claim 1 wherein the silicone elastomer of said wall is a reaction product of diphenylpolysiloxane and dimethylpolysiloxane, said product having from about 8 to about 50 mole percent diphenylpolysiloxane substituents.

3. The prosthesis of claim 1 wherein the silicone elastomer is a reaction product of methyl 3,3,3-trifluoropropylpolysiloxane and dimethylpolysiloxane, said product having at least 90 mole percent methyl 3,3,3-trifluoropropylpolysiloxane substituents.

4. The prosthesis of claim 1 wherein the silicone elastomer is comprised of a reaction product of methylphenylpolysiloxane and dimethylpolysiloxane, said product having from about 15 to about 50 mole percent methylphenylpolysiloxane substituents.

5. A prosthesis for subcutaneous implantation in a patient comprising a flexible sac and silicone gel contained within said sac, said sac being comprised of a composite wall comprising at least two layers of silicone elastomer and being between about 0.05 and about 0.2 mm thick, one of said layers comprising a silicone elastomer which substantially impedes the migration of the silicone gel through said sac and has a weight increase of less than 10% when tested in accordance with ASTM D471 utilizing a dimethylpolysiloxane test gel having a 300 centistoke viscosity, and is at least about 0.025 mm in thickness.

6. The prosthesis of claim 5 wherein the layer of said composite wall having a change in weight of less than 10% when tested in accordance with ASTM D471, is between about 0.025 mm and 0.05 mm in thickness.

7. The prosthesis of claim 5 wherein the layer of said composite wall having a change in weight of less than 10% when tested in accordance with ASTM D471 is a reaction product of diphenylpolysiloxane and dimethylpolysiloxane, said product having from about 8 to about 30 mole percent diphenylpolysiloxane substituents.

8. The prosthesis of claim 5 wherein the layer of said composite wall having a change in weight of less than 10% when tested in accordance with ASTM D471, is a reaction product of methyl 3,3,3-trifluoropropylpolysiloxane and dimethylpolysiloxane, said product having not less than 90 mole percent methyl 3,3,3-trifluoropropylpolysiloxane substituents.

9. The prosthesis of claim 5 wherein the layer of said composite wall having a change in weight of less than 10% when tested in accordance with ASTM D471 is a reaction product of methylphenylpolysiloxane and dimethylpolysiloxane polymers, said product having at least 30 mole percent methylphenylpolysiloxane substituents.

10. A silicone gel-filled silicone rubber article possessing a reduced tendency to exhibit surface-bleed comprising

(A) a flexible container of silicone rubber consisting essentially of a cross-linked gum of polydimethylsiloxane, said container being filled with

(B) a silicone gel composition consisting essentially of a silicone gel of cross-linked polydimethylsiloxane, there being

(C) an essentially continuous barrier layer of a filler-containing composition consisting essentially of fluorine-containing organopolysiloxane situated between the interior of container (A) and the gel composition of (B), said barrier layer being coated on the interior wall of container (A).

11. A silicone gel-filled silicone rubber article possessing a reduced tendency to exhibit surface-bleed comprising:

(A) a flexible container of fluorosilicone rubber consisting essentially of a cross-linked gum of fluoroalkylpolysiloxane, said fluoroalkylpolysiloxane consisting essentially of fluoroalkylsiloxane units and non-fluorine-containing siloxane units, there being less than 10 mole percent, based upon the total moles of siloxane units present, of non-fluorine-containing siloxane units in said fluoroalkylpolysiloxane, said container being filled with

(B) a silicone gel composition consisting essentially of a silicone gel of cross-linked polydimethylsiloxane.

12. A silicone gel-filled silicone rubber article possessing a reduced tendency to exhibit surface-bleed comprising

(A) a flexible container of silicone rubber consisting essentially of a cross-linked gum of polydimethylsiloxane, said container being filled with

(B) a silicone gel composition consisting essentially of a silicone gel of cross-linked polydimethylsiloxane, there being

(C) an essentially continuous barrier layer of a composition consisting essentially of fluorine-containing organopolysiloxane situated between the interior of container (A) and the gel composition of (B), said barrier layer being coated on the interior wall of container (A).