Lightweight cement slurry and method of use

• US 4,466,833 A
• Filed: 07/02/1982
• Issued: 08/21/1984
• Est. Priority Date: 04/30/1982
• Status: Expired due to Term

• Current Assignee: Dowell Schlumberger Incorporated (Schlumberger NV)
• Original Assignee: The Dow Chemical Company (Dow, Inc.)
• Inventors: Spangle, Lloyd B.
• Primary Examiner(s): Poer, James
• Application Number:
  US06/394,597
• Time in Patent Office: 781 Days
• Field of Search: 106/86-88, 106/90, 166/293
• US Class Current: 106/602
• CPC Class Codes: C04B 24/12 Nitrogen containing compounds organic derivatives of hydrazine hydrazine C04B22/00
• CPC Class Codes: C04B 28/26 Silicates of the alkali metals

Abstract

A foamed, cement slurry comprising an aqueous hydraulic cement slurry containing gas as discrete entrained bubbles and a specific quaternary ammonium compound as a foaming agent; and a process of plugging a subterranean void by emplacing the foamed slurry in the subterranean void and then permitting the foamed slurry to therein harden.

Claims

1. A foamed hydraulic cement slurry comprising an aqueous slurry of hydraulic cement, an entrained gas in the form of multiple, discrete bubbles and a foaming agent represented by the formula

View Dependent Claims (2, 3, 4, 5, 6, 7, 8, 9, 10, 11, 12, 13, 14, 15, 16, 17, 18, 19, 20, 21, 22, 23, 24, 25, 26, 27, 28, 29, 30)

2. The foamed slurry of claim 1 wherein, by volume, the solids therein comprise about 10 to about 35 percent of the foamed slurry, under conditions of use.

3. The foamed slurry of claim 1 wherein, by volume, the gas comprises about 20 to about 55 percent of the foamed slurry, under conditions of use.

4. The foamed slurry of claim 1, 2 or 3 wherein the hydraulic cement component comprises a Portland cement.

5. The foamed slurry of claim 1 wherein the solids and gas, by volume, comprise from about 10 and 20, respectively to about 35 and 55, respectively, percent of the foamed slurry, under conditions of use.

6. The foamed slurry of claim 1 or 5 wherein the foaming agent is present in an amount sufficient to permit the major portion of said gas to remain as discrete bubbles until said slurry has hardened.

7. The foamed slurry of claim 1 or 5 wherein the foaming agent is present, by volume, in an amount of about 0.1 part to about 3 parts per 100 parts water.

8. The foamed slurry of claim 7 wherein the foaming agent is present in an amount of about 0.5 to about 1.5 part per 100 parts water and the average diameter of said bubbles is about 0.5 millimeter or less.

9. The foamed slurry of claim 1 or 5 wherein the aqueous slurry further comprises, by weight, about 0.5 part to about 3 parts sodium silicate per 100 parts of the hydraulic cement component.

10. The foamed slurry of claim 9 wherein the hydraulic cement component comprises a Portland cement.

11. The foamed slurry of claim 9 which further comprises particles of finely divided fly ash having surface area of about 3000 cm² /g or greater and the surface area of the hydraulic cement component is about 2000 cm² /g or greater.

12. The foamed slurry of claim 6 wherein the foaming agent R is a hydrocarbyl radical of an average chain length of from 10 to 14 carbon atoms, R'"'"' is, independently each occurrence, methyl, ethyl, or in up to two occurrences hydroxyethyl, and X is chloride.

13. The foamed slurry of claim 9 wherein the foaming agent R is a hydrocarbyl radical of an average chain length of from 10 to 14 carbon atoms, R'"'"' is, independently each occurrence, methyl, ethyl, or in up to two occurrences hydroxyethyl, and X is chloride.

14. The foamed slurry of claim 12 wherein the hydraulic cement component comprises a Portland cement.

15. The foamed slurry of claim 6 wherein the foaming agent is selected from trimethylcocoammonium chloride, methyl bis(2-hydroxyethyl) cocoammonium chloride, trimethyldodecylammonium chloride or combinations thereof.

16. The foamed slurry of claim 15 wherein the foaming agent is present, by volume, in an amount of about 0.5 to about 1.5 part per 100 parts water and the hydraulic cement component comprises a Portland cement.

17. The foamed slurry of claim 15 wherein the foaming agent is present, by volume, in an amount of about 0.5 to about 1.5 part per 100 parts water, the hydraulic cement component comprises a Portland cement, the average diameter of said bubbles is about 0.5 millimeter or less and the foaming agent is selected from trimethylcocoammonium chloride and methyl bis(2-hydroxyethyl) cocoammonium chloride.

18. The foamed slurry of claim 17 which further comprises about 0.5 part to about 3 parts sodium silicate per 100 parts, by weight, of the Portland cement component.

19. The foamed slurry of claim 17 which further comprises bis(2-hydroxyethyl) cocoamine oxide.

20. The foamed slurry of claim 18 which further comprises bis(2-hydroxyethyl) cocoamine oxide in an amount of about 1 part, by volume, per 3 parts of the foaming agent, and the foaming agent is trimethylcocoammonium chloride.

21. The foamed slurry of claim 1 which further comprises finely divided silica.

22. The foamed slurry of claim 17 which further comprises finely divided silica.

23. A process for plugging a subterranean void with a lightweight, relatively impermeable plugging agent comprising emplacing a foamed slurry of claim 1 or 5 in the void and permitting same to harden.

24. A process for plugging a subterranean void with a lightweight, relatively impermeable plugging agent comprising a foamed slurry of claim 6 in the void and permitting same to harden.

25. A process for plugging a subterranean void with a lightweight, relatively impermeable plugging agent comprising emplacing a foamed slurry of claim 8 in the void and permitting same to harden.

26. A process for plugging a subterranean void with a lightweight, relatively impermeable plugging agent comprising emplacing a foamed slurry of claim 9 in the void and permitting same to harden.

27. A process for plugging a subterranean void with a lightweight, relatively impermeable plugging agent comprising emplacing a foamed slurry of claim 20 in the void and permitting same to harden.

28. A process for plugging a subterranean void with a lightweight, relatively impermeable plugging agent comprising emplacing a foamed slurry of claim 21 in the void and permitting same to harden.

29. The process of claim 24 wherein the foamed slurry is subjected to a temperature of about 150°

F. or greater prior to hardening.

30. The foamed slurry of claim 6 wherein the foaming agent is present in an amount sufficient to permit the major portion of said gas to remain as discrete bubbles at a temperature of about 150°

F. or greater until said slurry has hardened.