Tungsten barrier contact
First Claim
Patent Images
1. A method of fabricating a semiconductor device comprising the steps of:
- depositing a first metal layer onto a silicon substrate;
depositing a second metal layer onto the first metal layer, selected from the group consisting of tungsten, tantalum and hafnium;
depositing an aluminum contact onto the second metal layer; and
thereafterheating the substrate and metal layers on the substrate concurrently to anneal the first metal layer and the silicon substrate to form a silicide and also to sinter the aluminum contact in a single step, wherein the second metal layer prevents the aluminum from chemically reacting with the silicide during the single annealing and sintering step.
4 Assignments
0 Petitions
Accused Products
Abstract
A semiconductor contact has a thin barrier layer less than 500 angstroms in thickness of a metal such as tungsten applied between an aluminum contact layer and a metal-semiconductor compound. The metal semiconductor compound forms a junction with an underlying semiconductor substrate. The thin barrier prevents a chemical reaction between the aluminum of the contact layer and the metal of the metal-semiconductor compound.
31 Citations
7 Claims
-
1. A method of fabricating a semiconductor device comprising the steps of:
-
depositing a first metal layer onto a silicon substrate; depositing a second metal layer onto the first metal layer, selected from the group consisting of tungsten, tantalum and hafnium; depositing an aluminum contact onto the second metal layer; and
thereafterheating the substrate and metal layers on the substrate concurrently to anneal the first metal layer and the silicon substrate to form a silicide and also to sinter the aluminum contact in a single step, wherein the second metal layer prevents the aluminum from chemically reacting with the silicide during the single annealing and sintering step. - View Dependent Claims (2, 3, 4)
-
-
5. A method of fabricating a semiconductor device comprising the steps of:
-
depositing a layer of nickel onto a silicon substrate; depositing a layer of tungsten having a thickness of less than 500 angstroms on the nickel layer; depositing a contact layer of aluminum onto the tungsten; heating the substrate and metal layers in a furnace to anneal the nickel and silicon to form a nickel silicide and also to sinter the aluminum contact wherein the tungsten layer prevents the aluminum from chemically reacting with the nickel silicide and the annealing and sintering are performed in a single step.
-
-
6. A method of fabricating a semiconductor device comprising the steps of:
-
depositing three sequential metal layers of nickel, tungsten and aluminum on a silicon substrate by evaporation in a depressurized electron beam gun chamber while maintaining the depressurization of the chamber between depositions; and heating the substrate in a furnace to anneal the nickel and silicon into nickel silicide and to concurrently sinter the aluminum to provide an electrical contact wherein the tungsten layer provides an electrical connection between the aluminum contact and the nickel silicide region and also prevents a chemical reaction between the nickel and the aluminum so that the nickel silicide will form rather than a nickel aluminum compound.
-
-
7. A method of fabricating a semiconductor device comprising the steps of:
-
depositing a first metal layer for forming a metal silicide layer onto a silicon substrate in a depressurized chamber; depositing a second metal layer onto the first layer in the depressurized chamber, said second layer being selected from the group consisting of tungsten, tantalum and hafnium; and depositing an aluminum contact onto the second metal layer in the depressurized chamber; wherein the depressurization of the chamber is maintained between depositions.
-
Specification